Effect of Double Cold Rolling and Annealing on Texture Evolution and Mechanical Response of Ultrathin Ferritic Steel

The influence of double continuous cold rolling followed by annealing on the texture evolution and mechanical properties of a commercial low-carbon ferritic steel was investigated. Ultrathin sheets (final thickness 0.22 mm) were produced through a two-stage cold rolling process with intermediate and final annealing at 690 °C for 35 s, followed by light temper rolling at 100 °C for 20 s. Texture evolution was characterized using Electron Backscatter Diffraction (EBSD) with Orientation Imaging Microscopy (OIM), producing pole figures and orientation distribution functions (ODFs). Mechanical properties were evaluated through Vickers microhardness and ultimate tensile strength measurements obtained from three independent locations per sample. Quantitative ODF analysis (φ2 = 45°) revealed that γ-fiber ({111}//ND) intensity increased after each cold reduction stage and decreased after annealing due to recrystallization. The α-fiber (110/RD) and cube components (001//RD) showed a slight increase after annealing. The final ultrathin sheet exhibited moderate γ-fiber intensity (≈3 M.R.D), low Vickers microhardness (100–150 HV), and tensile strength (400–450 MPa). These results demonstrate controlled evolution of texture and microstructure during double cold rolling and annealing, providing a basis for future studies on forming-related behavior without directly assessing formability.