Effects of Waste Plastic and Glass Aggregates on the Strength Properties of Ambient-Cured One-Part Metakaolin-Based Geopolymer Concrete
Source abstract
Abstract
The production of Portland cement (PC) is associated with carbon emissions. One-part geopolymer “just add water” is a user- and environmentally-friendly binder that can potentially substitute PC. However, there is limited research on the setting time, fresh, and strength properties of one-part metakaolin (MK)-based geopolymer concrete (OMGPC) incorporating recycled aggregates. Hence, the study explored the fresh, mechanical (compressive, flexural, splitting tensile, and E-modulus) and microstructural properties of ambient cured (7-, 28-, and 90-day) OMGPC containing recycled waste plastics (RESIN8) and recycled fine waste glass aggregate (FWG) at 5% and 10% by volume of the sand. The study result shows that 2% trisodium phosphate by wt. of the binder retard the initial and final setting times of OMGPC. At the same time, the incorporation of RESIN8 and FWG aggregates improved the workability of geopolymer concrete. The lightweight properties of RESIN8 aggregate reduce the hardened density of OMGPC, while the FWG specimens show a similar density to the control. The compressive strength of RESIN8 and FWG OMGPC range from 19.8 to 24.6 MPa and 26.9 to 30 MPa, respectively, compared to the control (26 to 28.9 MPa) at all curing ages. The flexural and splitting tensile strength of the OMGPC range from 2.2 to 4.5 MPa and 1.7 to 2.8 MPa, respectively. OMGPC is a viable alternative to Portland cement, and FWG can substitute sand in structural concrete by up to 10% and RESIN8 aggregate at 5% by volume of the natural sand.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Innovative concrete reinforcement materials · Recycled Aggregate Concrete Performance
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Civil Engineering, Stellenbosch University, Stellenbosch 7602, South Africa
References (87)
Show source-provided references
1. Incorporation of waste materials into Portland cement clinker synthesised from reagent-grade chemicals10.1111/j.1744-7402.2008.02267.x ↗
2. A life-cycle assessment of Portland cement manufacturing: Comparing the traditional process with alternative technologies10.1016/j.jclepro.2008.04.007 ↗
3. Global Warming Impact on the Cement and Aggregates Industries
4. Performance and sustainability overview of sodium carbonate activated slag materials cured at ambient temperature
5. International Energy Agency (2023, September 12). Cement Technology Roadmap Plots Path to Cutting CO2 Emissions 24% by 2050. Available online: https://www.iea.org/news/cement-technology-roadmap-plots-path-to-cutting-co2-emissions-24-by-2050.
6. Towards greener one-part geopolymers through solid sodium activators modification10.1016/j.jclepro.2022.134370 ↗
7. Evaluation of environmental sustainability of one-part geopolymer binder concrete10.1016/j.clema.2022.100138 ↗
8. Global CO2 emissions from cement production10.5194/essd-10-195-2018 ↗
9. Alkali-Activated Fly Ashes-A Cement for the Future Alkali-activated fly ashes A cement for the future10.1016/S0008-8846(98)00243-9 ↗
10. Geopolymer technology: The current state of the art10.1007/s10853-006-0637-z ↗
11. Advances in geopolymer materials: A comprehensive review
12. Printability and particle packing of 3D-printable limestone calcined clay cement composites10.1016/j.conbuildmat.2021.122647 ↗
13. Mix-design and characterisation of alkali activated materials based on metakaolin and ladle slag10.1016/j.clay.2012.09.015 ↗
14. One part alkali activated materials: A state-of-the-art review10.1016/j.jobe.2022.104871 ↗
15. Influence of metakaolin on the properties of mortar and concrete: A review10.1016/j.clay.2008.11.007 ↗
16. Structural and durability properties of concrete made with Corex slag
17. One-part alkali-activated materials: A review10.1016/j.cemconres.2017.10.001 ↗
18. Roles of hybrid activators in improving the early-age properties of one-part geopolymer pastes10.1016/j.conbuildmat.2021.124880 ↗
