Retained Austenite Destabilization during Tempering of Low-Temperature Bainite

The thermal stability of nanostructured microstructures consisting of a mixture of bainitic ferrite and carbon-enriched retained austenite has been studied in two steels containing 0.6 C (wt %) by tempering cycles of 1 h at temperatures ranging from 450 to 650 °C. Volume changes due to microstructural transformations during thermal treatments were measured by high-resolution dilatometry. The correlation of these results with the detailed microstructural characterization performed by X-ray diffraction and scanning electron microscope examination showed a sequence of different decomposition events beginning with the precipitation of very fine cementite particles. This precipitation, which starts in the austenite thin films and then continues in retained austenite blocks, decreases the carbon content in this phase so that fresh martensite can form from the low-carbon austenite on cooling to room temperature. In a subsequent tempering stage, the remaining austenite decomposes into ferrite and cementite, and due to carbide precipitation, the bainitic ferrite loses its tetragonality, its dislocation density is reduced, and the bainitic laths coarsen.