Manufacture and Testing of a Functionality Graded Material
Source abstract
Abstract
A novel technique is presented for the fabrication and fracture testing of large-scale polymeric based Functionality Graded Materials (FGMs). The technique generates a continuously inhomogeneous property variation by taking advantage of the susceptibility of a polyethylene carbon monoxide copolymer (ECO) to ultraviolet irradiation. The resulting FGMs exhibit a varying Young’s modulus, usually in a linear fashion, from approximately 160 MPa to 250 MPa over 150 mm wide specimens. The fracture behaviour of the FGM is experimentally investigated through the use of single edge notch fracture tests on both homogeneously irradiated and functionally graded ECO. Two approaches are used to evaluate fracture parameters: The first, a hybrid numerical-experimental method, is based on far field measurements only. The second uses digital image correlation to obtain near tip measurements. The energy release rates of uniformly irradiated ECO and of several FGMs are measured and compared. It was seen that the FGM showed a built-in fracture resistance behavior implying that it requires increased driving force to sustain crack growth.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Infrastructure Maintenance and Monitoring · Optical measurement and interference techniques · Numerical methods in engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Mechanical Engineering Department, University of Delaware, Newark, DE 19716
References (20)
Show source-provided references
1. Andrady A. L. , and NakatsukaS., 1994, “Studies on Enhanced Degradable Plastics III.—The Effect of Weathering of Polyethylene and Ethylene-Carbon Monoxide Copolymers on Moisure and Carbon Dioxide Permeability,” Journal of Environmental Polymer Degradation, Vol. 2(2), pp. 161–167.10.1007/BF02074784 ↗
2. ASTM, D.-9., 1997, “Standard Test Method for Tensile Properties of Thin Plastic Sheeting,” 1997 Annual Book of ASTM Standards 08.01, pp. 159–167.
3. ASTM, G.-9., 1997, “Standard Practice for Operating Light and Water Exposure Apparatus (fluorescent UV-Condensation type) for Exposure of Nonmetallic Materials,” 1991 Annual Book of ASTM Standards, 14.02, pp. 1252–1260.
4. Chao Y. J. , LuoP. F., and KalthoffJ. F., 1998, “An experimental study of the deformation fields around a propagating crack tip,” Experimental Mechanics, Vol. 38(2), pp. 79–85.10.1007/BF02321648 ↗
5. Choi H. J. , 1996, “An analysis of cracking in a layered medium with a functionally graded nonhomogeneous interface,” ASME Journal of Applied Mechanics, Vol. 63(2), pp. 479–486.10.1115/1.2788893 ↗
6. Chu, T. C., Ranson, W. F., Sutton, M. A., and Peters, W. H., 1985, “Applications of digital-image-correlation techniques to experimental mechanics,” Experimental Mechanics, Sept., pp. 232–244.10.1007/BF02325092 ↗
7. Delale F. , and ErdoganF., 1983, “The crack problem for a nonhomogeneous plane,” ASME Journal of Applied Mechanics, Vol. 50, pp. 609–614.10.1115/1.3167098 ↗
8. Domininghaus, H., 1993, Plastics for Engineers: Materials, Properties and Applications, Hanser Publications Munich, Germany.
9. Ivanova, E., Chudnovsky, A., Wu, S., Sehanobish, K., and Bosnyak, C. P., 1995, “The Effect of UV Radiation on Fatigue Behavior of Polymers,” Proceedings of ANTEC 95, pp. 3893–3897.
10. Ivanova E. , ChudnovskyA., WuS., SehanobishK., and BosnyakC. P., 1996, “A New Experimental Technique for Modeling of a Micro-Heterogeneous Media,” Experimental Techniques, Vol. 20(6), pp. 11–13.10.1111/j.1747-1567.1996.tb00471.x ↗
11. Jin Z. H. , and BatraR. C., 1996, “Some Basic Fracture Mechanics Concepts in Functionally Graded Materials,” Journal of the Mechanics and Physics of Solids, Vol. 44(8), pp. 1221–1235.10.1016/0022-5096(96)00041-5 ↗
12. Jin Z. H. , and NodaN., 1994, “Crack-Tip Singular Fields in Nonhomogeneous Materials,” ASME Journal of Applied Mechanics, Vol. 61(3), pp. 738–740.10.1115/1.2901529 ↗
13. Konda N. , and ErdoganF., 1994, “The Mixed Mode Crack Problem in a Nonhomogeneous Elastic Medium,” Engineering Fracture Mechanics, Vol. 47(4), pp. 533–545.10.1016/0013-7944(94)90253-4 ↗
14. Lambros, J., Santare, M. H., Li, H., and Sapna, G. III, 1999, “A Novel Technique for the Fabrication of Laboratory Scale Functionally Graded Materials,” to appear in Experimental Mechanics.10.1007/BF02323551 ↗
15. Li, H., Lambros, J., Cheeseman, B. A., and Santare, M. H., 1999, “Experimental Investigation of the Quasi-Static Fracture of Functionally Graded Materials,” to appear in International Journal of Solids and Structures.10.1016/S0020-7683(99)00056-6 ↗
16. McNeill S. R. , PetersW. H., and SuttonM. A., 1987, “Estimation of Stress Intensity Factor by Digital Image Correlation,” Engineering Fracture Mechanics, Vol. 28(1), pp. 101–112.10.1016/0013-7944(87)90124-X ↗
17. Narayanaswamy, A., and Lambros, J., 1999, “Application of Digital Image Correlation in the Study of Fracture of Homogeneous and Inhomogeneous Materials,” in preparation.
18. Peters W. H. , and RansonW. F., 1982, “Digital Imaging Techniques in Experimental Stress Analysis,” Optical Engineering, Vol. 21(3), pp. 427–431.10.1117/12.7972925 ↗
19. Peters W. H. , and RansonW. F., SuttonM. A., ChuT. C., and AndersonJ., 1983, “Application of Digital Correlation Methods to Rigid Body Mechanics,” Optical Engineering, Vol. 22(6), pp. 738–742.10.1117/12.7973231 ↗
20. Rabin B. H. , and ShiotaI., 1995, “Functionally Graded Materials,” Materials Research Society Bulletin, Vol. 20(1), pp. 14–18.10.1557/S0883769400048855 ↗