Low temperature thermal annealing-induced α-FeSi2 derived phase in an amorphous Si matrix

Thermal annealing-induced recrystallisation in Fe ion-implanted Si was investigated by transmission electron microscopy. Single crystals of Si(111) were implanted with 120 keV Fe ions to a fluence of 1.0×1017 cm-2 at cryogenic temperature. A buried amorphous Fe-Si layer in an amorphous Si matrix was formed in the as-implanted sample. Nanobeam electron diffraction revealed that metastable α-FeSi2 precipitates embedded in the amorphous Si matrix were formed after annealing at 350 °C for 8 h. The formation of this α-FeSi2-derived phase was unusual, because it has been observed only in epitaxially grown thin films. Based on the Fe1-xSi (0<x<0.5) phase with the CsCl structure, which is another metastable phase in the Fe-Si binary system, we discuss the formation process of the metastable α-FeSi2 in the amorphous matrix.