Improving the shear strength of Sn–Ag–Cu–Ni/Cu–Zn solder joints via modifying the microstructure and phase stability of Cu–Sn intermetallic compounds

Abstract This study focuses on the correlation between high-speed impact tests and the interfacial reaction in Sn-3.0Ag-0.5Cu-0.1Ni/Cu (wt%) and Sn-3.0Ag-0.5Cu-0.1Ni/Cu-15Zn solder joints. Adding Ni into the Sn–Ag–Cu solder alters the interfacial morphology from scallop type to layer type and exhibits high shear strength after reflow in both solder joints. However, the shear strength of Sn-3.0Ag-0.5Cu-0.1Ni/Cu solder joints degrades significantly after thermal aging at 150 °C for 500 h. It is notable that Sn-3.0Ag-0.5Cu-0.1Ni/Cu-15Zn solder joints still present higher shear strength after aging at 150 °C. The weakened shear strength in Sn-3.0Ag-0.5Cu-0.1Ni/Cu solder joints is due to stress accumulation in the interfacial (Cu,Ni) 6 Sn 5 compound induced by the phase transformation from a high-temperature hexagonal structure (η-Cu 6 Sn 5 ) to a low-temperature monoclinic structure (η'-Cu 6 Sn 5 ). However, doping small amounts of Zn into (Cu,Ni) 6 (Sn,Zn) 5 can inhibit the phase transformation during thermal aging and maintain strong shear strength. These experiments demonstrate that Sn-3.0Ag-0.5Cu-0.1Ni/Cu-15Zn solder joints can act as a stable connection in the micro-electronic packaging of most electronic products at their average working temperatures.