Thermodynamic analysis of production parameters and microstructural evolution in shape memory Ni(50-x)Ti(50)Fe(x) (x = 5, 10) alloy synthesized by combustion synthesis

Abstract This study represents an initial effort to produce NiTiFe shape memory alloys via the self-propagating high-temperature synthesis (SHS) process. The synthesis successfully yielded Ni₄₅Ti₅₀Fe₅ and Ni₄₀Ti₅₀Fe₁₀ alloys from elemental Ni, Ti, and Fe powders at three distinct preheating temperatures (240, 330, 420 °C). To support empirical findings, thermodynamic analysis using Factsage Thermodynamic Software was employed to correlate reaction propagation behavior with chemical composition. The calculation showed that the addition of 5 at.% Fe to the B2 phase did not hinder reaction self-propagation. This conclusion was supported with the ∆H_f/Cp ratio and transient liquid ratio, computed using the sub-lattice model, which closely resembled that of NiTi. Whereas 10 at.% Fe that synthesized at preheating temperature of 240 °C exhibits struggle, thus an increase in triggering time causes an effect on crystallite size and a decrease in porosity. Empirical results confirmed these findings, albeit influenced by ignition times. An increase in the liquid ratio due to the adiabatic temperature rise can also result in a reduction of NiTi content when the Fe ratio is increased, consequently diminishing the driving force for the reaction. In the sample containing – 5% Fe, the main phase is B2, and the R martensitic phase is also present. Ms is determined to be – 38.7 °C. SEM analyses revealed the presence of Ti₂Ni and Ti₂Ni₃ phases in the upper and lower regions, while the distribution in the middle section is more homogeneous. No martensitic transformation was observed in 10% Fe. Additionally, nanocrystalline regions were detected within the samples by transmission electron microscopy, contributing to a nuanced understanding of their structural properties. Graphic abstract