Mechanisms of Alkali-Silica Reaction in Alkali-Activated High-Volume Fly Ash Mortars
Source abstract
Abstract
Alkali-activation of high-volume fly ash (HVFA) is a viable approach to produce durable cementitious binders with faster and stronger strength development than its water-activated counterparts. However, the use of alkaline activator increases the risk of alkali-silica reaction (ASR) in these systems. In this work, the compressive strength and ASR susceptibility of alkali-activated fly ash-OPC mortars containing reactive aggregate are studied. The results show that in comparison to plain water-activated fly ash-OPC mixture, the alkali incorporation at a low concentration improves strength development only when the fly ash replacement ratio is higher than about 80%; however, excessive alkali has an adverse influence. Regardless of activator type and dosage, alkali-activated fly ash-OPC mortars are ASR innocent as assessed in the accelerated mortar bar test and scanning electron microscopic analysis, provided that the fly ash percentage higher than about 40%. The mechanism for the insignificant ASR expansion and damage in alkali-activated HVFA mortars is likely attributed to the low calcium content that prevents gelation of deleterious and expansive ASR products.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Magnesium Oxide Properties and Applications · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Civil Engineering, The University of Hong Kong, Pokfulam, Hong Kong.
References (57)
Show source-provided references
1. 1) Alahrache, S., Winnefeld, F., Champenois, J. B., Hesselbarth, F. and Lothenbach, B., (2016). “Chemical activation of hybrid binders based on siliceous fly ash and Portland cement.” Cement and Concrete Composites, 66, 10-23.10.1016/j.cemconcomp.2015.11.003 ↗
2. 2) Atiş, C. D., (2002). “Heat evolution of high-volume fly ash concrete.” Cement and Concrete Research, 32(5), 751-756.10.1016/S0008-8846(01)00755-4 ↗
3. 3) Atiş, C. D., (2003). “High-volume fly ash concrete with high strength and low drying shrinkage.” Journal of Materials in Civil Engineering, 15(2), 153-156.10.1061/(ASCE)0899-1561(2003)15:2(153) ↗
4. 4) Bleszynski, R. F. and Thomas, M. D. A., (1998). “Microstructural studies of alkali-silica reaction in fly ash concrete immersed in alkaline solutions.” Advanced Cement Based Materials, 7(2), 66-78.10.1016/S1065-7355(97)00030-8 ↗
5. 5) Chappex, T. and Scrivener, K., (2012). “Alkali fixation of C-S-H in blended cement pastes and its relation to alkali silica reaction.” Cement and Concrete Research, 42(8), 1049-1054.10.1016/j.cemconres.2012.03.010 ↗
6. 6) Davidovits, J., (2005). “Geopolymer, Green Chemistry and Sustainable Development Solutions: Proceedings of the World Congress Geopolymer 2005.” Saint-Quentin, France: Geopolymer Institute.
7. 7) Diamond, S., (1989). “ASR-another look at mechanisms.” In: K. Okada, S. Nishibayashi and M. Kawamura, Eds. Proceedings of the 8th Intl. Conf. on Alkali-Aggregate Reaction in Concrete, Kyoto 17-20 July 1989. London: CRC Press, Taylor & Francis Group, 115-119.
