Experimental and Finite Element Analytical Guidelines for Fabricating Continuous Fiber (SCS-6) Metal Matrix (Ti-6A1-4V) Composites via the Foil/Fiber/Foil Technique
Source abstract
Abstract
The consolidation behavior of Ti-6A1-4V matrix SCS-6 silicon carbide fiber metal matrix composites fabricated using the foil/fiber/foil technique was studied by both experimental physical modeling and finite element analysis. The experiments were carried out at 875 0 C (T/Tm = 0.597 for the matrix material) for varying levels of uniaxial compressive stress and times to characterize the stages of consolidation observed prior to reaching full density. Three stages of consolidation were identified: (1) instantaneous plasticity, (2) time-dependent foil deformation prior to establishing contact between neighboring foils, and (3) time dependent consolidation to close the pores at each side of the fiber that remain after neighboring foils have contacted between the fibers. Finite element analysis using the commercial code ABAQUS was employed to model the process and to examine the role of fiber spacing and applied stress level on the time required to densify the composite. The simulation predictions for the times necessary to achieve various densities were in good agreement with the experimental observations. The FEA results were used to establish analytical relations that describe the entire densification process. These equations are quite general and can be used to characterize any foil/fiber/foil composite fabrication process since they include as variables the matrix flow properties, processing stress and temperature, foil thickness and fiber diameter. The results predicted a slowing in densification at the latter stages of pore closure. This slowing was attributed to the low stresses in the matrix near a pore. Also, as the fiber spacing decreases, the time to densify increases because the load per fiber is now smaller.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metal Forming Simulation Techniques · Aluminum Alloys Composites Properties · Metallurgy and Material Forming
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Center for Advanced Deformation Processing Research, Carnegie Mellon University, Pittsburgh, PA 15213-3890
Department of Materials Science and Engineering.;Center for Advanced Deformation Processing Research, Carnegie Mellon University, Pittsburgh, PA 15213-3890
Department of Civil Engineering.; Center for Advanced Deformation Processing Research, Carnegie Mellon University, Pittsburgh, PA 15213-3890
References (22)
Show source-provided references
1. Smith, P. R. · J. Metals · 1984 · 36 · 19
2. 10.1007/BF0322056410.1007/BF03220564 ↗
3. 10.1007/BF0322038510.1007/BF03220385 ↗
4. 10.1520/STP32814S10.1520/STP32814S ↗
5. 5. Jha, S. C., J. A. Forster, A. K. Pandley and R. G. Delago. 1991. In High Performance Composites for the 1990's, S. K. Das, C. P. Ballard and F. Maribar, eds. Warrendale, PA: The Minerals, Metals and Materials Society, pp. 159-169.
6. 6. Larson, L. and R. Warren. 1980. In Advanced Fibers and Composites for Elevated Temperatures, Warrendale, PA: TMS, pp. 108-125.
7. 7. Nicolaou, P. D., H. R. Piehler and M. A. Kuhni. 1991. In Developments in Ceramic and Metal Matrix Composites, K. Upadhya, ed. Warrendale, PA: The Minerals, Metals and Materials Society, pp. 37-47.
8. 8. Semiatin, S. L., R. L. Goetz and W. R. Kerr. 1992. In Intermetallic Matrix Composites II, D. B. Miracle, D. L. Anton and J. A. Graves, eds. Pittsburgh, PA: MRS, 273:351-364.10.1557/PROC-273-351 ↗
9. 9. Wilkining, W. W. and W. A. Backofen. 1970. Final Report, Contract N00019-70-C-0071.
10. 10.1520/STP35510S10.1520/STP35510S ↗
11. Shorshorov, M. K. · Soviet Powder Metallurgy Ceramics · 1981 · 20 · 46110.1007/BF00800521 ↗
12. 12. Nicolaou, P. D., H. R. Piehler and S. Saigal. 1993. In Computer Applications in Shaping and Forming of Materials, M. Y. Demeri, ed. Warrendale, PA: The Minerals, Metals and Materials Society, pp. 117-135.
13. 10.1007/BF0264881910.1007/BF02648819 ↗
14. 14. Bampton, C. C., J. A. Graves, K. J. Newell and R. H. Lorenz. 1992. In Intermetallic Matrix Composites II, D. B. Miracle, D. L. Anton, and J. A. Graves, eds. Pittsburgh, PA: Materials Research Society, 273:365-376.10.1557/PROC-273-365 ↗
15. 15. Backofen, W. A. 1972. Deformation Processing, Reading, MA: Addison Wesley Publishing Co., pp. 162-169.
16. Hibbitt, Karlsson and Sorensen, Inc. · 1991
17. 10.1179/msc.1981.15.10.44210.1179/msc.1981.15.10.442 ↗
18. 10.1016/0001-6160(87)90095-210.1016/0001-6160(87)90095-2 ↗
19. 10.1063/1.172187510.1063/1.1721875 ↗
20. 10.1016/0025-5416(88)90249-210.1016/0025-5416(88)90249-2 ↗
21. 10.1016/0001-6160(85)90177-410.1016/0001-6160(85)90177-4 ↗
22. 22. Frost, H. J. and M. F. Ashby. 1982. Deformation Mechanism Maps, New York, NY: Pergamon Press, pp. 44-50.