Metal–thermoplastic urethane hybrids in environmental exposure
Source abstract
Abstract
Abstract The long-term properties of injection moulded metal–thermoplastic urethane (TPU) hybrids were studied. The hybrids manufactured with different metal substrates, namely copper, stainless steel and aluminium, were compared, using two surface modifications for copper and stainless steel. N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane was used as coupling agent. It is concluded that the bond mechanism of the silane on different substrate differs, affecting the long-term behaviour of the respective hybrids. The thick layers of silane coupling agent on copper and stainless steel are sensitive to hydrolysis; thus the resistance in humid conditions is quite low. The high temperature exposure increased the bond strength and the fraction of cohesive failure in TPU in copper–TPU, aluminium–TPU and polished steel–TPU hybrids. The last one has native mixed oxide, contrary to controlled oxidised stainless steel, where adhesion decreased after any long-term experiments. This is suggested to derive from hydrogen bonding of the coupling agent to the surface Fe 2 O 3 oxide.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Silicone and Siloxane Chemistry · Polymer composites and self-healing
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Silane solution stability and film morphology of water-based bis-1,2-(triethoxysilyl)ethane for thin-film deposition on aluminium10.1016/j.porgcoat.2008.04.002 ↗
2. Effect of surface hydroxyl concentration on the bonding and morphology of aminopropylsilane thin films on austenitic stainless steel10.1002/sia.3200 ↗
3. Study of the hydrolysis and condensation of γ-aminopropyltriethoxysilane by FT-IR spectroscopy10.1007/s10853-006-1138-9 ↗
4. Influence of coating bath chemistry on the deposition of 3-mercaptopropyl trimethoxysilane films deposited on magnesium alloy10.1016/j.jcis.2009.11.062 ↗
5. Secondary neutral mass spectrometry studies of germanium–silane coupling agent-polymer interphases10.1163/156856190X00531 ↗
6. Effect of deposition conditions for γ-aminopropyltriethoxy silane on adhesion between copper and epoxy resins10.1016/S0169-4332(96)00857-4 ↗
7. Effect of miscibility between a silane and a sizing agent on silanol condensation10.1002/app.11297 ↗
8. Silane pre-treatments on copper and aluminium10.1016/j.electacta.2006.02.042 ↗
9. An XPS investigation of the adsorption of aminosilanes onto metal substrates10.1163/156856192X00016 ↗
10. A surface analytical study of functionalized mild steel for adhesion promotion of organic coatings10.1016/S0300-9440(02)00165-0 ↗
11. Effect of surface pretreatment on water absorption and wet adhesion of organic coatings10.1179/174327806X132196 ↗
12. Adhesion of injection molded PVC to steel substrates10.1080/00218460590954656 ↗
13. Surface engineering of shape memory alloy/polymer-composites: improvement of the adhesion between polymers and pseudoplastic shape memory alloys10.1016/j.msea.2007.05.118 ↗
14. Zhao G, Ehrenstein GW, Investigation of a thin-walled thermoplastic metal hybrid. SPE ANTEC Technical Papers; 1999. p. 1332–1336.
15. Zoellner OJ, Evans JA, Plastic–metal hybrid—a new development in the injection molding technology. SPE ANTEC Technical Papers; 2002. p. 2966–2969.
16. Michaeli W, Maesing R, Reinartz H, In-mould lamination of metal sheets with integrated forming for metal decorated parts. SPE ANTEC Technical Papers; 2010. p. 735–740.
17. Aminofunctional silane layers for improved copper-polymer interface adhesion10.1007/s10853-011-5611-8 ↗
18. Effect of silane treatment parameters on the silane layer formation and bonding to thermoplastic urethane10.1016/j.porgcoat.2011.08.002 ↗
19. Characterization of silane layers on modified stainless steel surfaces and related stainless steel–plastic hybrids10.1016/j.apsusc.2011.05.058 ↗
20. Metal–Plastic adhesion in injection-molded hybrids10.1163/016942409X12489445844435 ↗
21. Oxidation of copper alloys studied by analytical transmission electron microscopy cross-sectional specimens10.1557/JMR.2008.0160 ↗
22. Characterization of stainless steel surfaces—modified in air at 350°C10.1179/174329409X397750 ↗
23. Sheasby · 2001 · vol. 1
24. Sodium enrichment of an Al–Mg alloy surface after alkaline etching10.1016/j.corsci.2006.12.021 ↗
25. Lubrizol General Brochure EMEAI-1, 〈http://www.lubrizol.com/Engineered-Polymers/Brochure/General-Brochure-EMEAI.pdf〉, cited 12.4; 2011.
26. Holden · 2004
27. JESD22-A101C. Steady State Temperature Humidity Bias life Test. USA 2009, JEDEC Solid State Technology Association. p. 12.
28. Effects of hydrolysis-induced molecular weight changes on the phase separation of a polyester polyurethane10.1016/j.polymdegradstab.2006.05.019 ↗
29. Degradation of a poly(ester urethane) elastomer. III. Estane 5703 hydrolysis: experiments and modeling10.1002/pola.10656 ↗
30. Characterization of TPU-elastomers by thermal analysis (DSC)10.1016/j.polymertesting.2003.09.013 ↗
31. IR-change and yellowing of polyurethane as a result of UV irradiation10.1016/j.polymdegradstab.2009.01.013 ↗
32. Silverstein · 1997
33. A comparative study of molybdate/silane composite films on galvanized steel with different treatment processes10.1016/j.surfcoat.2010.07.033 ↗
34. Cerium salt activated nanoparticles as fillers for silane films: evaluation of the corrosion inhibition performance on galvanised steel substrates10.1016/j.electacta.2007.05.022 ↗
35. Determination of isoelectric points of metals and metallic alloys by adhesion of latex particles10.1016/j.jcis.2009.05.005 ↗
36. Compilation of PZC and IEP of sparingly soluble metal oxides and hydroxides from literature10.1016/j.cis.2009.08.003 ↗
37. The structure of films formed by γ-aminopropyltriethoxysilane absorber onto copper10.1016/0021-9797(83)90362-4 ↗
38. The effect of silane incorporation on a metal adhesive interface: a study by electron energy loss spectroscopy10.1016/j.micron.2009.10.001 ↗
39. Adhesion mechanism of polyvinyl chloride to silane primed metal surfaces10.1163/156856187X00058 ↗