Titanium implant osseointegration with calcium pyrophosphate in rabbits

Abstract The objective of this study was to characterize calcium pyrophosphate material, evaluate itsin vitrocytotoxicity, and assess its ability to induce bone formation. X‐ray diffraction (XRD) was used to deterimne crystallinity and phases present in material. Serial dilutions of extracts, from 10‐day dissolution tests in modified Eagle's medium, were exposed for 24 h to mouse fibroblasts and cytotoxicity assessed via viable staining.In vivoperformance was determined by placing Ti screws with and without calcium pyrophosphate agglutinated with marrow adipose tissue in the tibiae of eight rabbits. New bone formation around test and control implants was evaluated histomorphometrically by using three fluorochrome labels: alizarin, calcein, and tetracycline. After 8 postoperative weeks, the animals were killed and specimens were retrieved and processed for fluorescence and light microscopic analysis. Calcium pyrophosphate showed no cytotoxicity and the XRD showed that the main phase of the analyzed sample corresponded to β‐calcium pyrophosphate. The largest fluorochrome labeling area occurred during the fourth and fifth postoperative weeks, in both control and experimental groups. Histologically, the bone neoformation occurred in regions where the calcium pyrophosphate was resorbed. The morphometric analysis showed implants placed with calcium pyrophosphate resulted in smaller polyfluorochrome labeling area (p< 0.05). © 2005 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2006