Effects of Cement Brand on the Macro-performance and Microstructure of Self-compacting Concrete under Freeze-thaw Cycles
Source abstract
Abstract
Three self-compacting concrete (SCC) mixtures using different cements from the Xizang Autonomous Region were tested for macro-performance before freeze-thaw cycles (FTCs) via rheological, compressive, and splitting tensile strength tests. After FTCs, mass loss rate, relative dynamic elastic modulus (RDEM), and compressive strength were assessed, with scanning electron microscope and mercury intrusion porosimetry used for microstructural analysis. Damage and service life prediction models based on the Weibull distribution were established using mass loss rate and RDEM as failure indicators. Concurrently, a comprehensive evaluation model was developed, integrating compressive strength, freeze-thaw resistance, and material cost. Results show that cement with large negative zeta potential gives SCC better flowability. Lower total porosity correlates with higher compressive strength before FTCs. After 250 FTCs, compressive strength loss and porosity increase are proportional. Within 200 FTCs, lower porosity reduces mass loss and raises RDEM. After 250 FTCs, fewer harmful and highly harmful pores lead to lower mass loss and better RDEM. Damage models were employed to predict SCC the service life of SCC, followed by comprehensive evaluations of the mixtures. These analyses provide valuable guidance for selecting suitable cement brands for construction projects in the Xizang Autonomous Region.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Concrete Properties and Behavior · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Civil and Transportation Engineering, Hohai University, Nanjing, 210098, China.
College of Water Conservancy and Civil Engineering, Xizang Agricultural and Animal Husbandry University, Linzhi, 860000, China.
Research Center of Civil, Hydraulic and Power Engineering of Xizang, Xizang Agricultural and Animal Husbandry University, Linzhi, 860000, China.
College of Mechanics and Engineering Science, Hohai University, Nanjing, 211100, China.
References (48)
Show source-provided references
1. 1) Alkaysi, M., El-Tawil, S., Liu, Z., & Hansen, W. (2016). Effects of silica powder and cement type on durability of ultra high performance concrete (UHPC). Cement and Concrete Composites, 66, 47-56.10.1016/j.cemconcomp.2015.11.005 ↗
2. 2) Bamigboye, G. O., Ede, A. N., Egwuatu, C. S., Jolayemi, J. K., Olowu, O., & Odewumi, T. J. C. (2015). Assessment of compressive strength of concrete produced from different brands of Portland cement. International Journal of Civil and Environmental Research, 7(8), 1081-1092.
3. 3) Bentz, D. P., Garboczi, E. J., Haecker, C. J., & Jensen, O. M. (1999). Effects of cement particle size distribution on performance properties of Portland cement-based materials. Cement and Concrete Research, 29(10), 1663-1671.10.1016/S0008-8846(99)00163-5 ↗
4. 4) Celik, I. B. (2009). The effects of particle size distribution and surface area upon cement strength development. Powder Technology, 188(3), 272-276.10.1016/j.powtec.2008.05.007 ↗
5. 5) Chen, J. J., & Kwan, A. K. H. (2012). Superfine cement for improving packing density, rheology and strength of cement paste. Cement and Concrete Composites, 34(1), 1-10.10.1016/j.cemconcomp.2011.09.006 ↗
6. 6) CPP. (2021). Technical specification for application of self-compacting concrete (T/CECS 203-2021). Beijing: China Planning Press (CPP).
7. 7) Daimon, M., & Roy, D. M. (1978). Rheological properties of cement mixes: I. Methods, preliminary experiments, and adsorption studies. Cement and Concrete Research, 8(6), 753-764.10.1016/0008-8846(78)90084-4 ↗
8. 8) Divanedari, H., & Eskandari-Naddaf, H. (2020). Insights into surface crack propagation of cement mortar with different cement fineness subjected to freezing/thawing. Construction and Building Materials, 233, 117207.10.1016/j.conbuildmat.2019.117207 ↗
9. 9) Elmahdy, E. E. (2015). A new approach for Weibull modeling for reliability life data analysis. Applied Mathematics and Computation, 250, 708-720.10.1016/j.amc.2014.10.036 ↗
10. 10) Ge, H., Sun, Z., Lu, Z., Yang, H., Zhang, T., & He, N. (2024). Influence and mechanism analysis of different types of water reducing agents on volume shrinkage of cement mortar. Journal of Building Engineering, 82, 108392.10.1016/j.jobe.2023.108204 ↗
11. 11) He, L., Wang, J., Wu, X., Wang, G., Wang, Y., & Chu, H. (2023a). A novel fatigue cohesive model for interface between ballastless track slab and self-compacting concrete. Construction and Building Materials, 377, 130962.10.1016/j.conbuildmat.2023.130962 ↗
12. 12) He, R., & Lu, N. (2024a). Air void system and freezing-thawing resistance of concrete composite with the incorporation of thermo-expansive polymeric microspheres. Construction and Building Materials, 419, 135535.10.1016/j.conbuildmat.2024.135535 ↗
13. 13) He, R., & Lu, N. (2024b). Hydration, fresh, mechanical, and freeze-thaw properties of cement mortar incorporated with polymeric microspheres. Advanced Composites and Hybrid Materials, 7(3), 092.10.1007/s42114-024-00899-2 ↗
