Formation of SmCo5 single-crystal submicron flakes and textured polycrystalline nanoflakes

B.Z. Cui, W.F. Li, G.C. Hadjipanayis

Acta Materialia· Volume 59· Issue 2
Publisher page

Abstract

Abstract Surfactant-assisted high-energy ball milling (HEBM) of malleable materials has been found to lead to the formation of flakes. However, SmCo 5 magnetic materials are inherently brittle and, therefore, are not expected to “flake” during ball milling. In this study, we report the fabrication of high-aspect-ratio single-crystal flakes with a submicron thickness and textured polynanocrystalline flakes with a submicron or nanosize thickness of SmCo 5 by one-step surfactant-assisted HEBM in heptane with 15 wt.% oleic acid. Single-crystal micron flakes were first formed via a basal cleavage along the easy glide (0 0 1) planes of the initial irregular and large single-crystal particles during the first stage of HEBM. Subsequently, single-crystal submicron flakes were formed by continuous cleavage. With further ball milling, polycrystalline submicron flakes with small-angle grain boundaries were formed. Finally, crystallographically anisotropic polycrystalline SmCo 5 nanoflakes were formed with [0 0 1]-out-of-plane texture, thicknesses of 6–80 nm, average grain sizes of 7–8 nm, an aspect ratio of 10 2 –10 3 and coercivities of 16.3–17.7 kOe. The mechanism responsible for unusual formation of single-crystal submicron flakes and anisotropic nanocrystalline nanoflakes from initial inherently brittle polycrystalline ingots with irregular grains of tens of microns in size is discussed.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Magnetic Properties of Alloys · Metallic Glasses and Amorphous Alloys · Magnetic properties of thin films

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (22)

Show source-provided references
1. Wohlfarth · 1988 · vol. 4
2. Zhang · J Magn Magn Mater · 2004 · 283 · 8910.1016/j.jmmm.2004.04.131 ↗
3. Wan · Scripta Metall Mater · 1995 · 32 · 182710.1016/0956-716X(95)00034-S ↗
4. Liu · Nanostruct Mater · 1999 · 12 · 18710.1016/S0965-9773(99)00095-1 ↗
5. Kirkpatrick · IEEE Trans Magn · 1996 · 32 · 450210.1109/20.538911 ↗
6. Chakka · J Appl Phys · 2006 · 99 · 08E91210.1063/1.2170593 ↗
7. Wang · Nanotechnology · 2007 · 18 · 46570110.1088/0957-4484/18/46/465701 ↗
8. Hadjipanayis · Nanostruct Mater · 1999 · 12 · 116110.1016/S0965-9773(99)00319-0 ↗
9. Zhou · J Alloys Compd · 2008 · 448 · 30310.1016/j.jallcom.2006.10.061 ↗
10. Kao · J Electron Mater · 2004 · 33 · 144510.1007/s11664-004-0085-y ↗
11. Xiao · Mater Sci Eng A · 2008 · 475 · 6610.1016/j.msea.2007.04.084 ↗
12. Chen · Appl Phys Lett · 1999 · 75 · 316510.1063/1.125265 ↗
13. Cui · J Appl Phys · 2010 · 107 · 09A72110.1063/1.3339775 ↗
14. Kocks UF, Kallend JS, Wenk HR, Rollett AD, Wright SI. popLA: preferred orientation package. Los Alamos; 1995.
15. Hu · J Appl Phys · 1990 · 67 · 483810.1063/1.344753 ↗
16. Aikin · Metall Trans A · 1993 · 24 · 246510.1007/BF02646525 ↗
17. Guérard · Rev Adv Mater Sci · 2008 · 18 · 225
18. Kaczmarek · Mater Chem Phys · 1995 · 40 · 2110.1016/0254-0584(94)01450-U ↗
19. Jiang · Int J Plast · 2004 · 20 · 200710.1016/j.ijplas.2003.10.010 ↗
20. Fecht · Nanostruct Mater · 1995 · 6 · 3310.1016/0965-9773(95)00027-5 ↗
21. Vasil’ev · J Mater Sci · 2004 · 39 · 541110.1023/B:JMSC.0000039256.82224.5c ↗
22. Gabay · J Phys Condens Matter · 2010 · 22 · 16421310.1088/0953-8984/22/16/164213 ↗