Effect of a neutral citrate solution on the fluoride release of resin-modified glass ionomer and polyacid-modified composite resin cements

The effect of 0.01 mol/l citrate solution at pH = 7 on the fluoride release is compared for the resin-modified glass ionomer cements (RM-GIC) GC Lining LC, PhotacBond, Vitremer and Vitrebond and for the polyacid-modified composite resins (PAM-C) Variglass and Dyract by means of the six-month fluoride release profiles at 37 degrees C. The fluoride release of both RM-GIC and PAM-C increases in the neutral citrate solution as compared to water, which can be explained by the ability of citrate to complex metal ions and hence to degrade the glass as well as the polysalt matrix of the cement. Although RM-GIC release more fluoride than PAM-C in water as well as in citrate solution, the relative increase in fluoride release upon immersion in citrate solution is most pronounced for PAM-C. Whereas for the latter citrate affects both the short-term and long-term fluoride release, for RM-GIC only the long-term fluoride release is affected. This suggests that the action of citrate increases with decreasing importance of the polysalt formation in the hardening of the material. This could be explained on the basis of the difference in the chemical properties of the cement matrix.