Machinability Evaluation of PM Vanadis 4 Extra Steel Under Varying Milling Conditions

Powder metallurgy tool steels, such as Vanadis 4 Extra (1.2210), are increasingly used in cold-work applications due to their superior hardness, wear resistance, and microstructural uniformity. Despite their growing popularity, there is limited data regarding their machinability, especially in milling processes. In this study, experimental milling tests were performed on Vanadis 4 Extra steel using AlCrN-coated carbide tools. A full factorial experimental design (34) was applied to investigate the effects of cutting speed, depth of cut, width of cut, and feed per tooth on cutting forces (Fx, Fy, Fz, Fc), surface roughness parameters (Ra, Rz), and tool wear. Cutting forces were measured using a Kistler dynamometer, and surface roughness was evaluated using a contact profilometer. Regression models were developed and statistically validated. The results indicate that depth of cut had the most significant influence on cutting force, while cutting speed had the greatest impact on surface roughness. Moderate correlation between cutting forces and roughness was observed, particularly under low-load conditions. SEM analysis revealed abrasive wear and chipping of the coating layer. The findings provide insights into the machinability of Vanadis 4 Extra and offer guidelines for optimizing milling parameters to enhance tool life and surface integrity.