Effect of a large population of seeded alumina inclusions on crack initiation and small crack fatigue crack growth in Udimet 720 nickel-base disk superalloy
Source abstract
Abstract
Abstract Crack initiation, crack coalescence and small crack growth behavior were monitored for over 400 seeded inclusions during interrupted low cycle fatigue testing conducted on the P/M Udimet 720 nickel disk alloy at 650 °C. Two types of seeded alumina inclusions with average sizes of 54 µm and 122 µm were used in the study performed at varying loading conditions resulting in LCF lives ranging from 2,000 cycles to over 1,000,000 cycles. The fatigue behavior was sub-categorized into four groups. Visual maps detailing inclusion size/cycle history were developed. The effect of surface residual stresses on the fatigue life was also investigated.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · Fatigue and fracture mechanics · Surface Treatment and Residual Stress
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Kantzos P, Bonacuse P, Telesman J, Gabb T, Barrie R, Banik A. Effect of powder cleanliness on the fatigue behavior of powder metallurgy Ni-disk alloy Udimet 720 – superalloys 2004 ed by Green KA, Pollock TM, Harada H, TMS, 2004, p. 409–17.10.7449/2004/Superalloys_2004_409_417 ↗
2. SWRI, DARWIN®, Design assessment of reliability with inspection, Software Code, San Antonio, 2018.
3. Huron E, Roth P. The influence of inclusions on low cycle fatigue life in a P/M nickel-base disk superalloy. In: Kissinger RD, Deye DJ, Anton DL, Cetel AD, Nathal MV, Pollock TM, Woodford DA, editors. Superalloys 1996 The Minerals, Metals & Materials Society, 1996, p. 359–68.10.7449/1996/Superalloys_1996_359_368 ↗
4. Small fatigue crack growth and failure mode transitions in a Ni-base superalloy at elevated temperature10.1016/j.ijfatigue.2010.01.015 ↗
5. On the mechanistic basis of fatigue crack nucleation in Ni superalloy containing inclusions using high resolution electron backscatter diffraction10.1016/j.actamat.2015.06.035 ↗
6. The growth of small fatigue cracks in 7075–T6 Aluminum10.1111/j.1460-2695.1982.tb01251.x ↗
7. The merging of fatigue and fracture mechanics concepts: a historical perspective10.1016/S0376-0421(98)00006-2 ↗
8. Microstructurally sensitive crack nucleation around inclusions in powder metallurgy nickel-based superalloys10.1016/j.actamat.2016.07.023 ↗
9. X-ray characterization of the micromechanical response ahead of a propagating small fatigue crack in a Ni-based superalloy10.1016/j.actamat.2019.08.005 ↗
10. The effect of defects on the fatigue crack initiation process in two P/M superalloys: Part I. Fatigue origins10.1007/BF02642413 ↗
11. Gabb TP, Telesman J, Kantzos P, Bonacuse PJ, Barrie RL. Initial assessment of the effects of non-metallic inclusions on fatigue life of powder metallurgy processed Udimet Alloy 720, NASA TM 211571, 2002.
12. Kantzos PT, Barrie R, Bonacuse P, Gabb T, Telesman J. The effects of forging strain on ceramic inclusions in a disk superalloy. In: Fuchs G, James A, Gabb T, McLean M, Harada H, editors. Advanced materials and processes for gas turbines. The Mining, Metallurgy, and Materials Society, Sept. 2003, p. 245–54.
13. Effectiveness of shot peening in suppressing fatigue cracking at non-metallic inclusions in Udimet® 72010.1016/j.msea.2007.03.100 ↗
14. ASTM E647-15. Standard test method for measurement of fatigue crack growth rates. ASTM International, 2015.
15. ASTM E21-09. Standard test methods for elevated temperature tension tests of metallic materials. ASTM International, 2009.
16. X-ray diffraction residual techniques
17. Fatigue deformation in a polycrystalline nickel base superalloy at intermediate and high temperature: competing failure modes10.1016/j.actamat.2018.03.035 ↗
18. Forman R, Shivakumar V. Growth behavior of surface cracks in the circumferential plane of solid and hollow cylinders. In: Underwood J. et al., editors. Fracture mechanics: seventeenth volume. ASTM International, 1986, p. 59–74.10.1520/STP17388S ↗
19. Newman JC, Jr. A nonlinear fracture mechanics approach to the growth of small cracks. AGARD CP-328, 1983; 6.1-26.
20. Propagation of short fatigue cracks
21. On the development of crack closure and the threshold condition for short and long fatigue cracks in 7150 aluminum alloy10.1007/BF02658679 ↗
22. A literature survey on the stability and significance of residual stresses during fatigue10.1111/j.1460-2695.2007.01102.x ↗
23. Prevey Paul S, Telesman Jack, Gabb Tim, Kantzos Pete. FOD resistance and fatigue crack arrest in low plasticity burnished IN718 in Proceedings: 5th national turbine engine high cycle fatigue conference chandler, AZ, March 7-9, 2000.