Preparation and characterization of Z-type hexaferrites, Ba3(1−x)Sr3x Co2Fe24O41 with x = 0–0.5, via a two-step calcination with an intermediate wet milling

Z-type hexaferrites (Ba3(1 − x)Sr3x Co2Fe24O41with x = 0–0.5, Z-hex) were prepared in a nearly phase pure state by a two-step calcination with an intermediate wet milling. The first calcination of the starting mixture comprising oxides or hydroxides at temperatures below 1100∘C brought about a mixture of layer-structured M and Y-type hexaferrite phases, together with a spinel phase of Co ferrite. Z-hex was fully crystallized after the second calcination up to 1230∘C. Wet milling between the two calcination steps was decisive for the phase purity. Emphasis was laid on the quantitative analyses of Z-hex, together with the evaluation of anisotropic growth of the crystallites. Sr addition stabilizes Z-hex, while decreases degree of anisotropy simultaneously.