Characteristics of barium hexaferrite nanocrystalline powders prepared by a sol-gel combustion method using inorganic agent
Source abstract
Abstract
Nanocrystalline particles of barium hexaferrite were synthesized by a sol-gel combustion route using nitrate-citrate gels prepared from metal nitrates and citric acid solutions under various Fe/Ba molar ratios of 10, 11 and 12. Sodium hydroxide was used as a pH-adjusting agent. The results revealed that the formation temperature of barium hexaferrite is influenced by Fe/Ba molar ratio; the Fe/Ba molar ratio of 12 is more favorable. For sample synthesized with a Fe/Ba molar ratio of 12, barium hexaferrite started to form at 800 °C and fully formed at 1000 °C. The results also showed that the coercivity of the samples decreases as the Fe/Ba molar ratio increases from 10 to 12, whilst the saturation magnetization increases.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties and Synthesis of Ferrites · Multiferroics and related materials · Electromagnetic wave absorption materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (9)
Show source-provided references
1. H. Kojima, Ferromagnetic Materials: A Handbook on the Properties of Magnetically Ordered Substances, vol. 3, ch. 5 E.P. Wohlfarth (North-Holland, Amsterdam (1982), 305
2. A. Ataie, S. Heshmati-Manesh, H. Kazempour, J. Mater. Sci. 37, 2125 (2002)10.1023/A:1015254221872 ↗
3. X. Liu, J. Wang, L.M. Gan, S.C. Ng, J. Magn. Magn. Mater. 195, 452 (1999)10.1016/S0304-8853(99)00123-7 ↗
4. W. Zhong, W. Ding, N. Zhang, J. Hong, Q. Yan, Y. Du, J. Magn. Magn. Mater. 168, 196 (1997)10.1016/S0304-8853(96)00664-6 ↗
5. C. Surig, K.A. Hempel, D. Bonnonberg, IEEE. Trans. Magn Mag-30, 4092 (1994)10.1109/20.333999 ↗
6. V.K. Sankaranarayanan, D.C. Khan, J. Magn. Magn. Mater. 153, 337 (1996)10.1016/0304-8853(95)00537-4 ↗
7. S.K. Mishra, L.C. Pathak, V. Rao, Mater. Lett. 32, 137 (1997)10.1016/S0167-577X(97)00027-X ↗
8. Z. Yue, J. Zhou, L. Li, H. Zhang, Z. Gui, J. Magn. Magn. Mater. 208, 55 (2000)10.1016/S0304-8853(99)00566-1 ↗
9. B.D. Cullity, Elements of X-Ray Diffraction, 2nd edn. Addison-Wesley, Reading, (MA, 1978), p 102