19. Alkaline activation of metakaolin: Effect of calcium hydroxide in the products of reaction10.1111/j.1151-2916.2002.tb00070.x ↗
20. Kim, B., Lee, S., Chon, C.M., and Cho, S. (2022). Setting behaviour and phase evolution on heat treatment of metakaolin-based geopolymers containing calcium hydroxide. Materials, 15.10.3390/ma15010194 ↗
21. Effect of the adsorbing behaviour of phosphate retarders on hydration of cement paste10.1061/(ASCE)MT.1943-5533.0001929 ↗
22. Sood, D., and Hossain, K.M.A. (2021). Strength, shrinkage and early age characteristics of one-part alkali-activated binders with high-calcium industrial wastes, solid reagents and fibers. J. Comp. Sci., 5.10.3390/jcs5120315 ↗
23. A study on the setting characteristics of sodium silicate-activated slag pastes10.1016/S0008-8846(02)01096-7 ↗
24. Effect of sodium carbonate and sodium phosphate on hydration of cement paste10.1016/j.jobe.2021.103577 ↗
25. An overview of construction and demolition waste management in Canada: A lifecycle analysis approach to sustainability10.1007/s10098-012-0481-6 ↗
26. Circular economy in the construction industry: A systematic literature review10.1016/j.jclepro.2020.121046 ↗
27. Production, use, and fate of all plastics ever made10.1126/sciadv.1700782 ↗
28. Performance of structural concrete with recycled plastic waste as a partial replacement for sand10.1016/j.conbuildmat.2017.11.127 ↗
29. Mechanical and physical characteristics of alkali- activated mortars incorporated with recycled polyvinyl chloride and rubber aggregates10.1016/j.jobe.2022.105043 ↗
30. The effect of sulfuric acid attack on mechanical properties of steel fiber-reinforced concrete containing waste nylon aggregates: Experiments and RSM-based optimisation10.1016/j.jobe.2022.105500 ↗
31. South Africa-State of Waste Report II (2023, July 06). A Report on the State of Waste in South Africa, Available online: www.environment.gov.za.
32. Glass waste versus sand as aggregates: The characteristics of the evolving geopolymer binders10.1016/j.jclepro.2018.05.086 ↗
33. Mechanical and durability properties of natural fiber-reinforced geopolymers containing lead smelter slag and waste glass sand10.1016/j.conbuildmat.2022.129043 ↗
34. Concrete containing waste recycled glass, plastic and rubber as sand replacement10.1016/j.conbuildmat.2020.121242 ↗
35. (2008). Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete (Standard No. ASTM C618-08a).
36. Structural transition to well-ordered phases of NaOH-activated slag-metakaolin cements aged by 6 years10.1016/j.cemconres.2022.106791 ↗
37. Davidovit, U.S. (1982).
38. Davidovit, U.S. (1984).
39. Properties of alkali-activated mortar and concrete using lightweight aggregates10.1617/s11527-009-9499-6 ↗
40. Concrete Mix Design by Packing Density Method10.9790/1684-11213446 ↗
41. Performance evaluation on engineering properties and sustainability analysis of high strength geopolymer concrete10.1016/j.jobe.2022.105147 ↗
42. Cimbala, J.M. (2014). Taguchi Orthogonal Arrays, Pennsylvania State University.
43. Preparation of drying powder inorganic polymer cement based on alkali-activated slag technology10.1016/j.powtec.2017.02.036 ↗
44. Engineering properties of cementless concrete produced from GGBFS and recycled desulfurisation slag10.1016/j.conbuildmat.2014.04.017 ↗
45. Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition10.1016/j.conbuildmat.2014.05.080 ↗
46. (2016). Methods of Testing Cement–Part 3: Determination of Setting Times and Soundness (Standard No. EN 196-3:2016).
47. (2019). Testing Fresh Concrete (Standard No. BS EN 12350-2: 2019).
48. (2019). Testing Hardened Concrete Density (Standard No. BS EN 12390-7: 2019).
49. (2021). Testing Hardened Concrete Shape, Dimensions and other Requirements for Specimens and Moulds (Standard No. BS EN 12390-1: 2021).
50. (2019). Testing Hardened Concrete Making and Curing Specimens for Strength Tests (Standard No. BS EN 12390-2, 2019).
51. (2009). Testing Hardened Concrete Tensile Splitting Strength of Test Specimens (Standard No. BS EN 12390-6: 2009).
52. (2002). Standard Test Method for Static Modulus of Elasticity and Poisson’s Ratio of Concrete in Compression (Standard No. ASTM C469-02).