8. 8) Donatello, S., Fernández-Jimenez, A. and Palomo, A., (2013). “Very high volume fly ash cements: early age hydration study using Na2SO4 as an activator.” Journal of the American Ceramic Society, 96(3), 900-906.10.1111/jace.12178 ↗
9. 9) Duxson, P., Fernández-Jiménez, A., Provis, J. L., Lukey, G. C., Palomo, A. and van Deventer, J. S. J., (2007). “Geopolymer technology: the current state of the art.” Journal of Materials Science, 42(9), 2917-2933.10.1007/s10853-006-0637-z ↗
10. 10) Fernández-Jiménez, A., García-Lodeiro, I. and Palomo, A., (2007). “Durability of alkali-activated fly ash cementitious materials.” Journal of Materials Science, 42(9), 3055-3065.10.1007/s10853-006-0584-8 ↗
11. 11) Fernández-Jiménez, A. and Palomo, A., (2005). “Composition and microstructure of alkali activated fly ash binder: effect of the activator.” Cement and Concrete Research, 35(10), 1984-1992.10.1016/j.cemconres.2005.03.003 ↗
12. 12) Fernández-Jiménez, A., Palomo, A. and Criado, M., (2005). “Microstructure development of alkali-activated fly ash cement: a descriptive model.” Cement and Concrete Research, 35(6), 1204-1209.10.1016/j.cemconres.2004.08.021 ↗
13. 13) Garcia-Lodeiro, I., Fernández-Jiménez, A. and Palomo, A., (2013). “Variation in hybrid cements over time: alkaline activation of fly ash-portland cement blends.” Cement and Concrete Research, 52, 112-122.10.1016/j.cemconres.2013.03.022 ↗
14. 14) García-Lodeiro, I., Palomo, A. and Fernández-Jiménez, A., (2007). “Alkali-aggregate reaction in activated fly ash systems.” Cement and Concrete Research, 37(2), 175-183.10.1016/j.cemconres.2006.11.002 ↗
15. 15) Hardjito, D., Wallah, S. E., Sumajouw, D. M. J. and Rangan, B. V., (2004). “On the development of fly ash-based geopolymer concrete.” Materials Journal, 101(6), 467-472.
16. 16) Hobbs, D. W., (1988). “Alkali-silica reaction in concrete.” London: Thomas Telford Publishing.10.1680/aric.13179 ↗
17. 17) Iler, R. K., (1973). “Effect of adsorbed alumina on the solubility of amorphous silica in water.” Journal of Colloid and Interface Science, 43(2), 399-408.10.1016/0021-9797(73)90386-X ↗
18. 18) Katayama, T., (2006). “Modern petrography of carbonate aggregates in concrete-diagnosis of so-called alkali-carbonate reaction and alkali-silica reaction.” In: B. Fournier Ed. Marc-Andre-Berube Symposium on Alkali-Aggregate Reactivity in Concrete, 8th CANMET/ACI International Conference on Recent Advances in Concrete Technology, Montreal, Canada 31 May - 3 June 2006. Montreal: CANMET/ACI, 423-444.
19. 19) Katayama, T., (2010). “The so-called alkali-carbonate reaction (ACR): its mineralogical and geochemical details, with special reference to ASR.” Cement and Concrete Research, 40(4), 643-675.10.1016/j.cemconres.2009.09.020 ↗
20. 20) Kawabata, Y. and Yamada, K., (2015). “Evaluation of alkalinity of pore solution based on the phase composition of cement hydrates with supplementary cementitious materials and its relation to suppressing ASR expansion.” Journal of Advanced Concrete Technology, 13(11), 538-553.10.3151/jact.13.538 ↗
21. 21) Khatri, R. P., Sirivivatnanon, V. and Gross, W., (1995). “Effect of different supplementary cementitious materials on mechanical properties of high performance concrete.” Cement and Concrete Research, 25(1), 209-220.10.1016/0008-8846(94)00128-L ↗
22. 22) Lane, D. S. and Ozyildirim, H. C., (1995). “Use of fly ash, slag, or silica fume to inhibit alkali-silica reactivity.” Virginia Transportation Research Council, Technical Report VTRC 95-R21.
23. 23) Li, C., Sun, H. and Li, L., (2010). “A review: the comparison between alkali-activated slag (Si+ Ca) and metakaolin (Si+ Al) cements.” Cement and Concrete Research, 40(9), 1341-1349.10.1016/j.cemconres.2010.03.020 ↗
24. 24) Li, Z., (2017). “Acid Leaching Resistance and Alkali Silica Reaction (ASR) of Alkali-Activated Cement Free Binders.” Thesis (PhD). Clarkson University, New York, USA.
25. 25) Lloyd, R. R., Provis, J. L. and Van Deventer, J. S. J., (2010). “Pore solution composition and alkali diffusion in inorganic polymer cement.” Cement and Concrete Research, 40(9), 1386-1392.10.1016/j.cemconres.2010.04.008 ↗
26. 26) Lothenbach, B., Scrivener, K. and Hooton, R. D., (2011). “Supplementary cementitious materials.” Cement and Concrete Research, 41(12), 1244-1256.10.1016/j.cemconres.2010.12.001 ↗
27. 27) Ma, Y., Hu, J., and Ye, G., (2013). “The pore structure and permeability of alkali activated fly ash.” Fuel, 104, 771-780.10.1016/j.fuel.2012.05.034 ↗
28. 28) Malhotra, V. M., (2002). “High-performance high-volume fly ash concrete.” Concrete International, 24(7), 30-34.
