Hydrogen embrittlement of work-hardened Ni–Ti alloy in fluoride solutions
Source abstract
Abstract
Hydrogen embrittlement of work-hardened Ni-Ti alloy has been examined in acidulated phosphate fluoride (APF) solutions. Upon immersion in a 2.0% APF solution with a pH of 5.0, tensile strength decreased markedly with immersion time. Moreover, the fracture mode changed from ductile to brittle due to brittle layer formation at the peripheral part of the cross section of the specimen. The amount of absorbed hydrogen increased linearly with immersion time, and it reached above 5000 mass ppm after 24 h. The hydrogen desorption temperature of the immersed specimens shifted from 450 degrees C to a lower temperature with immersion time. As the amount of absorbed hydrogen was larger than 500 mass ppm, the degradation of mechanical properties was recognized. Although the tensile properties and fracture mode scarcely change in a 0.2% APF solution, the slight reduction in hardness and hydrogen absorption of several hundreds mass ppm were observed. The results of the present study imply that work-hardened Ni-Ti alloy is less sensitive to hydrogen embrittlement compared with Ni-Ti superelastic alloy.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (48)
Show source-provided references
1. An evaluation of 55 cobalt substituted nitinol wire for orthodontics10.14219/jada.archive.1971.0209 ↗
2. Chinese NiTi wire—a new orthodontic alloy10.1016/0002-9416(85)90083-1 ↗
3. The super-elastic property of the Japanese NiTi alloy wire for use in orthodontics10.1016/0889-5406(86)90021-1 ↗
4. Transformation pseudoelasticity and deformation behavior in a Ti-50.6 at% Ni alloy10.1016/0036-9748(81)90346-X ↗
5. Pseudoelasticity and shape memory effects in alloys10.1179/imr.1986.31.1.93 ↗
6. The corrosion behaviour of nickel titanium shape memory alloys10.1016/0010-938X(90)90004-O ↗
7. Biological and chemical evaluation of TiNi alloys10.4028/www.scientific.net/MSF.56-58.705 ↗
8. Corrosion resistance tests on NiTi shape memory alloy10.1016/0142-9612(95)00352-5 ↗
9. Electrochemical and surface characterization of a nickel–titanium alloy10.1016/S0142-9612(97)00210-X ↗
10. Effect of surface treatment and sterilization processes on the corrosion behavior of NiTi shape memory alloy10.1002/1097-4636(20000915)51:4<685::AID-JBM17>3.0.CO;2-S ↗
11. Physicochemical and biological aspects of Nitinol as a biomaterial10.1179/095066001771048745 ↗
12. Surface corrosion of nitinol and stainless steel under clinical conditions
13. Surface analysis of nickel–titanium archwire used in vivo10.1016/S0109-5641(97)80118-2 ↗
14. Surface characterization of retrieved NiTi orthodontic archwires10.1093/ejo/22.3.317 ↗
15. Nitinol arch wire in a simulated oral environment; changes in mechanical properties10.1016/0889-5406(88)90080-7 ↗
16. The effect of long-term deflection on permanent deformation of nickel–titanium archwires
17. Examination of Chinese NiTi wire by a combined clinical and laboratory approach10.1093/ejo/13.5.386 ↗
18. Degradation and fracture of Ni–Ti superelastic wire in an oral cavity10.1016/S0142-9612(00)00414-2 ↗
19. Hydrogen embrittlement of nickel–titanium alloy in biological environment10.1007/s11661-002-0111-8 ↗
20. Hydrogen embrittlement of Ni–Ti superelastic alloy in fluoride solution10.1002/jbm.a.10457 ↗
21. Degradation in performance of orthodontic wires caused by hydrogen absorption during short-term immersion in 2.0% acidulated phosphate fluoride solution
22. Delayed fracture of Ni–Ti superelastic alloys in acidic and neutral fluoride solutions10.1002/jbm.a.20122 ↗
23. Delayed fracture of beta titanium orthodontic wire in fluoride aqueous solutions10.1016/S0142-9612(02)00642-7 ↗
24. Hydrogen absorption behavior of beta titanium alloy in acid fluoride solutions10.1016/j.biomaterials.2003.09.006 ↗
25. Fracture associated with hydrogen absorption of sustained tensile-loaded titanium in acid and neutral fluoride solutions10.1002/jbm.a.20067 ↗
26. A role of hydrogen in shape memory effect of Ti–Ni alloys10.1016/0956-716X(90)90298-U ↗
27. Effect of hydrogen on the shape memory effect and transformation behavior of Ti–Ni alloy10.2320/jinstmet1952.54.5_525 ↗
28. Effect of hydrogen on transformation characteristics and deformation behavior in a TiNi shape memory alloy10.2320/jinstmet1952.56.7_747 ↗
29. Effect of a small amount of hydrogen on pseudo-elastic properties of Ti–Ni alloy10.2320/jinstmet1952.57.10_1123 ↗
30. Biscarini A, Campanella R, Coluzzi B, Mazzolai G, Trotta L, Tuissi A, Mazzolai FM. Martensitic transitions and mechanical spectroscopy of Ni50.8Ti49.2 alloy containing hydrogen. Acta Mater 1999;47:4525–33.10.1016/S1359-6454(99)00337-7 ↗
31. Degradation of tensile strength of Ni–Ti superelastic alloy due to hydrogen absorption in methanol solution containing hydrochloric acid10.1016/S0921-5093(03)00403-9 ↗
32. Function of hydrogen in embrittlement of high-strength steels10.2355/isijinternational.41.590 ↗
33. Hydrogen solubility and diffusion in the shape-memory alloy NiTi10.1088/0953-8984/1/14/003 ↗
34. Susceptibility to delayed fracture of Ni–Ti superelastic alloy10.1016/S0921-5093(02)00201-0 ↗
35. Hydrogen in trapping states innocuous to environmental degradation of high-strength steels10.2355/isijinternational.43.520 ↗
36. Accelerated oxide grown on titanium implants during autoclaving caused by fluorine contamination10.1016/0142-9612(85)90033-X ↗
37. SEM observations on stress corrosion cracking of commercially pure titanium in a topical fluoride solution10.1016/0109-5641(95)80061-1 ↗
38. Effects of fluorides on titanium and other dental alloys in dentistry10.1016/S0142-9612(97)00179-8 ↗
39. Effect of fluoride concentration and pH on corrosion behavior of titanium for dental use10.1177/00220345990780091201 ↗
40. Effects of fluoride concentration and elastic tensile strain on the corrosion resistance of commercially pure titanium10.1016/S0142-9612(01)00079-5 ↗
41. Influence of fluoride content and pH on the corrosion resistance of titanium and its alloys10.1016/S0142-9612(01)00328-3 ↗
42. A new model for hydrogen-assisted cracking (hydrogen “embrittlement”)10.1007/BF02642048 ↗
43. Hydrogen-enhanced localized plasticity—a mechanism for hydrogen-related fracture10.1016/0921-5093(94)90975-X ↗
44. Equilibrium aspects of hydrogen-induced cracking of steels10.1016/0001-6160(74)90061-3 ↗
45. Nature of hydrogen trapping sites in steels induced by plastic deformation10.1016/S0925-8388(99)00322-9 ↗
46. Accelerated failure in high strength steel by alternating hydrogen-charging potential10.1016/S1359-6462(00)00683-7 ↗
47. Hydride formation during cathodic polarization of Ti–I
48. Electrochemical, galvanic, and mechanical responses of grade 2 titanium in 6% sodium chloride solution10.5006/1.3283973 ↗