Optimizing the Soft Magnetic Properties of Mn-Zn Ferrite by a Proper Control of Sintering Process
Source abstract
Abstract
Manganese zinc (Mn-Zn) ferrites were prepared by solid-state reaction. The sintering process was investigated in detail using differential scanning calorimetry/thermogravimetric analysis and x-ray diffraction characterizations. A three-step weight loss was observed and the main Mn-Zn ferrite formation reaction was detected. Two-step heat treatment was employed to achieve high density Mn-Zn ferrite. For sintering temperatures from 1300°C to 1400°C, crystal grains of Mn-Zn ferrite became uniform with larger size and more equiaxed shape. The grain boundaries changed from curved to straight. Such features were believed helpful for the magnetic domain wall movement. In addition, better diffusivity at higher sintering temperature homogenized the distribution of impurities which also facilitated the magnetic domain alignment. Thanks to the microstructure acquired by controlling the sintering process, a high-amplitude permeability of 1151, a low total loss of 411 W/kg and coercivity of 57.63 A/m at 65 kHz were simultaneously achieved on samples sintered at 1400°C.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties and Synthesis of Ferrites · Multiferroics and related materials · Electromagnetic wave absorption materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Z. Xu, J. Fan, T. Liu, Y. Han, and H. Zhang, J. Alloys. Compd. 814, 152307 (2020).10.1016/j.jallcom.2019.152307 ↗
2. S. Ikram, J. Jacob, M. Arshad, K. Mahmood, A. Ali, N. Sabir, N. Amin, and S. Hussain, Ceram. Int. 45, 3563 (2019).10.1016/j.ceramint.2018.11.015 ↗
3. A. Anupama, V. Kumaran, and B. Sahoo, Rheol. Acta 58, 273 (2019).10.1007/s00397-019-01137-z ↗
4. M. Ali, M. Khan, F. Chowdhury, M. Hossain, M. Rahaman, S. Hoque, M. Matin, and M. Uddin, Results Phys. 14, 102517 (2019).10.1016/j.rinp.2019.102517 ↗
5. N. Al-Hada, H. Kamari, A. Shaari, and E. Saion, Results Phys. 12, 1821 (2019).10.1016/j.rinp.2019.02.019 ↗
6. E. Petrova, D. Kotsikau, V. Pankov, and A. Fahmi, J. Magn. Magn. Mater. 473, 85 (2019).10.1016/j.jmmm.2018.09.128 ↗
7. R. Gimenes, M. Baldissera, M. Silva, C. Silveira, D. Soares, L. Perazolli, M. Silva, and M. Zaghete, Ceram. Int. 38, 741 (2012).10.1016/j.ceramint.2011.07.066 ↗
8. J. Kalarus, G. Kogias, D. Holz, and V. Zaspalis, J. Magn. Magn. Mater. 324, 2788 (2012).10.1016/j.jmmm.2012.04.011 ↗
9. A. Smirnov and J. Tarduno, Eos 83, 309 (2002).10.1029/2002EO000222 ↗
10. G. Thirupathi and R. Singh, IEEE Trans. Magn. 48, 3630 (2012).10.1109/TMAG.2012.2199475 ↗
11. P. Hu, H. Yang, D. Pan, H. Wang, J. Tian, S. Zhang, X. Wang, and A. Volinsky, J. Magn. Magn. Mater. 322, 173 (2010).10.1016/j.jmmm.2009.09.002 ↗
12. A. Bajorek, C. Berger, M. Dulski, P. Lopadczak, M. Zubko, K. Prusik, M. Wojtyniak, A. Chrobak, F. Grasset, and N. Randrianantoandro, J. Phys. Chem. Solids 129, 1 (2019).10.1016/j.jpcs.2018.12.045 ↗
13. A. Farheen and R. Singh, AIP Conf. Proc. 1953, 120067 (2018).10.1063/1.5033132 ↗
14. M. Arshad, M. Asghar, M. Junaid, M. Warsi, M. Rasheed, M. Hashim, M. Al-Maghrabi, and M. Khan, J. Magn. Magn. Mater. 474, 98 (2019).10.1016/j.jmmm.2018.10.141 ↗