29. 29) Malhotra, V. M. and Mehta, P. K., (2002). “High-performance, high-volume fly ash concrete: materials, mixture proportioning, properties, construction practice, and case histories.” Ottawa, Canada: Supplementary Cementing Materials for Sustainable Development Inc.
30. 30) Malvar, L. J., Cline, G. D., Burke, D. F., Rollings, R., Sherman, T. W. and Greene, J. L., (2002). “Alkali-silica reaction mitigation: state of the art and recommendations.” Materials Journal, 99(5), 480-489.
31. 31) Malvar, L. J. and Lenke, L. R., (2006). “Efficiency of fly ash in mitigating alkali-silica reaction based on chemical composition.” ACI Materials Journal, 103(5), 319-326.
32. 32) Maraghechi, H., Rajabipour, F., Pantano, C. G. and Burgos, W. D., (2016). “Effect of calcium on dissolution and precipitation reactions of amorphous silica at high alkalinity.” Cement and Concrete Research, 87, 1-13.10.1016/j.cemconres.2016.05.004 ↗
33. 33) McKeen, R. G., Lenke, L. R., Pallachulla, K. K. and Barringer, W. L., (2000). “Mitigation of alkali-silica reactivity in New Mexico.” Transportation Research Record: Journal of the Transporatation Research Board, 1698(1), 9-16.10.3141/1698-02 ↗
34. 34) Mehta, P. K., (2004). “High-performance, high-volume fly ash concrete for sustainable development.” In: Proceedings of the International Workshop on Sustainable Development and Concrete Technology, Beijing, China 20-21 May 2004, 3-14.
35. 35) Mota, B., Matschei, T. and Scrivener, K., (2018). “Impact of NaOH and Na2SO4 on the kinetics and microstructural development of white cement hydration.” Cement and Concrete Research, 108, 172-185.10.1016/j.cemconres.2018.03.017 ↗
36. 36) Nath, P. and Sarker, P. K., (2015). “Use of OPC to improve setting and early strength properties of low calcium fly ash geopolymer concrete cured at room temperature.” Cement and Concrete Composites, 55, 205-214.10.1016/j.cemconcomp.2014.08.008 ↗
37. 37) Nedeljkovic, M., Arbi, K., Zuo, Y. and Ye, G., (2016). “Physical properties and pore solution analysis of alkali-activated fly ash-slag pastes.” In: M. Azenha, I. Gabrijel, D. Schlicke, T. Kanstad and O. M. Jensen, Eds. Proceedings of the International RILEM Conference Materials Systems and Structures in Civil Engineering (MSSCE 2016) on Concrete with Supplementary Cementitious Materials. Lyngby, Denmark 15-29 August 2016. Paris, France: RILEM Publications, 22-24.
38. 38) Neves, J. M., (2016). “The alkali-silica reaction in alkali-activated fly ash concrete.” Thesis (MSc). The Pennsylvania State University, Pennsylvania, USA.
39. 39) Oh, J. E., Monteiro, P. J. M., Jun, S. S., Choi, S. and Clark, S. M., (2010). “The evolution of strength and crystalline phases for alkali-activated ground blast furnace slag and fly ash-based geopolymers.” Cement and Concrete Research, 40(2), 189-196.10.1016/j.cemconres.2009.10.010 ↗
40. 40) Palomo, A., Fernández-Jiménez, A., Kovalchuk, G., Ordoñez, L. M. and Naranjo, M. C., (2007). “OPC-fly ash cementitious systems: study of gel binders produced during alkaline hydration.” Journal of Materials Science, 42(9), 2958-2966.10.1007/s10853-006-0585-7 ↗
41. 41) Palomo, A., Grutzeck, M. W. and Blanco, M. T., (1999). “Alkali-activated fly ashes: a cement for the future.” Cement and Concrete Research, 29(8), 1323-1329.10.1016/S0008-8846(98)00243-9 ↗
42. 42) Pepper, L. and Mather, B., (1959). “Effectiveness of mineral admixtures in preventing excessive expansion of concrete due to alkali-aggregate reaction.” Proceedings of the American Society Testing & Materials, 59, 1178-1203.
