Small angle neutron scattering and photoluminescence property of wet chemistry process synthesised ZnO nanoparticles

We report the synthesis of zinc oxide (ZnO) nanoparticles from aqueous solution at 25°C and subsequent heating of the solution at 115°C by the suitable selection of the solution chemistry and the control of the alkaline conditions. The structure of the synthesised ZnO particles was studied by X-ray diffraction (XRD), confirming the formation of Wurtzite structure. The optical property of synthesised ZnO nanoparticles is investigated through room temperature photoluminescence (PL) measurement. The PL of ZnO nanoparticles shows a strong UV emission band at approximately 385 nm, a blue–green band at approximately 473 nm and a very weak green band at approximately 554 nm, although polydispersity of the sample shows no presence on the PL spectrum. Small angle neutron scattering is used to determine the size and the size distribution of ZnO nanoparticles. The SANS data analysis and model fitting predict the size as about 18–20 nm, which is closely matched with XRD and transmission electron microscopy results with Gaussian distribution.