Hydration Products, Morphology and Microstructure of Activated Slag Cement
Source abstract
Abstract
This paper reports the physical properties and hydration products of slag cement that was prepared by activating ground granulated blast furnace slag with commercial lime and plaster of Paris (POP) as activators. The consistency, setting times and soundness of various mixes of slag-lime-POP is reported. The hydration products and formation of bonds in the paste during setting were studied with the help of SEM, FTIR and XRD tests and the same are correlated to the hydration process. The setting times of the mixes are found to be lower than that of the value prescribed for ordinary Portland cement (OPC). Borax is used as a setting retarder and a borax content of 0.4 % by mass gives setting times that are normally prescribed for OPC. In the early stages of setting C–A–S–H gels are found in this cementing material instead of C–S–H gel, as generally observed in the OPC.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Innovative concrete reinforcement materials · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Benghazi, Z., Zeghichi, L., & Hamdane, A. (2009). Study of alkali activated pozzolana/slag cement. 1st International conference on Sustainable Built Environment Infrastructures in Developing Countries,ENSET Oran (Algeria), 335–342.
2. Bijen, J., & Niel, E. (1981). Super sulphated cement from blast furnace slag and chemical gypsum available in the Netherland and neighboring countries. Cement Concrete Research,11(3), 307–322.10.1016/0008-8846(81)90104-6 ↗
3. Brough, A. R., Holloway, M., Sykes, J., & Atkinson, A. (2000). Sodium silicate based alkali-activator slag mortars: Part II the retarding effect of additions of sodium chloride or malic acid. Cement Concrete Research,30(9), 1375–1379.10.1016/S0008-8846(00)00356-2 ↗
4. Chandra, S. (1996). Waste materials used in concrete manufacturing (pp. 235–282). Westwood, NJ: William Andrew.
5. Chang, J. J. (2003). A study on the setting characteristics of sodium silicate-activated slag pastes. Cement Concrete Research,33, 1005–1011.10.1016/S0008-8846(02)01096-7 ↗
6. Dutta, D. K., & Borthakur, P. C. (1990). Activation of low lime high alumina granulated blast furnace slag by anhydrite. Cement Concrete Research,20(5), 711–722.10.1016/0008-8846(90)90005-I ↗
7. Feret, R. (1939). Revuedes Materiaux de construction et des. Travaux Publics,355, 61.
8. Glukhovsky, V. D., Zaitsev, Y., & Pakhomow, V. (1983). Slag-alkaline cements and concrete structures, properties, technological and economic aspects of the use. SilicInd,10, 197–200.
9. Gong, C., & Yang, N. (2000). Effect of phosphate on the hydration of alkali activated red-mud slag cementious materials. Cement Concrete Research,30(7), 1013–1016.10.1016/S0008-8846(00)00260-X ↗
10. IS: 4031–1988 (PT 4). Method of physical test for hydraulic cement: Part 4 Determination of standard consistency of cement paste, Bureau of Indian Standards, New Delhi, India, 1988.
11. IS: 4031–1988 (PT 5). Method of physical test for hydraulic cement: Part 5 Determination of initial and final setting time, Bureau of Indian Standards, New Delhi, India, 1988.
12. IS: 4031–1988 (PT 3). Method of physical test for hydraulic cement: Part 3 Determination of soundness, Bureau of Indian Standards, New Delhi, India, 1988.
13. Jolibois, P., & Nicol, A. (1952). Revue des Materiaux de construction et des. Travaux Publics,437, 33.
14. Kim, J. C., & Hong, S. Y. (2001). Liquid concentration changes during slag cement hydration by alkali activation. Cement Concrete Research,31(2), 283–285.10.1016/S0008-8846(00)00455-5 ↗
15. Mehrotra, V. P., Sai, A. S. R., & Kapur, P. C. (1982). Plaster of Paris activated super sulfated slag cement. Cement and Concrete Research,12(4), 463–473.10.1016/0008-8846(82)90061-8 ↗
16. Naceri, A., Bouglada, M. S., & Belouar, A. (2011). Activation of slag cement by hydrated lime. Applied Mechanics and Material,71–78, 706–711.10.4028/www.scientific.net/AMM.71-78.706 ↗
17. Naceri, A., Bouglada, M. S., & Grosseau, P. (2009). Mineral activator and physical characteristics of slag cement at anhydrous and hydrated states. World Academy of Science, Engineering and Technology,32, 137–139.
18. Puertas, F., & Fernandez-Jimenez, A. (2003). Mineralogical and microstructure characterization of alkali-activated fly ash/slag pastes. Cement Concrete Composites,25(3), 287–293.10.1016/S0958-9465(02)00059-8 ↗
19. Puertas, F., Palacios, M., Manzano, H., Dolado, J. S., Rico, A., & Rodríguez, J. (2011). A model for the C–A–S–H gel formed in alkali-activated slag cements. Journal of the European Ceramic Society,31(12), 2043–2056.10.1016/j.jeurceramsoc.2011.04.036 ↗
20. Shi, C., & Li, Y. (1989). Investigation on some factors affecting the characteristics of alkali-phosphorus slag. Cement Concrete Research,19(4), 527–533.10.1016/0008-8846(89)90004-5 ↗
21. Talling, B., & Brandstetr, J. (1989). Present state and future of alkali–activated slag concretes fly ash, silica fume, slag, and natural pozzolans in concrete. In Proceedings 3rd International Conference Trondheim, Norway, SP114-74, 1519–1545.
22. Wang, S. D., Pu, X. C., Scrivener, K. L., & Pratt, P. L. (1995). Alkali-activated cement and concrete: A review of properties and problems. Advanced Cement Research,7(27), 93–102.10.1680/adcr.1995.7.27.93 ↗