14. 14) He, R., Nantung, T., & Lu, N. (2024). Unraveling microstructural evolution in air-entrained mortar and paste: Insights from MIP and micro-CT tomography amid cyclic freezing-thawing damage. Journal of Building Engineering, 94, 109922.10.1016/j.jobe.2024.109922 ↗
15. 15) He, R., Nantung, T., Olek, J., & Lu, N. (2023b). Field study of the dielectric constant of concrete: A parameter less sensitive to environmental variations than electrical resistivity. Journal of Building Engineering, 74, 106938.10.1016/j.jobe.2023.106938 ↗
16. 16) Jin, F., Huang, D., Lino, M., & Zhou, H. (2024). A brief review of rock-filled concrete dams and prospects for next-generation concrete dam construction technology. Engineering, 32, 99-105.10.1016/j.eng.2023.09.020 ↗
17. 17) Kazmi, S. M. S., Munir, M. J., Wu, Y.-F., Patnaikuni, I., Zhou, Y., & Xing, F. (2020). Effect of different aggregate treatment techniques on the freeze-thaw and sulfate resistance of recycled aggregate concrete. Cold Regions Science and Technology, 178, 103126.10.1016/j.coldregions.2020.103126 ↗
18. 18) Kim, B.-G., Jiang, S., Jolicoeur, C., & Aï-tcin, P.-C. (2000). The adsorption behavior of PNS superplasticizer and its relation to fluidity of cement paste. Cement and Concrete Research, 30(6), 887-893.10.1016/S0008-8846(00)00256-8 ↗
19. 19) Li, C., Jiang, L., Xu, N., & Jiang, S. (2018). Pore structure and permeability of concrete with high volume of limestone powder addition. Powder Technology, 338, 416-424.10.1016/j.powtec.2018.07.054 ↗
20. 20) Li, G. (2023). Thoroughly implement the spirit of the 20th National Congress of the Communist Party of China and solidly promote the high quality development of water conservancy in the new stage. Water Resource Development Research, 23(1), 1-11. (in Chinese)
21. 21) Li, S., Chen, G., Ji, G., & Lu, Y. (2014). Quantitative damage evaluation of concrete suffered freezing–thawing by DIP technique. Construction and Building Materials, 69, 177-185.10.1016/j.conbuildmat.2014.07.072 ↗
22. 22) Li, Z., Zhang, W., & Liu, L. (2024). Boosting high-quality development of water conservancy by vigorously developing new quality productive forces - Understanding and thoughts on developing new quality productive forces in the water sector. Water Resource Development Research, 24(6), 21-25. (in Chinese)
23. 23) Long, G. C., Liu, H., Ma, K. L., Xie, Y. J., & Li, W. G. (2018). Development of high-performance self-compacting concrete applied as the filling layer of high-speed railway. Journal of Materials in Civil Engineering, 30(2), 017268.10.1061/(ASCE)MT.1943-5533.0002129 ↗
24. 24) Lu, H., Bao, W., & Yin, Y. (2024). Durability deterioration mechanism and carbonation depth prediction model of tunnel lining concrete in high-altitude cold area under low-pressure-freeze-thaw conditions. Construction and Building Materials, 456, 139259.10.1016/j.conbuildmat.2024.139259 ↗
25. 25) MOHURD. (2024). Standard for test methods of long-term performance and durability of ordinary concrete (GB/T 50082-2024). Beijing: Ministry of Housing and Urban-Rural Development of the People's Republic of China (MOHURD).
26. 26) Okamura, H., & Ouchi, M. (2003). Self-compacting concrete. Journal of Advanced Concrete Technology, 1(1), 5-15.10.3151/jact.1.5 ↗
27. 27) Sebaibi, N., Benzerzour, M., Sebaibi, Y., & Abriak, N. (2013). Composition of self compacting concrete (SCC) using the compressible packing model, the Chinese method and the European standard. Construction and Building Materials, 43, 382-388.10.1016/j.conbuildmat.2013.02.028 ↗
28. 28) Shen, Y., Liu, J., Zhou, S., & Li, G. (2019). Experimental investigation on the freeze–thaw durability of concrete under compressive load and with joints. Construction and Building Materials, 229, 116893.10.1016/j.conbuildmat.2019.116893 ↗
29. 29) Taheri, B. M., Ramezanianpour, A. M., Sabokpa, S., & Gapele, M. (2021). Experimental evaluation of freeze-thaw durability of pervious concrete. Journal of Building Engineering, 33, 101617.10.1016/j.jobe.2020.101617 ↗
30. 30) Wang, A., Zhang, C., & Zhang, N. (1997). Study of the influence of the particle size distribution on the properties of cement. Cement and Concrete Research, 27(5), 685-695.10.1016/S0008-8846(97)00060-4 ↗
31. 31) Wang, A., Zhang, C., & Zhang, N. (1999). The theoretic analysis of the influence of the particle size distribution of cement system on the property of cement. Cement and Concrete Research, 29(11), 1721-1726.10.1016/S0008-8846(99)00148-9 ↗
32. 32) Wang, X., Shen, X., Wang, H., Gao, C., & Zhang, T. (2016). Nuclear magnetic resonance analysis of freeze-thaw damage in natural pumice concrete. Materiales de Construcción, 66(322), e087.10.3989/mc.2016.09014 ↗
33. 33) Wang, Y., Yang, W., Ge, Y., Liu, P., & Zhang, A. (2022). Analysis of freeze-thaw damage and pore structure deterioration of mortar by low-field NMR. Construction and Building Materials, 319, 126097.10.1016/j.conbuildmat.2021.126097 ↗
34. 34) Wu, H., Jin, W.-L., Yan, Y., & Xia, J. (2012). Environmental zonation and life prediction of concrete in frost environments. Journal of Zhejiang University. Engineering Science, 46(4), 650-657.
