Effect of SiC and WC Reinforcements on Microstructural and Mechanical Characteristics of Copper Alloy-Based Metal Matrix Composites Using Stir Casting Route

This study focuses on a comparative analysis of mechanical behavior and microstructural characteristics of Cu matrix (C87600) based hybrid composites reinforced with SiC-Grp and WC-Grp fabricated by the stir casting process. The graphite particle percentage was kept constant, whereas the content of SiC and WC in the respective composites was varied to analyze the mechanical properties of the fabricated composites. The morphological observation was carried out by field emission scanning electron microscope (FESEM), which revealed uniform dispersion of the reinforced particles in the hybrid composites. Clear phases of SiC and WC along with the Cu alloy were identified by the x-ray diffractometer (XRD). Further, a comparative study was conducted to analyze the mechanical behavior of the Cu-SiC-Gr and Cu-WC-Gr hybrid composites. With the addition of the hard ceramic materials, the tensile behavior and microhardness of both the Cu-based MMCs were improved. The WC-Gr reinforced composites exhibited higher mechanical properties than the SiC-Gr reinforced hybrid composites. Further, the fracture surfaces were also characterized to study the tensile behavior of the fabricated copper-based hybrid composites, which shows that ductile fracture was mainly associated with both hybrid composites.