Preparation and characterization of 3D bioprinted gelatin methacrylate hydrogel incorporated with curcumin loaded chitosan nanoparticles for in vivo wound healing application

This study developed a biomimetic composite bioink consisting of gelatin methacrylate (GelMA) /chitosan nanoparticles (CSNPs) for extrusion-based 3D bioprinting. Additionally, curcumin(Cur)-loaded nanoparticles were incorporated which increased the proliferation and antibacterial activity of biomimetic skin constructs. The hydrogel, curcumin-loaded NPs, and the biocomposite was characterized chemically and physically. The results indicated proper modified gelatin with tunable physical characteristics, e.g., swelling ratio and biodegradability up to 1200 % and 25 days, respectively. In addition, the characterized CSNPs showed good distribution with a size of 370 nm and a zeta potential of 41.1 mV. We investigated the mechanical and cytocompatibility properties of chitosan nanoparticles encapsulated in hydrogel for emulating an extracellular matrix suitable for skin tissue engineering. CSNPs entrapped in GelMA (15 % w/v) exhibited controlled drug release during 5 days, which was fitted into various kinetic models to study the mass transfer mechanism behavior. Also, the composite hydrogels were effective as a barrier against both gram-positive and gram-negative bacteria at a concentration of 50 μg/ml nanoparticles in GelMA 15 %. Furthermore, the biocomposite was applied on Wistar rats for wound healing. As a result, this study provides a GelMA-NP50-Cur3 scaffold that promotes cell proliferation and decreases microbial infections in wounds.