35. 35) Wu, H., Liu, Z., Sun, B., & Yin, J. (2016). Experimental investigation on freeze–thaw durability of Portland cement pervious concrete (PCPC). Construction and Building Materials, 117, 63-71.10.1016/j.conbuildmat.2016.04.130 ↗
36. 36) Wu, Z., & Lian, H. (1999). High performance concrete. Beijing: China Railway Press. (in Chinese)
37. 37) Xue, G., Zhu, H., Xu, S., & Dong, W. (2023). Fatigue performance and fatigue equation of crumb rubber concrete under freeze–thaw cycles. International Journal of Fatigue, 168, 107456.10.1016/j.ijfatigue.2022.107456 ↗
38. 38) Zhang, D., Mao, M., Zhang, S., & Yang, Q. (2019). Influence of stress damage and high temperature on the freeze–thaw resistance of concrete with fly ash as fine aggregate. Construction and Building Materials, 229, 116845.10.1016/j.conbuildmat.2019.116845 ↗
39. 39) Zhang, J., Hu, C., Shen, D., Nie, D., Qin, X., & An, X. (2025a). Effects of fly ash content on the macro-performance and microstructure of self-compacting concrete using tuff powder under freeze-thaw cycles. Case Studies in Construction Materials, e04926.10.1016/j.cscm.2025.e04926 ↗
40. 40) Zhang, J., Yan, G., Shen, D., Pingcuo, Z., Han, X., & An, X. (2025b). Influence of powder characteristics on paste rheological thresholds of self-compacting concrete: A case study of cement and tuff powder from Xizang, China. Journal of Materials in Civil Engineering (accepted for publication in December 2025 issue).
41. 41) Zhang, K., Zhou, J., & Yin, Z. (2021). Experimental study on mechanical properties and pore structure deterioration of concrete under freeze–thaw cycles. Materials, 14(18), 5340.10.3390/ma14216568 ↗
42. 42) Zhang, S., & Zhao, B. (2013). Research on the performance of concrete materials under the condition of freeze-thaw cycles. European Journal of Environmental and Civil Engineering, 17(9), 860-871.10.1080/19648189.2013.826601 ↗
43. 43) Zhang, T., Yu, Q., Wei, J., & Zhang, P. (2011). Effects of size fraction on composition and fundamental properties of Portland cement. Construction and Building Materials, 25(7), 3038-3043.10.1016/j.conbuildmat.2011.01.005 ↗
44. 44) Zhang, Y., Yan, Z., Ju, J. W., Zhu, H., & Chen, Q. (2017). A multi-level micromechanical model for elastic properties of hybrid fiber reinforced concrete. Construction and Building Materials, 152, 804-817.10.1016/j.conbuildmat.2017.07.024 ↗
45. 45) Zheng, X., Wang, Y., Zhang, S., Xu, F., Zhu, X., Jiang, X., Zhou, L., Shen, Y., Chen, Q., Yan, Z., Zhao, W., Zhu, H., & Zhang, Y. (2022). Research progress of the thermophysical and mechanical properties of concrete subjected to freeze-thaw cycles. Construction and Building Materials, 330, 127254.10.1016/j.conbuildmat.2022.127254 ↗
46. 46) Zhu, X., Bai, Y., Chen, X., Tian, Z., & Ning, Y. (2022). Evaluation and prediction on abrasion resistance of hydraulic concrete after exposure to different freeze-thaw cycles. Construction and Building Materials, 316, 126055.10.1016/j.conbuildmat.2021.126055 ↗
47. 47) Zhu, X., Chen, X., & Zhang, N. (2021a). Experimental and numerical investigation on cyclic triaxial behavior of self-compacting concrete subjected to freeze–thaw damage. International Journal of Fatigue, 149, 106277.10.1016/j.ijfatigue.2021.106277 ↗
48. 48) Zhu, X., Chen, X., Zhang, N., Wang, X., & Diao, H. (2021b). Experimental and numerical research on triaxial mechanical behavior of self-compacting concrete subjected to freeze–thaw damage. Construction and Building Materials, 288, 123110.10.1016/j.conbuildmat.2021.123110 ↗