53. Effect of phosphate on the hydration of alkali-activated red mud-slag cementitious material10.1016/S0008-8846(00)00260-X ↗
54. Influence of recycled glass content and curing conditions on the properties of self-compacting concrete after exposure to elevated temperatures10.1016/j.cemconcomp.2011.08.010 ↗
55. Study of concrete involving use of waste glass as partial replacement of fine aggregates10.9790/3021-03760813 ↗
56. Recycled glass replacement as fine aggregate in self-compacting concrete10.1007/s11709-013-0224-8 ↗
57. Investigation on the roles of glass sand in sustainable engineered geopolymer composites10.1016/j.conbuildmat.2022.129576 ↗
58. Mechanical performance and optimisation of high-volume fly ash concrete containing plastic wastes and graphene nanoplatelets using response surface methodology10.1016/j.conbuildmat.2021.125085 ↗
59. Multiscale investigation of the impact of recycled plastic aggregate as a fine aggregate replacement on one-part alkali-activated mortar performance10.1016/j.jobe.2024.108768 ↗
60. Recycled plastic aggregate in mortars composition: Effect on physical and mechanical properties10.1016/j.matdes.2013.06.025 ↗
61. Natural fibers as reinforcement additives for geopolymers–A review of potential eco-friendly applications to the construction industry
62. Babafemi, A.J., Šavija, B., Paul, S.C., and Anggraini, V. (2018). Engineering properties of concrete with waste recycled plastic: A review. Sustainability, 10.10.3390/su10113875 ↗
63. Ajayi, B.L., and Babafemi, A.J. (2023, January 12–14). Performance of slag-metakaolin-based geopolymer concrete (GPC) with recycled plastic eco-aggregate. Proceedings of the Young Concrete Researchers, Engineers & Technologists, Stellenbosch, South Africa.10.3390/app14051856 ↗
64. Sustainable one-part geopolymer foams with glass fines versus sand as aggregates10.1016/j.conbuildmat.2018.03.120 ↗
65. Performance of sustainable concrete containing different types of recycled plastic10.1016/j.jclepro.2021.129517 ↗
66. Use of recycled plastics in concrete: A critical review10.1016/j.wasman.2016.03.005 ↗
67. Use of different forms of waste plastic in concrete—A review10.1016/j.jclepro.2015.08.042 ↗
68. Use of recycled plastic as fine aggregate in cementitious composites: A review10.1016/j.conbuildmat.2020.119146 ↗
69. Alkali activated materials with recycled unplasticised polyvinyl chloride aggregates for sand replacement10.1016/j.conbuildmat.2023.134188 ↗
70. Physical, mechanical and thermal properties of lightweight composite mortars containing recycled polyvinyl chloride10.1016/j.conbuildmat.2018.11.070 ↗
71. Chen, W., Dong, S., Liu, Y., Liang, Y., and Skoczylas, E. (2022). Effect of waste glass as fine aggregate on properties of mortar. Materials, 15.10.3390/ma15238499 ↗
72. Borek, K., Czapik, P., and Dachowski, R. (2020). Recycled glass as a substitute for quartz sand in silicate products. Materials, 13.10.3390/ma13051030 ↗
73. Geopolymer cement: A review
74. Influence of different curing temperatures and alkali activators on properties of GBFS geopolymer mortars containing fly ash and palm-oil fuel ash10.1016/j.conbuildmat.2016.08.153 ↗
75. Recycling vanadium-bearing shale leaching residue for the production of one-part geopolymers10.1088/2053-1591/ab3755 ↗
76. Strength, microstructure, efflorescence behavior and environmental impacts of waste glass geopolymers cured at ambient temperature10.1016/j.jclepro.2019.119610 ↗
77. Physical and mechanical properties of mortar using waste polyethylene terephthalate bottles10.1016/j.conbuildmat.2013.02.073 ↗
78. Mechanical and durability assessment of recycled waste plastic (Resin8 & PET) eco-aggregate concrete10.3390/su14095725 ↗
79. Cement and concrete as an engineering material: An historic appraisal and case study analysis10.1016/j.engfailanal.2014.02.004 ↗
80. Physical and mechanical properties of mortars containing PET and PC waste aggregates10.1016/j.wasman.2010.03.028 ↗
81. The effect of using polyethylene terephthalate particles on physical and strength-related properties of concrete; A laboratory evaluation10.1016/j.conbuildmat.2016.01.056 ↗
82. Effects of waste PET bottles aggregate on the properties of concrete10.1016/j.cemconres.2004.05.014 ↗
83. (2014). Building Code Requirements for Structural Concrete (ACI 318-14) and Commentary (ACI 318R-14) (Standard No. ACI 318M-14).
84. (2004). Design of Concrete Structures—Part 1-1: General rules and rules for buildings (Standard No. EN 1992-1-1: 2004).
85. Use of selected waste materials in concrete mixes10.1016/j.wasman.2006.07.026 ↗
86. Recycling of plastic waste materials in the composition of ecological mortars10.1016/j.promfg.2018.03.042 ↗
87. Properties of lightweight aggregate concrete prepared with PVC granules derived from scraped PVC pipes10.1016/j.wasman.2008.06.014 ↗