Solvothermal Treatment of Micron-Sized Commercial SrAl2O4:Eu2+, Dy3+ Phosphors and One-Step Preparation of Nanophosphors for Fingerprint Imaging

Preparing submicron and nanoscale phosphors with good optical properties for practical applications is a challenging task for current inorganic long afterglow luminescent materials. This study utilized commercialized SrAl2O4:Eu2+, Dy3+ phosphors (SAOED) as raw materials and employed solvents with lower polarity or non-polar solvents for dynamic solvothermal treatment. The commercialized phosphor’s overall average particle size was reduced from 42.3 μm to 23.6 μm while maintaining the fluorescence intensity at 91.39% of the original sample. Additionally, the study demonstrated the applicability of the dynamic solvothermal method to most other commercialized inorganic phosphors. The experiment produced a high-brightness nano-sized phosphor with a yield of 5.64%. The average diameter of the phosphor was 85 nm, with an average thickness of 16 nm. The quantum efficiency of the phosphor was 74.46% of the original sample. The fingerprint imaging results suggest that the nano-sized phosphors have potential for practical applications.