Enhanced Surface Area Carbon Cathodes for the Hydrogen–Bromine Redox Flow Battery

The hydrogen–bromine redox flow battery is a promising energy storage technology with the potential for capital costs as low as 220 $ kWh−1 and high operational power densities in excess of 1.4 W cm−2. In this work, enhanced surface area bromine electrodes incorporating carbon black (CB) and graphene nanoplatelets (GnPs) on carbon paper and carbon cloth substrates were investigated, and the effect of electrolyte concentration on performance of the electrodes was studied. Carbon-black-modified electrodes are found to possess the largest electrochemically active surface areas, i.e., up to 11 times that of unmodified materials, while GnP electrodes are shown to have superior kinetic activity towards the bromine electrode reaction. In terms of performance, lower electrolyte concentrations are found to favour the improved kinetic parameters associated with graphene nanoplatelet electrodes, while highly concentrated electrolytes favour the larger electrochemically active surface area of carbon black electrodes. The optimal performance was achieved on a carbon-black-modified carbon cloth electrode in a 6 M HBr/2 M Br2 electrolyte concentration, with polarisation current densities approaching 1.6 A cm−2 at overpotentials of ±400 mV, and mean overpotentials of 364 mV during oxidation and 343 mV during reduction, resulting from bromine oxidation/reduction cycling tests at ±1.5 A cm−2.