Electrophoretic Deposition for Lithium‐Ion Battery Electrode Manufacture

Abstract Electrophoretic deposition (EPD) has received increasing attention as an alternative manufacturing approach to slurry casting for the production of battery and supercapacitor electrodes. This process is of relevance for industrial scalability as evidently seen in the current electrophoretic paints industry. Nevertheless, the reported work so far have only concentrated on thin films of electrophoretically deposited electrodes for energy storage. Here, the electrochemical performance of thick films (up to tens of μm) as lithium‐ion battery electrodes produced by EPD is reported. A commercially sourced LiN_1/3M_1/3C_1/3O₂ (5 to 25 μm particle size) was used in this exemplary investigation. This work shows the production of binder‐free high density active material (>90 %) electrodes. Coin cells were assembled and the battery performance was measured. Tests included: cyclic voltammetry, C‐rate vs capacity, battery cycling and electrochemical impedance spectroscopy. Other investigations also studied: colloidal electrolyte formulation, electrode manufacture, microstructure characterisation and elemental mapping analysis. In short, EPD electrode manufacture can be applied as a platform technology for any battery and supercapacitor material, and the reported manufacturing processes and methodologies represent direct relevance to produce energy storage electrodes useful to practical applications.