Investigation of the influence of Ni powder size on microstructural evolution and the thermal explosion combustion synthesis of NiTi

M. Whitney, S.F. Corbin, R.B. Gorbet

Intermetallics· Volume 17· Issue 11
Publisher page

Abstract

Abstract A key microstructural feature that controls the sintering behavior of Ni + Ti powders was determined to be the transformation of alpha-Ti to beta-Ti during heating. The use of very fine Ni powders causes this transformation to occur at the eutectoid temperature (i.e., 765 °C). The use of coarse Ni powders causes a gradual beta-Ti transformation from 765 to 882 °C. At 950 °C a large volume fraction of beta-Ti remains in coarse Ni/Ti mixtures whereas in fine Ni/Ti mixtures this phase is almost eliminated. Further heating above 950 °C causes the beta-Ti to melt, initiating a large exothermic reaction in the coarse Ni/Ti mixtures (i.e., 158 J/g) at 980 °C. The use of fine Ni significantly reduces this reaction (i.e., 3 J/g). Consequently, Ni powder size, and its influence over beta-Ti content can be used to control the reactive sintering behavior of Ni + Ti mixtures.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Intermetallics and Advanced Alloy Properties · Shape Memory Alloy Transformations · Advanced materials and composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (23)

Show source-provided references
1. Martynova · Sov Powder Metall Met Ceram · 1983 · 22 · 89510.1007/BF00805543 ↗
2. Igharo · Powder Metall · 1985 · 28 · 13110.1179/pom.1985.28.3.131 ↗
3. Igharo · Powder Metall · 1986 · 29 · 3710.1179/pom.1986.29.1.37 ↗
4. McNeese · Mater Sci Eng · 2000 · A280 · 33410.1016/S0921-5093(99)00550-X ↗
5. Green · Powder Metall · 1997 · 40 · 4310.1179/pom.1997.40.1.43 ↗
6. Zhang · Mater Sci Eng · 1992 · A150 · 26310.1016/0921-5093(92)90120-P ↗
7. Hey · Mater Sci Eng · 1994 · A188 · 29110.1016/0921-5093(94)90384-0 ↗
8. Bram · Mater Sci Eng · 2002 · A337 · 25410.1016/S0921-5093(02)00028-X ↗
9. Schüller · Adv Eng Mater · 2003 · 5 · 91810.1002/adem.200300366 ↗
10. Schüller · J Mater Sci · 2005 · 40 · 423110.1007/s10853-005-2819-5 ↗
11. Krone · Mater Sci Eng · 2004 · A378 · 18510.1016/j.msea.2003.10.345 ↗
12. Li · J Mater Res · 1998 · 13 · 284710.1557/JMR.1998.0389 ↗
13. Li · Mater Sci Eng · 1998 · A255 · 7010.1016/S0921-5093(98)00780-1 ↗
14. Zhu · Mater Lett · 2004 · 58 · 236910.1016/j.matlet.2004.02.017 ↗
15. Lee · Mater Sci Eng · 2000 · A281 · 27510.1016/S0921-5093(99)00715-7 ↗
16. Dey · Acta Mater · 2003 · 51 · 254910.1016/S1359-6454(03)00055-7 ↗
17. Biswas · Acta Mater · 2005 · 53 · 141510.1016/j.actamat.2004.11.036 ↗
18. Yeh · J Alloys Compd · 2004 · 376 · 7910.1016/j.jallcom.2003.12.016 ↗
19. Li · Acta Mater · 2000 · 48 · 389510.1016/S1359-6454(00)00184-1 ↗
20. Yi · Scr Metall · 1998 · 22 · 188910.1016/S0036-9748(88)80232-1 ↗
21. Whitney · Acta Mater · 2008 · 56 · 55910.1016/j.actamat.2007.10.012 ↗
22. Bastin · Met Trans · 1974 · 5 · 181710.1007/BF02644146 ↗
23. Alloy phase diagrams