Analysis of Corrosion-Mechanical Properties of Electroplated and Hot-Dip Zinc Coatings on Mechanically Pre-Treated Steel Substrate

This study evaluates the effects of three mechanical pre-treatment methods on S235JRG2 steel sheets: blasting with a synthetic corundum (F40), blasting with steel shot (S170), and grinding with synthetic corundum (P40). Untreated samples served as a reference. The analysis of mechanical pre-treatments focused on surface integrity, including measurements of surface roughness parameters Ra and Rz (ISO 21920-2) and subsurface microhardness (ISO 6507-1). Zinc coatings were assessed through mechanical testing (cupping test, ISO 1520) and corrosion testing in a neutral salt spray environment (ISO 9227), with results evaluated using digital image analysis. Experimental findings indicate that electroplated zinc deposition rates are influenced by surface roughness, while subsurface microhardness has no significant effect. In contrast, for hot-dip galvanizing, both parameters impact the process. The mechanical properties of electroplated zinc coatings are further affected by steel surface integrity, whereas hot-dip zinc coatings are primarily governed by intermetallic phase formation, making the influence of steel surface integrity statistically negligible. Corrosion testing revealed that blasting with a synthetic corundum is particularly unsuitable, as it leads to numerous inhomogeneities in both coating types, accelerating corrosion degradation.