Effects of high‐temperature exposure on properties of lightweight geopolymer foams incorporating diatomite powders
Source abstract
Abstract
Abstract A kind of metakaolin‐based geopolymer foams incorporating diatomite powders (GKGP) with open cellular was presented by addition of diatomite powder via hydrogen peroxide method. Impacts of high‐temperature exposure on the microstructure, pore structure, and mechanical properties of the GKGP samples were investigated. The GKGP foams achieved a typical amorphous phase structure at room temperature. Open porosity of the samples reached approximately 74%. After high‐temperature exposure treatment, the KGP matrix is basically transformed into leucite crystal phase. The compression strength of the leucite foams was also enhanced with increasing temperature to 1200℃ (9.28 MPa). The lightweight foamed GKGP samples with high open porosity might have great potential for membranes and industries, etc.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Magnesium Oxide Properties and Applications · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Metallurgy Northeastern University Shenyang Liaoning Province P. R. China
Funding
Natural Science Foundation of Liaoning Province · Fundamental Research Funds for the Central Universities
References (69)
Show source-provided references
1. 10.1016/j.scitotenv.2021.14707410.1016/j.scitotenv.2021.147074 ↗
2. 10.1016/j.ecoenv.2015.06.01910.1016/j.ecoenv.2015.06.019 ↗
3. 10.1016/j.ceramint.2017.08.21510.1016/j.ceramint.2017.08.215 ↗
4. 10.1016/j.mspro.2014.07.14910.1016/j.mspro.2014.07.149 ↗
5. 10.1016/j.clay.2019.10539010.1016/j.clay.2019.105390 ↗
6. 10.1016/j.clay.2019.10533310.1016/j.clay.2019.105333 ↗
7. 10.1016/j.jenvman.2018.10.04110.1016/j.jenvman.2018.10.041 ↗
8. 10.1016/j.jclepro.2019.03.05110.1016/j.jclepro.2019.03.051 ↗
9. 10.1016/j.conbuildmat.2019.06.07610.1016/j.conbuildmat.2019.06.076 ↗
10. 10.1016/j.conbuildmat.2014.01.08110.1016/j.conbuildmat.2014.01.081 ↗
11. 10.1016/j.conbuildmat.2019.01.21210.1016/j.conbuildmat.2019.01.212 ↗
12. 10.1016/j.conbuildmat.2006.11.01110.1016/j.conbuildmat.2006.11.011 ↗
13. 10.1016/j.jclepro.2011.03.01210.1016/j.jclepro.2011.03.012 ↗
14. 10.1016/j.matchemphys.2020.12326610.1016/j.matchemphys.2020.123266 ↗
15. 10.1016/j.jmrt.2020.05.03410.1016/j.jmrt.2020.05.034 ↗
16. 10.1007/s40145-019-0352-210.1007/s40145-019-0352-2 ↗
17. 10.1007/s40145-018-0312-210.1007/s40145-018-0312-2 ↗
18. Geopolymer for use in heavy metals adsorption, and advanced oxidative processes: A critical review
19. 10.1016/j.jclepro.2019.01.26810.1016/j.jclepro.2019.01.268 ↗
20. 10.1016/j.conbuildmat.2021.12303010.1016/j.conbuildmat.2021.123030 ↗
21. 10.1016/j.compositesb.2016.02.00210.1016/j.compositesb.2016.02.002 ↗
22. 10.1016/j.cemconcomp.2019.10336110.1016/j.cemconcomp.2019.103361 ↗
23. 10.1016/j.cemconcomp.2019.10334310.1016/j.cemconcomp.2019.103343 ↗
