A Comparative Study of Arc Welding and Laser Welding for the Fabrication and Repair of Multi-Layer Hydro Plant Bellows
Source abstract
Abstract
The development of clean energy resources, including hydro power, plays an important role in protecting the global environment. Multi-layer bellows are key components and are widely used in hydro power plants. Due to the special multi-layer structures, conventional arc welding is prone to the defects of pores and insufficient fusion when fabricating or repairing such bellows. Precise laser welding with a high energy density and a low heat input has the potential to join multi-layer bellows in a high-quality manner. In this study, a comparative investigation was conducted on the arc welding and laser welding of multi-layer 316L stainless steel sheets and B610CF high-strength steel plates regarding the weld quality, microstructure and tensile properties. The results show that laser-welded joints produced a narrower heat-affected zone and a full weld without visible defects. Compared with arc welding, laser welding had more equiaxed grain regions in the fusion zone and a homogeneous elemental distribution in the heat-affected zone. This led to a more reliable welded joint using laser welding.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Welding Techniques and Residual Stresses · Additive Manufacturing Materials and Processes · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute of Intelligent Manufacturing, Guangdong Academy of Sciences, Guangzhou 510070, China
China Yangtze Power Co., Ltd., No. 1 Jianshe Road, Xiba, Xiling District, Yichang 443002, China
Funding
China Yangtze Power Company Limited
References (35)
Show source-provided references
1. Effect of repeated weld repairs on microstructure and mechanical properties of heat-affected zone in CA6NM stainless steel
2. Extended producer responsibility for fossil fuels10.1088/1748-9326/aca4e8 ↗
3. Key parameters that affect the fatigue life of metal bellows-type expansion joint: Another look10.1016/j.mtcomm.2024.108400 ↗
4. Design and analysis aspect of metal expansion bellows: A review10.1016/j.finmec.2023.100244 ↗
5. Residual stress analysis and measurement in multi-layer bellows10.1016/j.jmapro.2021.10.021 ↗
6. Deformation behaviors of four-layered U-shaped metallic bellows in hydroforming10.1016/j.cja.2020.02.007 ↗
7. Effect of residual stress on the axial buckling behaviour of the hydraulic-formed bellows10.1016/j.ijpvp.2025.105468 ↗
8. Impact of strain on the corrosion resistance of 304 stainless steel welded joints using electrochemical methods and numerical modeling of stress corrosion10.1016/j.ijoes.2024.100910 ↗
9. On the Si content prediction for submerged arc welded metal via calphad technique: A brief discussion10.1016/j.jmrt.2022.10.028 ↗
10. Study on weld quality characteristics of micro plasma arc welded austenitic stainless steels10.1016/j.proeng.2014.12.305 ↗
11. Mathematical description and mechanical characteristics of reinforced S-shaped bellows10.1016/j.ijpvp.2019.103931 ↗
12. Microstructures and properties of a novel 115 mm thick 08Cr9W3Co3VNbCuBN heat-resistant steel tube joints welded by shielded metal arc welding10.1016/j.ijpvp.2023.104918 ↗
13. Pore formation and its mitigation during hybrid laser/arc welding of advanced high strength steel10.1016/j.matdes.2014.10.072 ↗
14. Laser-arc hybrid welding of 25 mm high strength steel sections10.1016/j.optlastec.2024.112193 ↗
15. Determination of heat input impact on residual stress, microstructure and mechanical characteristics of welded ferrite-pearlite (α-P) steel joints by using taguchi optimization approach10.1016/j.jajp.2024.100278 ↗
16. Thermal cycle method’s applicable conditions for predicting residual stresses in low-strength steel weldments induced by arc welding10.1016/j.tsep.2023.102260 ↗
17. Reliability analysis of thermal cycle method on the prediction of residual stresses in arc-welded ultra-high strength steels10.1016/j.ijthermalsci.2022.108085 ↗
18. Gas tungsten arc welding of CoCrFeMnNi high entropy alloy to 316 stainless steel10.1016/j.msea.2024.147664 ↗
19. Effects of mechanical stress on the corrosion behaviour of an austenitic stainless steel welded joint—Stress corrosion cracking susceptibility10.1016/j.corsci.2024.112629 ↗
20. A review on heat affected zone softening of dual-phase steels during laser welding10.1016/j.jmapro.2023.07.059 ↗
21. All-fiber 3 kW LP02 laser output based on long-period fiber grating for precise welding10.1016/j.optlastec.2024.111047 ↗
22. Experimental study and finite volume modeling of keyhole dynamics, temperature distribution and weld characteristics in laser welding of austenitic stainless steel tube10.1016/j.optlastec.2024.112366 ↗
23. Role of layer arrangement in microstructure and corrosion behavior for 78-mm thick-plate 316L stainless steel fabricated via narrow gap laser wire filling welding10.1016/j.jmrt.2024.06.176 ↗
24. Fusion welding of ultra-high strength structural steels—A review10.1016/j.jmapro.2022.07.049 ↗
25. A review: Suppression of the solidification cracks in the laser welding process by controlling the grain structure and chemical compositions10.1016/j.jajp.2023.100139 ↗
26. Zhou, S., Yan, T., Muneer, W., Yin, X., Gao, Q., and Zhan, X. (2021). Effect of heat input on LMHMW joint of carbon steel. Appl. Sci., 12.10.3390/app12010301 ↗
27. Comparative study on microstructure and properties of laser welding and argon arc welding Hastelloy C-276/SS304 with filler wire10.1016/j.optlastec.2023.109565 ↗
28. A comparative study of the galvanized DP980 steel and 2 GPa PHS welded joint via laser beam welding and cold metal transfer welding10.1016/j.matlet.2024.136726 ↗
29. Investigations on induced residual stresses, mechanical and metallurgical properties of CO2 laser beam and pulse current gas tungsten arc welded SMO 25410.1016/j.jmapro.2019.05.044 ↗
30. (2021). Metallic Materials—Tensile Testing—Part 1: Method of Test at Room Temperature. Standard No. GB/T228.1-2021.
31. Effect of building orientation on weld characteristics of additively manufactured 316L stainless steel: Microstructure and mechanical properties10.1016/j.msea.2024.147086 ↗
32. Shielding gas effects on flux cored arc welding of AISI 316L (N) austenitic stainless steel joints10.1016/j.matdes.2012.09.012 ↗
33. Inhomogeneity of microstructure and mechanical properties in the interlayer regions for narrow gap laser wire filling welding of 316L stainless steel10.1016/j.optlastec.2023.110050 ↗
34. Solidification behavior and texture of 316L austenitic stainless steel by laser wire directed energy deposition10.1016/j.matchar.2024.113916 ↗
35. Synchronous-hammer-forging-assisted laser directed energy deposition additive manufacturing of high-performance 316L samples10.1016/j.jmatprotec.2022.117695 ↗