Corrosion resistance tests of strained rods from polymer composite materials
Source abstract
Abstract
A method of estimating the resistance of samples from composite polymer materials to corrosion damage under load is described. The scheme of tests of this method based on the longitudinal bending of the samples is presented. The comparative results of the tests of samples selected from fiberglass plates in air and in an acid medium are presented.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Material Properties and Applications · Structural mechanics and materials · Material Properties and Failure Mechanisms
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (17)
Show source-provided references
1. Karpenko, G.V. and Vasilenko, I.I., Korrozionnoe rastreskivanie stalei (Corrosion Cracking of Steels), Kiev: Tekhnika, 1971.
2. CIGRE Working Group 10 of Study Committee 22. Suspension and tension composite insulators for overhead lines. CIGRE 1980 Session, 1980, pp. 22–80.
3. Chandler, H.D., Jones, R.L., and Reynders, J.P., Stress Corrosion of Composite Long Rod Insulators, Proc. 4th Int. Symp. High Voltage Eng. (1983 ISH), Athens, 1983, pp. 23–09.
4. Kumosa, M., Failure Analysis of Composite High Voltage Insulators, EPRI Rep. 1007464, 2002.
5. Kumosa, M., Interview with M. Kumosa, Research of Brittle Fractures in Composite Insulators, Insul. News Market Rep. 1997, pp. 46–51.
6. Tourreil C., Influence of Acidic Solution on the Fracture Mode of Nonceramic Insulator GRP Rods, Trans. Eng. Oper. Div., Can. Electr. Assoc. 1983, vol. 22, p. 4.
7. Golovatyuk, P.N., Kul’matitskii, V.V., Kuks, S.V., Shumilov, M.Yu., and Shumilov, Yu.N., Examination of Polymer Insulators for VL. 35–750 kV in Order to Enhance Their Safe Exploitation, Energo-Info, 2007, no. 5, www.energo-info.ru/images/pdf/Shumilov.pdf.
8. Kumosa, M., Kumosa, L., and Armentrout, D., Failure Analyses of Nonceramic Insulators Part I: Brittle fracture Characteristics, IEEE Electr. Insul. Mag., 2005, vol. 21, no. 3, pp. 14–27.10.1109/MEI.2005.1437604 ↗
9. Kumosa, M., Kumosa, L., and Armentrout, D., Failure Analyses of Nonceramic Insulators: Part II-The Brittle Fracture Model and Failure Prevention, IEEE Electr. Insul. Mag., 2005, vol. 21, no. 4, pp. 28–41.10.1109/MEI.2005.1489987 ↗
10. Noble B., Harris S.J., and Owen M.J., Stress Corrosion Cracking of GRP Pultruded Rods in Acid Environments, J. Mater. Sci., 1983, vol. 18, pp. 1244–1254.10.1007/BF00551994 ↗
11. Akhtar, A., Nadeau, J.S., Wang, J.Y., Romily, D.P., and Taggart, C., Brittle Fracture of Nonceramic Insulators, Can. Electr. Assoc. Rep., 1986, rep. 186T350.
12. Qiu, Q., Brittle Fracture Mechanisms of Glass Fiber Reinforced Polymer Insulators, Ph. D. Diss., Portland, OR: Oregon Graduate Inst. Sci. Technol., 1995.
13. Kuhl, M., FRP Rods for Brittle Fracture Resistant Composite Insulators, IEEE Trans. Dielecrt. Electr. Insul., 2001, vol. 8, no. 2, pp. 182–190.10.1109/94.919922 ↗
14. Hull, D., Kumosa, M., and Price, J.N., Stress Corrosion of Aligned Glass Fiber-Polyester Composite Material, Mater. Sci. Technol., 1985, vol. 1, pp. 177–182.10.1179/mst.1985.1.3.177 ↗
15. Savin, V.F., Blaznov, A.N., Startsev, O.V., et al., Ispytaniya Uprugikh Sterzhnei Metodom Prodol’nogo Izgiba (Tests of Elastic Rods via Longitudinal Bending Method), Barnaul: Izd. Altaiskogo Gos. Univ., 2009, vol. 222.
16. Volkov, Yu.P., Lugovoi, A.N., Savin, V.F., Khe, A.I., and Blaznov, A.N., Method for Determination of the Mechanical Characteristics of Rods Based on the Results of Tests for Longitudinal Bending, Zavod. Lab., Diagn. Mater., 2004, vol. 70, no. 9, pp. 58–62.
17. Lugovoi, A.N., Investigation of the Mechanical Characteristics of Unidirectional Reinforced Fiberglass via Longitudinal Bending Method, Cand. Sci. (Eng.) Dissertation, Biisk, 2005.