24. 10.1016/j.ceramint.2015.05.07510.1016/j.ceramint.2015.05.075 ↗
25. 10.1016/j.ceramint.2016.06.08010.1016/j.ceramint.2016.06.080 ↗
26. 10.1617/s11527-016-0967-510.1617/s11527-016-0967-5 ↗
27. 10.1016/j.jclepro.2019.01.15510.1016/j.jclepro.2019.01.155 ↗
28. 10.1016/j.compositesb.2017.07.02010.1016/j.compositesb.2017.07.020 ↗
29. 10.1016/j.matdes.2013.09.04910.1016/j.matdes.2013.09.049 ↗
30. 10.1007/s10934-006-9039-510.1007/s10934-006-9039-5 ↗
31. 10.1016/j.cej.2003.11.02910.1016/j.cej.2003.11.029 ↗
32. 10.5004/dwt.2017.2055310.5004/dwt.2017.20553 ↗
33. 10.1016/j.cej.2016.05.10810.1016/j.cej.2016.05.108 ↗
34. 10.1016/j.ceramint.2018.12.08210.1016/j.ceramint.2018.12.082 ↗
35. 10.1016/j.jeurceramsoc.2017.02.03210.1016/j.jeurceramsoc.2017.02.032 ↗
36. 10.1016/j.matchemphys.2019.12174210.1016/j.matchemphys.2019.121742 ↗
37. 10.1016/j.ceramint.2017.07.22210.1016/j.ceramint.2017.07.222 ↗
38. 10.1177/0021955X1769509210.1177/0021955X17695092 ↗
39. 10.1111/jace.1408910.1111/jace.14089 ↗
40. 10.1016/j.ceramint.2016.07.13910.1016/j.ceramint.2016.07.139 ↗
41. 10.1039/C6RA26340B10.1039/C6RA26340B ↗
42. 10.1016/j.cemconcomp.2019.10337610.1016/j.cemconcomp.2019.103376 ↗
43. 10.1016/j.jclepro.2019.04.18510.1016/j.jclepro.2019.04.185 ↗
44. 10.1016/j.matchar.2016.01.01910.1016/j.matchar.2016.01.019 ↗
45. 10.1016/j.ceramint.2018.10.02110.1016/j.ceramint.2018.10.021 ↗
46. 10.1016/j.cemconcomp.2017.03.01010.1016/j.cemconcomp.2017.03.010 ↗
47. 10.1016/j.ceramint.2017.07.19010.1016/j.ceramint.2017.07.190 ↗
48. 10.1016/j.conbuildmat.2017.03.23410.1016/j.conbuildmat.2017.03.234 ↗
49. 10.1007/s40145-018-0289-x10.1007/s40145-018-0289-x ↗
50. 10.1016/j.desal.2010.03.05410.1016/j.desal.2010.03.054 ↗
51. Porosity and fire resistance of fly ash based geopolymer
52. 10.1016/j.clay.2017.02.00210.1016/j.clay.2017.02.002 ↗
53. 10.1016/j.mtla.2021.10108310.1016/j.mtla.2021.101083 ↗
54. 10.1016/j.jobe.2021.10276210.1016/j.jobe.2021.102762 ↗
55. 10.1016/j.matlet.2018.04.01010.1016/j.matlet.2018.04.010 ↗
56. 10.1016/j.jclepro.2016.01.05710.1016/j.jclepro.2016.01.057 ↗
57. 10.1007/s10853-006-0818-910.1007/s10853-006-0818-9 ↗
58. 10.1111/j.1551-2916.2008.02882.x10.1111/j.1551-2916.2008.02882.x ↗
59. 10.1016/j.jnoncrysol.2006.09.01910.1016/j.jnoncrysol.2006.09.019 ↗
60. 10.1016/j.ceramint.2010.08.00810.1016/j.ceramint.2010.08.008 ↗
61. 10.1016/j.powtec.2018.01.09010.1016/j.powtec.2018.01.090 ↗
62. 10.1016/j.jhazmat.2010.09.09910.1016/j.jhazmat.2010.09.099 ↗
63. 10.1016/j.jeurceramsoc.2020.02.05210.1016/j.jeurceramsoc.2020.02.052 ↗
64. 10.1016/j.jeurceramsoc.2021.01.01910.1016/j.jeurceramsoc.2021.01.019 ↗
65. 10.1016/j.jenvman.2019.05.12010.1016/j.jenvman.2019.05.120 ↗
66. 10.1016/j.ceramint.2016.10.20510.1016/j.ceramint.2016.10.205 ↗
67. 10.1016/j.conbuildmat.2017.09.11210.1016/j.conbuildmat.2017.09.112 ↗
68. 10.1016/j.matlet.2017.03.09710.1016/j.matlet.2017.03.097 ↗
69. 10.1016/j.cemconcomp.2015.03.01310.1016/j.cemconcomp.2015.03.013 ↗