43. 43) Rajabipour, F., Giannini, E., Dunant, C., Ideker, J. H. and Thomas, M. D. A., (2015). “Alkali-silica reaction: current understanding of the reaction mechanisms and the knowledge gaps.” Cement and Concrete Research, 76, 130-146.10.1016/j.cemconres.2015.05.024 ↗
44. 44) Saha, A. K., Khan, M. N. N., Sarker, P. K., Shaikh, F. A. and Pramanik, A., (2018). “The ASR mechanism of reactive aggregates in concrete and its mitigation by fly ash: A critical review.” Construction and Building Materials, 171, 743-758.10.1016/j.conbuildmat.2018.03.183 ↗
45. 45) Shehata, M. H. and Thomas, M. D. A., (2000). “The effect of fly ash composition on the expansion of concrete due to alkali-silica reaction.” Cement and Concrete Research, 30(7), 1063-1072.10.1016/S0008-8846(00)00283-0 ↗
46. 46) Shehata, M. H. and Thomas, M. D. A., (2002). “Use of ternary blends containing silica fume and fly ash to suppress expansion due to alkali-silica reaction in concrete.” Cement and Concrete Research, 32(3), 341-349.10.1016/S0008-8846(01)00680-9 ↗
47. 47) Somna, K., Jaturapitakkul, C., Kajitvichyanukul, P. and Chindaprasirt, P., (2011). “NaOH-activated ground fly ash geopolymer cured at ambient temperature.” Fuel, 90(6), 2118-2124.10.1016/j.fuel.2011.01.018 ↗
48. 48) Swamy, R. N., (2002). “The alkali-silica reaction in concrete.” London: CRC Press, Taylor & Francis Group.
49. 49) Tarnopol, M. S. and Junge, A. E., (1946). “Resistance of plate glass to alkaline solutions.” Journal of the American Ceramic Society, 29(2), 36-39.10.1111/j.1151-2916.1946.tb11547.x ↗
50. 50) Thomas, M., (2001). “The role of calcium hydroxide in alkali recycling in concrete.” In: J. P. Skalny, J. Gebauer and I. Odler Eds. Materials Science of Concrete: Special Volume, 225-236.
51. 51) Thomas, M., (2011). “The effect of supplementary cementing materials on alkali-silica reaction: A review.” Cement and Concrete Research, 41(12), 1224-1231.10.1016/j.cemconres.2010.11.003 ↗
52. 52) Vayghan, A. G., Rajabipour, F. and Rosenberger, J. L., (2016). “Composition-rheology relationships in alkali-silica reaction gels and the impact on the gel’s deleterious behavior.” Cement and Concrete Research, 83, 45-56.10.1016/j.cemconres.2016.01.011 ↗
53. 53) Velandia, D. F., Lynsdale, C. J., Provis, J. L. and Ramirez, F., (2018). “Effect of mix design inputs, curing and compressive strength on the durability of Na2SO4-activated high volume fly ash concretes.” Cement and Concrete Composites, 91, 11-20.10.1016/j.cemconcomp.2018.03.028 ↗
54. 54) Williamson, T. and Juenger, M. C. G., (2016). “The role of activating solution concentration on alkali-silica reaction in alkali-activated fly ash concrete.” Cement and Concrete Research, 83, 124-130.10.1016/j.cemconres.2016.02.008 ↗
55. 55) Wright, J. R., Shafaatian, S. and Rajabipour, F., (2014). “Reliability of chemical index model in determining fly ash effectiveness against alkali-silica reaction induced by highly reactive glass aggregates.” Construction and Building Materials, 64, 166-171.10.1016/j.conbuildmat.2014.04.042 ↗
56. 56) Ye, H. and Radlińska, A., (2017). “Effect of alkalis on cementitious materials: understanding the relationship between composition, structure, and volume change mechanism.” Journal of Advanced Concrete Technology, 15(4), 165-177.10.3151/jact.15.165 ↗
57. 57) Ye, H., Radlińska, A. and Neves, J., (2017). “Drying and carbonation shrinkage of cement paste containing alkalis.” Materials and Structures, 50(2), 1-13.10.1617/s11527-017-1006-x ↗