Parametrization Study of Electrospun Nanofiber Including LiCl Using Response Surface Methodology (RSM) for Water Treatment Application

The influence of the electrospinning parameters on the diameter of the polyethersulfone (PES) nanofibers was demonstrated using response surface methodology. The electrospinning parameters studied were lithium chloride (LiCl) concentration, PES concentration, feed rate, and tip-to-collector distance. The average fiber diameter was correlated to these factors by using a second-order polynomial function at a 95% confidence level. The statistical analysis indicated that LiCl concentration, PES concentration, and feed rate had the significant connection with the fiber diameter, and LiCl concentration was the most important factor in determining the fiber diameter. When LiCl concentration increased, the fiber diameter decreased, because with more LiCl that is added, more applied voltage is needed to overcome the electrostatic attractions. The interactive effect between PES concentration and feed rate, the interactive effect between PES concentration and tip-to-collector distance, and the quadratic coefficients of LiCl concentration were also found to be significant. The adjusted determination coefficient (Radj2) of the model was calculated to be 0.9106. The water flux measurements showed that the decrease in the fiber diameter of the membrane caused the decrease in the initial pure water flux. The retention tests with 0.6 μm polystyrene (PS) suspension indicated that as the fiber diameter decreased, the pore sizes decreased and the particle removal efficiency increased.