A Novel and Simple Process for Nanosized Mg‐Mn Ferrite Preparation from Solution Combustion Method and Study of its Characteristics

A novel solution combustion method has been used to prepare Mg‐Mn ferrites of various compositions, Mg _0.9 Mn _0.1 Fe _1‐x O ₄ where x = 0.2, 0.4, 0.6, 0.8, and the properties were investigated in the present work. Nano‐size Mg‐Mn ferrite particles with diameter in the range of 8~ 15 nm were successfully formed via this method. The combustion temperature of the oxidation‐reduction was apparently occurred at 200°C. The result of X‐ray diffraction ( XRD ) analysis indicated that the as‐burnt powder affords a pure single spinel ferrite phase at low temperature. The thermal analysis of nitrate–citrate gels was characterized by DTA‐TG . The TEM and SEM observations give the morphology and microstructure of the products. The dielectric properties of the sintered Mg‐Mn ferrites were investigated by using HP/Agilent 4291B RF impedence/material analyzer. It was found that there was no maximum dielectric loss within the measured frequency range until 1 GHz due to excellent compositional control in this method.