15. C. Beatrice, V. Tsakaloudi, S. Dobák, V. Zaspalis, and F. Fiorillo, J. Magn. Magn. Mater. 429, 129 (2017).10.1016/j.jmmm.2016.12.121 ↗
16. M. Drofenik, A. Žnidaršič, and I. Zajc, J. Appl. Phys. 82, 333 (1997).10.1063/1.365817 ↗
17. B. Rezaei, A. Kermanpur, and S. Labbaf, J. Magn. Magn. Mater. 481, 16 (2019).10.1016/j.jmmm.2019.02.085 ↗
18. P. Thakur, R. Sharma, M. Kumar, S. Katyal, P. Barman, V. Sharma, and P. Sharma, J. Magn. Magn. Mater. 479, 317 (2019).10.1016/j.jmmm.2019.02.048 ↗
19. S. Dobák, C. Beatrice, F. Fiorillo, V. Tsakaloudi, and C. Ragusa, IEEE Magn. Lett. 10, 1 (2019).10.1109/LMAG.2018.2881108 ↗
20. Y. Qu, Y. Wu, G. Fan, P. Xie, Y. Liu, Z. Zhang, J. Xin, Q. Jiang, K. Sun, and R. Fan, J. Alloys. Compd. 834, 155164 (2020).10.1016/j.jallcom.2020.155164 ↗
21. P. Tiwari, R. Verma, S. Kane, T. Tatarchuk, and F. Mazaleyrat, Mater. Chem. Phys. 229, 78 (2019).10.1016/j.matchemphys.2019.02.030 ↗
22. C. Srinivas, B. Tirupanyam, A. Satish, V. Seshubai, D. Sastry, and O. Caltun, J. Magn. Magn. Mater. 382, 15 (2015).10.1016/j.jmmm.2015.01.008 ↗
23. B. Argymbek, S. Kichanov, D. Kozlenko, E. Lukin, A. Morchenko, S. Dzhabarov, and B. Savenko, Phys. Solid State 60, 1727 (2018).10.1134/S1063783418090020 ↗
24. P. Hankare, S. Jadhav, U. Sankpal, S. Chavan, K. Waghmare, and B. Chougule, J. Alloys. Compd. 475, 926 (2009).10.1016/j.jallcom.2008.08.082 ↗
25. V. Harris, A. Geiler, Y. Chen, S. Yoon, M. Wu, A. Yang, Z. Chen, P. He, P. Parimi, X. Zuo, C. Patton, M. Abe, O. Acher, and C. Vittoria, J. Magn. Magn. Mater. 321, 2035 (2009).10.1016/j.jmmm.2009.01.004 ↗
26. P. Thakur, R. Sharma, V. Sharma, and P. Sharma, Mater. Chem. Phys. 193, 285 (2017).10.1016/j.matchemphys.2017.02.043 ↗
27. E. Macklen, J. Appl. Phys. 36, 1022 (1965).10.1063/1.1714082 ↗
28. M. Phan and H. Peng, Prog. Mater Sci. 53, 323 (2008).10.1016/j.pmatsci.2007.05.003 ↗
29. X. Guan, J. Zhang, C. Zhu, X. He, and S. Zhou, Mater. Rev. 20, 109 (2006).
30. C. Stergiou and V. Zaspalis, Ceram. Int. 41, 4798 (2015).10.1016/j.ceramint.2014.12.034 ↗
31. M. Drofenik and S. Besenicar, Am. Ceram. Soc. Bull. 65, 656 (1986).
32. D. Hu, F. Zhao, L. Miao, Z. Zhang, Y. Wang, H. Cheng, Y. Han, M. Tian, H. Gu, and R. Ma, Ceram. Int. 45, 10028 (2019).10.1016/j.ceramint.2019.02.047 ↗
33. M. Reddy, M. Bamana, W. Madhuri, K. Sadhana, K. Kumar, and R. Reddy, Adv. Appl. Ceram. 114, 326 (2015).10.1179/1743676115Y.0000000003 ↗
34. Z. Wang, K. Sun, H. Wu, P. Xie, Z. Wang, X. Li, and R. Fan, J. Mater. Sci. 55, 15481 (2020).10.1007/s10853-020-05126-z ↗
35. A. Hussain, A. Naeem, G. Bai, and G. Yan, J. Mater. Sci. Mater. Electron. 29, 20783 (2018).10.1007/s10854-018-0220-9 ↗
36. H. Zhang, Z. Wang, J. Pei, and Y. Gao, J. Solgel Sci. Technol. 90, 404 (2019).10.1007/s10971-019-04978-5 ↗
37. V. Tsakaloudi, E. Eleftheriou, M. Stoukides, and V. Zaspalis, J. Magn. Magn. Mater. 318, 58 (2007).10.1016/j.jmmm.2007.04.023 ↗
38. V. Tsakaloudi, G. Kogias, and V. Zaspalis, J. Alloys. Compd. 588, 222 (2014).10.1016/j.jallcom.2013.11.047 ↗
39. Y. Liu and S. He, J. Magn. Magn. Mater. 320, 3318 (2008).10.1016/j.jmmm.2008.07.001 ↗
40. A. Fujita, H. Kobiki, and S. Gotoh, J. Phys. Soc. Jpn. 22, S1_286 (1998).