Synthesis of scheelite with wolframite and calcium carbonate by a direct solid-state synthesis route
Source abstract
Abstract
Abstract Scheelite was successfully prepared by solid-state calcination synthesis using wolframite [(Fe,Mn)WO 4 ] and calcium carbonate as materials in air atmosphere. The effects of processing parameters, such as calcination temperature, holding time and calcium carbonate dosage on conversion ratio of wolframite were investigated. The conversion of wolframite increased with increasing of temperature, holding time and calcium carbonate dosage. The results demonstrated that 97.58% of wolframite was converted to scheelite in 2 h at temperature of 800 °C under the condition of calcium carbonate stoichiometric ratio of 1.3, and the corresponding reaction products are scheelite, iron oxide and manganese dioxide.
Source: openaire · Quality: candidate unverified · Source record ↗
References (17)
Show source-provided references
1. Wan · 2011
2. The investigation of dissolution behavior of gangue materials during the dissolution of scheelite concentrate in oxalic acid solution10.1016/j.hydromet.2013.02.013 ↗
3. Processing of tungsten
4. Kinetics of the decomposition of scheelite concentrate by leachex process
5. Extracting tungsten from scheelite concentrate with caustic soda by autoclaving process10.1016/j.hydromet.2011.03.004 ↗
6. Production of high purity APT from scheelite and complex tungsten raw material with high Mo content10.1016/S1003-6326(08)60064-3 ↗
7. Studies on the recovery of tungsten from a composite wolframite–scheelite concentrate10.1016/S0304-386X(00)00126-2 ↗
8. Leaching kinetics of scheelite in hydrochloric acid solution containing hydrogen peroxide as complexing agent10.1016/j.hydromet.2014.02.006 ↗
9. Ion exchange hydrometallurgy of tungsten using anion exchangers with long-chained cross-linking agents10.1016/S0304-386X(99)00041-9 ↗
10. Adsorption behaviour of WO4 2− onto 201×7 resin in highly concentrated tungstate solutions10.1016/j.ijrmhm.2010.04.005 ↗
11. The Advance and development of APT's environment-friendly smelting technology in Zhangyuan Tungsten Co., Ltd
12. L.S. Wan, L.F. Zhao, Z.H. Huang, et al. A method of decomposing scheelite with ammonium salt. Chinese patent, 102154547 B.2011-03-14 (in Chinese).10.4236/ib.2011.32018 ↗
13. Tungsten recovery from alkaline leach solutions as synthetic scheelite10.1016/j.hydromet.2006.08.007 ↗
14. Control of calcium tungstate granularity and the recycle of tungsten from the scheelite mother liquor
15. Preparation of different particles artificial scheelite
16. Hallimond tube flotation of scheelite and calcite with amines10.1016/0301-7516(78)90011-X ↗
17. The surface chemical properties of scheelite (CaWO4) II. Collector adsorption and recovery of fine scheelite particles at the iso-octane/water interface10.1016/0166-6622(87)80119-1 ↗