Using polystyrene spheres to produce thin, porous interlayers in alumina laminates
Source abstract
Abstract
Abstract Porous alumina layers were produced by colloidal processing of alumina with the addition of 15, 30, and 45 vol% polystyrene spheres (PS) as pore formers. Alumina laminates were designed with dense layers alternated with porous interlayers using 45 vol% of PS spheres and sintered at 1350°C. The layers’ thickness ranged from 2 to 15 μm, with a random distribution of pores. The higher volume fraction of pores tends to decrease the alumina average grain size, but does not influence the final size of bulk and surface pores. The obtained values of hardness and Young's modulus for the porous interlayer are ∼30% of the values obtained for the dense layer. Vickers indentations suggested that crack propagation can be opposed by the porous interlayers. However, values of mechanical strength, fracture toughness ( K IC ), and work of fracture presented no relevant difference compared to a monolithic reference. R ‐curves presented a slight increase and K IC a decrease due to crack propagation through the porous interlayers. Although no macrodeviations of the crack path were observed in the fractured surfaces, microdeviations were detected in the interlayer regions.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Ferroelectric and Piezoelectric Materials · Bone Tissue Engineering Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Laboratory of Ceramics Processing (PROCER) Federal University of Santa Catarina (UFSC) Florianópolis Santa Catarina Brazil
Institute of Advanced Ceramics Hamburg University of Technology (TUHH) Hamburg Germany
Funding
Deutscher Akademischer Austauschdienst · Deutsche Forschungsgemeinschaft · Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
References (24)
Show source-provided references
1. 10.1002/978352762241210.1002/9783527622412 ↗
2. 10.1179/1743676114Y.000000021510.1179/1743676114Y.0000000215 ↗
3. 10.1038/347455a010.1038/347455a0 ↗
4. 10.1016/0956-7151(92)90471-P10.1016/0956-7151(92)90471-P ↗
5. 10.1111/j.1151-2916.2002.tb00480.x10.1111/j.1151-2916.2002.tb00480.x ↗
6. 10.1111/j.1151-2916.1998.tb02438.x10.1111/j.1151-2916.1998.tb02438.x ↗
7. Ceramic laminates with tailored residual stresses
8. 10.1016/0022-3115(65)90146-710.1016/0022-3115(65)90146-7 ↗
9. 10.1016/S0955-2219(02)00430-210.1016/S0955-2219(02)00430-2 ↗
10. 10.1016/S0955-2219(99)00031-X10.1016/S0955-2219(99)00031-X ↗
11. 10.1016/j.jeurceramsoc.2008.07.04810.1016/j.jeurceramsoc.2008.07.048 ↗
12. 10.1016/j.jeurceramsoc.2006.05.05410.1016/j.jeurceramsoc.2006.05.054 ↗
13. 10.1016/j.ceramint.2012.06.04110.1016/j.ceramint.2012.06.041 ↗
14. 10.1016/j.jeurceramsoc.2004.11.00310.1016/j.jeurceramsoc.2004.11.003 ↗
15. 10.1111/j.1151-2916.2001.tb00957.x10.1111/j.1151-2916.2001.tb00957.x ↗
16. 10.1115/1.317607810.1115/1.3176078 ↗
17. 10.1016/S0955-2219(98)00134-410.1016/S0955-2219(98)00134-4 ↗
18. 10.1111/j.1151-2916.2000.tb01563.x10.1111/j.1151-2916.2000.tb01563.x ↗
19. 10.1111/jace.1749010.1111/jace.17490 ↗
20. 10.1557/jmr.2004.19.1.310.1557/jmr.2004.19.1.3 ↗
21. 10.1016/j.jeurceramsoc.2005.03.14710.1016/j.jeurceramsoc.2005.03.147 ↗
22. 10.1007/978-3-642-58407-710.1007/978-3-642-58407-7 ↗
23. 10.1111/jace.1341310.1111/jace.13413 ↗
24. 10.1016/j.jeurceramsoc.2015.06.00310.1016/j.jeurceramsoc.2015.06.003 ↗