Preparation and application of microfiltration porous coal gangue–loess‐based ceramic membrane
Source abstract
Abstract
Abstract The ceramic membrane is widely used in the field of domestic sewage treatment due to its high flexural strength, acid and alkali corrosion resistance, easy cleaning, and other advantages. This article uses coal gangue and loess as the main raw material (coal gangue:loess = 8:2), calcium carbonate as the pore‐forming agent, and carboxymethyl cellulose as the binder. The ceramic membrane was prepared by extrusion molding method and solid particle sintering method. The effects of pore‐forming agent content and sintering temperature on the physical and chemical properties of the ceramic membrane, such as flexural strength, microstructure, pure water flux, and acid‐base corrosion rate, were investigated. The results show that when the sintering temperature is 1000°C and the pore‐forming agent content is 10wt%, the pure water flux exceeds 1434L/h m 2 MPa, the flexural strength exceeds 25.4 MPa, the porosity exceeds 46.9%, and the acid‐alkali corrosion rate of the ceramic membrane below 1.6%/0.15%. At this time, the treatment efficiency of domestic sewage is excellent, the removal rate of COD, suspended solids and ammonia nitrogen exceeds 27.66%, 99.9%, and 26.77%, respectively. This work has trend‐setting significance for the fabrication and application of low‐cost ceramic membranes.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Membrane Separation Technologies · Adsorption and biosorption for pollutant removal · Membrane Separation and Gas Transport
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Shaanxi Science and Technology Holding Group Co. Ltd. Xi'an China
School of Environmental and Chemical Engineering Xi'an Polytechnic University Xi'an China
References (25)
Show source-provided references
1. 10.1016/j.watres.2019.11518010.1016/j.watres.2019.115180 ↗
2. 10.3390/ma1101007410.3390/ma11010074 ↗
3. 10.1016/j.desal.2010.07.05510.1016/j.desal.2010.07.055 ↗
4. 10.1016/j.memsci.2016.03.02310.1016/j.memsci.2016.03.023 ↗
5. 10.1016/j.memsci.2004.03.04710.1016/j.memsci.2004.03.047 ↗
6. 10.1016/j.ceramint.2007.09.11710.1016/j.ceramint.2007.09.117 ↗
7. 10.1016/j.resconrec.2010.05.00510.1016/j.resconrec.2010.05.005 ↗
8. 10.1016/j.fuel.2012.02.02710.1016/j.fuel.2012.02.027 ↗
9. 10.1016/j.coal.2008.04.00310.1016/j.coal.2008.04.003 ↗
10. 10.1016/j.coal.2003.03.00210.1016/j.coal.2003.03.002 ↗
11. 10.1016/j.coal.2007.01.00110.1016/j.coal.2007.01.001 ↗
12. Porous tubular ceramic matrix and its characterization based on low temperature firing of natural loess
13. 10.1016/j.jhazmat.2014.03.02610.1016/j.jhazmat.2014.03.026 ↗
14. Effects of temperature regime and pore‐forming agent dosage on the properties of gangue based multiporous ceramic membrane
15. Preparation of inorganic ceramic membrane from coal gangue
16. Effect of particle morphology on pore size structure and water permeability of ceramic membrane
17. Study on comprehensive combustion performance and combustion dynamics of coal gangue
18. Change law of phase of carb‐thermal reduction fly ash
19. Structure and contribution to photocatalytic activity of the interfaces in nanofibers with mixed anatase and TiO2(B)phased
20. Xing J · 2018
21. Preparation and properties of a new type of low‐cost porous ceramic membrane support
22. Preparation of kaolin‐based low‐cost porous ceramic supports using different amounts of carbonates
23. 10.1021/acsami.1c0815710.1021/acsami.1c08157 ↗
24. Effect of sintering system on properties of fly ash‐loess based ceramic membrane support
25. Effect of bentonite and sintering temperature on properties of loess‐based ceramic membrane support