High strength mullite-bond SiC porous ceramics fabricated by digital light processing

Fabricating SiC ceramics via the digital light processing (DLP) technology is of great challenges due to the strong light absorption and high refractive index of deep-colored SiC powders, which highly differ from those of resin and therefore, significantly affect the curing performance of the photosensitive SiC slurry. In this paper, a thin silicon oxide (SiO₂) layer was in-situ formed on the surface of SiC powders by pre-oxidation treatment. This method was proven to effectively improve the curing ability of SiC slurry. The SiC photosensitive slurry was fabricated with a solid content of 55 vol% and viscosity of 7.77 Pa·s (shear rate of 30 s^-1). The curing thickness was 50 μm with an exposure time of only 5 s. Then, a well-designed sintering additive was added to completely convert the low-strength SiO₂ into mullite reinforcement during sintering. Complex-shaped mullite-bond SiC ceramics were successfully fabricated. The flexural strength of the SiC ceramics sintered at 1550 ℃ in air reached 97.6 MPa with a porosity of 39.2 vol%, as high as those prepared by SPS techniques.