Microstructure characterization and formability assessment of electron beam welded Nb-10Hf-1Ti (wt.%) refractory alloy sheets
Source abstract
Abstract
Formability study on welded blanks of Nb-based refractory alloy C-103 (Nb-10Hf-1Ti (wt.%)) has tremendous potential for utilizing smaller sheets for realization of large-size divergent portions of upper-stage liquid engine nozzle of satellite launch vehicles and thrusters of attitude orbital control systems. In this work, vacuum-annealed monolithic C-103 sheets were electron beam welded successfully to obtain defect-free welds and detailed microstructural and mechanical characterizations were investigated. Columnar epitaxial grains were found in fusion zone (FZ) instead of equiaxed grains in base metal (BM). Detailed SEM and HRTEM analyses revealed spherical shape of nano-sized HfO 2 precipitates with monoclinic crystal structure in the C-103 sheet. Further, microhardness across the weld cross-section indicated that the FZ had a uniform and maximum hardness of ∼195 HV 0.5 due to formation of finer nano-sized HfO 2 precipitates with higher number density, followed by a lowering of hardness in a narrow heat-affected zone. A marginal reduction in tensile strength of ∼6% with a considerable decrease in ductility of ∼29% was noticed for the welded sample. However, fracture occurred in the BM region, indicating good weld integrity. Furthermore, formability of the welded blanks was evaluated in terms of limiting dome height (LDH), forming limit diagram, and deep drawn cup depth. The effect of the presence of WZ on the formability of the C-103 sheet was estimated under uniaxial, plane strain, and biaxial tensile strain paths for the first time, and the results were compared with the monolithic sample. It was noted that the failure limit of the welded specimens decreased compared to that of the monolithic sample, resulting in a lower LDH of approximately 69% and 62% when deformed along plane strain and biaxial tensile strain paths, respectively. However, a marginal variation in LDH was observed for the uniaxial strain path. Also, the welded blank had more resistance to material flow into the die cavity due to the harder weld region, resulting in a reduction of deep drawn cup depth by 52% than that of the monolithic blank. The overall results concluded that the presence of the WZ significantly affected the formability of the C-103 sheet, especially in plane strain and biaxial strain paths. However, the fracture was never found to be propagating along the weld line, indicating the ability of the weld to sustain large plastic strains. This study provides insightful information on the formability of electron beam welded C-103 sheets for the successful fabrication of space components.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. Welding of tantalum and niobium10.1080/09507118909446635 ↗
2. Niobium as mint metal: production–properties–processing10.1016/j.ijrmhm.2005.10.008 ↗
3. Effect of beam current on the microstructure, crystallographic texture and mechanical properties of electron beam welded high purity niobium10.1016/j.matchar.2021.111318 ↗
4. Electron beam welding of difficult-to-weld austenitic stainless steel/Nb-based alloy dissimilar joints without interlayer10.1016/j.vacuum.2017.09.046 ↗
5. Plane strain compression of Nb-10Hf-1Ti alloy: effect on microstructure and Micro-texture10.1007/s12666-021-02205-w ↗
6. A novel experimental setup for in situ oxidation behavior study of Nb/Hf/Ti (C-103) alloy for high temperature environments10.1016/j.matlet.2021.130336 ↗
7. Metallurgical characterization and analysis of locally melted C-103(Nb-10Hf-1Ti) sheet during vacuum heat treatment10.1007/s11668-022-01473-y ↗
8. Materials for Indian space program: an overview10.1007/s41745-021-00284-8 ↗
9. Laser beam weldability of TiZrHfNbTa high entropy alloy and dissimilar weldability to C103 refractory alloy10.1016/j.ijrmhm.2023.106270 ↗
10. Welding, brazing and joining of refractory metals and alloys10.1080/08827509808962487 ↗
11. Powder HIP of pure Nb and C-103 alloy: the influence of powder characteristics on mechanical properties10.1016/j.ijrmhm.2022.105803 ↗
12. Experimental investigation on microstructure and mechanical properties of laser-welded Nb-1% Zr-0.1% C alloy10.1007/s11665-021-05979-8 ↗
13. Electron beam welding studies on Nb-Hf-Ti refractory alloy10.4028/www.scientific.net/MSF.710.608 ↗
14. Tensile behavior of Electron beam-welded and post-weld vacuum-annealed Nb-10% Hf-1% Ti refractory alloy weldments10.1007/s11665-018-3146-8 ↗
15. The microstructure analysis, mechanical properties, and fracture behavior of electron beam welded C-103 niobium-based refractory alloy10.1016/j.jmrt.2023.05.070 ↗
16. An investigation of electron beam welding of Nb-1Zr-0.1C alloy: process parameters and microstructural analysis10.1016/j.jmapro.2017.07.001 ↗
17. Effect of electron beam welding current variations on the microstructure and mechanical properties of Nb-1Zr advanced alloy10.1016/j.vacuum.2018.01.043 ↗
18. Formability assessment of Prestrained automotive grade steel sheets using stress based and polar effective plastic strain-forming limit diagram10.1115/1.4030786 ↗
19. Microstructures and failure analyses of DP980 laser welded blanks in formability context10.1016/j.msea.2015.11.091 ↗
20. Effect of orientation of weld line on formability of Electron beam-welded dissimilar thickness titanium sheets10.1007/s11665-018-3689-8 ↗
21. Investigation of cracks generated in columbium alloy (C-103) sheets during deep drawing operation10.1007/s11668-010-9341-z ↗
22. ASTM E517-19: standard test method for plastic strain ratio for sheet metal
23. 22 standard test methods for tension testing of metallic materials
24. Microstructure, forming limit diagram, and strain distribution of pre-strained DP-IF steel tailor–welded blank for auto body application10.1007/s00170-019-03938-1 ↗
25. Deep drawability of electron beam welded tailored blanks of commercially pure titanium thin sheets
26. Microstructures, forming limit and failure analyses of Inconel 718 sheets for fabrication of aerospace components10.1007/s11665-017-2547-4 ↗
27. Effect of internal oxidation on the microstructure and mechanical properties of C-103 alloy10.1016/j.msea.2013.02.057 ↗
28. The role of the metal-oxide Interface’s terminating layer on the selective cold cracking of a commercial niobium–hafnium–titanium (C-103) alloy10.1016/j.jallcom.2020.157427 ↗
29. On the occurrence of dynamic strain aging in C-103 Nb based alloy10.1016/j.msea.2014.10.016 ↗
30. Investigations into the influence of weld zone on formability of Fiber laser-welded advanced high strength steel10.1007/s11665-014-0881-3 ↗
31. Prediction of earing defect and deep drawing behavior of commercially pure titanium sheets using CPB06 anisotropy yield theory10.1016/j.jmapro.2018.05.003 ↗
32. Influence of SC-HAZ microstructure on the mechanical behavior of Si-TRIP steel welds10.1016/j.msea.2018.01.108 ↗
33. Warm redrawing of AA6082 sheets and investigations into the effect of aging heat treatment on cup wall strength10.1016/j.msea.2019.138445 ↗
34. Effect of solution treatment on deep drawability of IN718 sheets: experimental analysis and metallurgical characterization10.1016/j.msea.2018.04.110 ↗
35. Limiting drawing ratio and deep drawing behavior of dual phase steel tailor welded blanks: FE simulation and experimental validation10.1016/j.jmatprotec.2014.10.022 ↗
36. Deep drawing and redrawing of solution-treated cu-Cr-Zr-Ti alloy sheets and post-forming characterization of the redrawn cup wall10.1007/s43452-023-00754-z ↗