Influence of Low-Pressure Plasma on the Surface Properties of CAD-CAM Leucite-Reinforced Feldspar and Resin Matrix Ceramics

The introduction of new ceramic materials for dental restorations is currently a reality; however, little information is available on their surface treatment for the bonding process. Furthermore, surface treatment with plasma on ceramic materials has been recently introduced, although not many studies are available. The aim of this study was to evaluate the surface properties of a leucite-reinforced feldspar ceramic (LIC) and resin matrix ceramic (RMC) after low-pressure plasma treatment. From each material, 48 discs were prepared and subject to surface treatment. The LIC group was treated by hydrofluoric acid (HF) (LIC-HF), plasma with oxygen (LIC-O2), and plasma with argon (LIC-Ar). The RMC group was treated by sandblasting with alumina (RMC-SB), plasma with oxygen (RMC-O2), and plasma with argon (RMC-Ar). The groups whose surfaces were not subjected to treatment were considered as the control group. Surface wettability and roughness was analyzed. The results showed significant differences among the treatments for both ceramics regarding wettability and roughness. Plasma treatments increased the wettability and had a very low effect on the roughness. Plasma treatments achieved similar values for both surface properties in each ceramic group with no differences between both treatments. Plasma treatment seems to be a promising alternative for ceramic surface treatments since it increased the surface energy of the ceramics analyzed and hardly affects the roughness. Further studies are necessary to evaluate the effect of plasma treatment on the bond strength of ceramics.