Structural, morphological and electroluminescence studies of Zno:Co nanophosphor

The nanoparticles of zinc oxide (ZnO) doped with various concentrations of cobalt (Co) were synthesized by chemical precipitation method in the presence of capping agent polyvinylpyrrolidone (PVP). The effect of doping concentration on structural and morphological properties has been studied by X-ray diffraction (XRD) and scanning electron microscope (SEM). