Effects of surface fluorination on the dyeing of polycarbonate (PC) resin
Source abstract
Abstract
The surface of polycarbonate (PC) was fluorinated with a mixed gas of F2 and O2 at 25 °C for 1 h. The surface roughness (Ra) of the fluorinated PC samples was about double that of the untreated sample (0.685 nm), while the water contact angle of the fluorinated PC samples decreased from 80° to 12°. The dyeing properties of the PC surface were enhanced after surface fluorination due to the increased roughness and hydrophilicity. Fluorination using a mixed gas with a higher F2 proportion led to the formation of a thicker dyeable fluoride layer, thereby giving a deeper color after staining of the PC surface.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Dyeing and Modifying Textile Fibers · Photopolymerization techniques and applications · Surface Modification and Superhydrophobicity
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. VanDelinder, V, Wheeler, DR, Small, LJ, Brumbach, MT, Spoerke, ED, Henderson, I, Bachand, GD, “Aqueous-Based Amination of Polycarbonate Surfaces.” ACS Appl. Mater. Inter., 7 5643–5649 (2015)10.1021/am508797h ↗
2. Pedrosa, P, Chappe, JM, Fonseca, C, Machado, AV, Nobrega, JM, Vaz, F, “Plasma Surface Modification of Polycarbonate and Poly(propylene) Substrates for Biomedical Electrodes.” Plasma Process. Polym., 7 676–686 (2010)10.1002/ppap.200900176 ↗
3. Verkuijlen, ROF, Van Dongen, MHA, Stevens, AAE, Geldrop, J, Van Bernards, JPC, “Surface Modification of Polycarbonate and Polyethylene Naphtalate Foils by UV-Ozone Treatment and μPlasma Printing.” Appl. Surf. Sci., 290 381–387 (2014)10.1016/j.apsusc.2013.11.089 ↗
4. Mello, CB, Kostov, KG, Machida, M, de Oliveira Hein, LRO, de Campos, KA, “Surface Modification of Polycarbonate by Atmospheric-Pressure Plasma Jets.” IEEE Trans. Plasma Sci., 40 2800–2805 (2012)10.1109/TPS.2012.2210055 ↗
5. Jia, Y, Asahara, H, Hsu, YI, Ahoh, TA, Uyama, H, “Surface Modification of Polycarbonate Using the Light-Activated Chlorine Dioxide Radical.” Appl. Surf. Sci., 530 147202 (2020)10.1016/j.apsusc.2020.147202 ↗
6. Du, Y, Zhang, Y, Jiang, H, Li, T, Luo, M, Wang, L, Wang, C, Wang, H, “Hydrophilic Modification of Polycarbonate Surface with Surface Alkoxylation Pretreatment for Efficient Separation of Polycarbonate and Polystyrene by Froth Flotation.” Waste Manag., 118 471–480 (2020)10.1016/j.wasman.2020.09.006 ↗
7. Abenojar, J, Torregrosa-Coque, R, Martinez, MA, Martin-Martinez, JM, “Surface Modifications of Polycarbonate (PC) and Acrylonitrile Butadiene Styrene (ABS) Copolymer by Treatment with Atmosphere Plasma.” Surf. Coat. Technol., 203 2173–2180 (2009)10.1016/j.surfcoat.2009.01.037 ↗
8. Slepička, P, Siegel, J, Lyutakov, O, Slepičková Kasalkova, N, Kolská, Z, Bačáková, L, Švorčík, V, “Polymer Nanostructures for Bioapplications Induced by Laser Treatment.” Biotechnol. Adv., 36 839–855 (2018)10.1016/j.biotechadv.2017.12.011 ↗
9. Strobel, M, Lyons, CS, “The Role of Low-Molecular-Weight Oxidized Materials in the Adhesion Properties of Corona-Treated Polypropylene Film.” J. Adhes. Sci. Technol., 17 15–23 (2003)10.1163/15685610360472411 ↗
10. Gao, SL, Häβer, R, Mäder, E, Bahners, T, Opwis, K, Schollmeyer, S, “Photochemical Surface Modification of PET by Excimer UV Lamp Irradiation.” Appl. Phys. B Lasers Opt., 81 681–690 (2005)10.1007/s00340-005-1928-9 ↗
11. Löhbach, C, Bakowsky, U, Kneuer, C, Jahn, D, Graeter, T, Schäfers, HJ, Lehr, CM, “Wet Chemical Modification of PTFE Implant Surface with a Specific Cell Adhesion Molecule.” Chem. Commun., 21 2568–2569 (2002)10.1039/B206100G ↗
12. Ku, SH, Lee, JS, Park, CB, “Spatial Control of Cell Adhesion and Patterning Through Mussel-Inspired Surface Modification by Polydopamine.” Langmuir, 26 15104–15108 (2010)10.1021/la102825p ↗
13. Kim, J-H, Namie, M, Yonezawa, S, “Enhanced Adhesion Between Polyethylene Terephthalate and Metal Film by Surface Fluorination.” Comp. Commun., 10 205–208 (2018)10.1016/j.coco.2018.10.006 ↗
14. Kharitonov, AP, Simbirtseva, GV, Bouznik, VM, Chepezubov, MG, Dubois, M, Guerin, K, Hamwi, A, Kharbache, H, Masin, F, “Modification of Ultra-High-Molecular Weight Polyethylene by Various Fluorinating Routes.” J. Polym. Sci. Part A, 49 3559–3573 (2011)10.1002/pola.24793 ↗
15. Kim, J-H, Umeda, H, Ohe, M, Yonezawa, S, Takashima, M, “Preparation of Pure LiPF6 Using Fluorine Gas at Room Temperature.” Chem. Lett., 40 360–361 (2011)10.1246/cl.2011.360 ↗
16. Li, B, Gao, J, Wang, X, Fan, C, Wang, H, Liu, X, “Surface Modification of Polypropylene Battery Separator by Direct Fluorination with Different Gas Components.” Appl. Surf. Sci., 290 137–141 (2014)10.1016/j.apsusc.2013.11.015 ↗
17. Kamaraj, AB, Shaw, V, Sundaram, MM, “Novel Fabrication of Un-Coated Super-Hydrophobic Aluminum via Pulsed Electrochemical Surface Modification.” Proc. Manuf., 1 892–903 (2015)
18. Kim, J-H, Nishimura, F, Yonezawa, S, Takashima, M, “Enhanced Dispersion Stability and Photocatalytic Activity of TiO2 Particles Fluorinated by Fluorine Gas.” J. Fluor. Chem., 144 165–170 (2012)10.1016/j.jfluchem.2012.08.010 ↗
19. Yamaguchi, S, Minbuta, S, Matsui, K, “Adsorption of the Cationic Dye Methylene Blue on Anodic Porous Alumina in Sodium Dodecyl Sulfate Solutions.” Langmuir, 36 4592–4599 (2020)10.1021/acs.langmuir.0c00182 ↗