The Impact of Hollow Wear on the Stability of High-Speed Railway Vehicles

Hollow wear on wheels is a common form of surface damage often observed in high-velocity vehicles. It is widely recognized that hollow wear of the wheel tread degrades the dynamic performance of rail vehicles, especially in the issue commonly referred to as “operational stability”, and leads to abnormal wheel–rail contact interactions. However, the evaluation criteria for vehicle stability are not uniform, which affects the assessment of wheel conditions and the timing of wheel re-profiling during maintenance. Therefore, numerical simulations were conducted by matching the measured worn wheel profiles with standard rails, and three different methods were employed to evaluate vehicle stability in this article. The numerical results revealed that the wheel equivalent conicity exhibits a nonlinear characteristic caused by hollow wear, which means that the nominal equivalent conicity is unable to accurately represent the geometric contact relationship between the wheel and rail. Under identical wheel wear conditions, a certain difference was observed in the critical speed of the vehicle determined by the velocity-reducing method and the bifurcation configuration method. Both methods were capable of reflecting the impact of wheel hollow wear on vehicle stability at the critical speed. Compared to the velocity-reducing method, the bifurcation configuration method can better reflect the transition process of a vehicle from stable running to hunting instability. Furthermore, the lateral vibration acceleration values measured above the bogie frame indicated that slight wheel wear is insensitive to increased speed. However, when the wear was severe, the lateral vibration acceleration of the bogie was found to increase sharply, exceeding the established stability criteria. This phenomenon was consistent with the safety alarms that occurred during actual vehicle operation, indicating that the vehicle had failed to meet stability requirements.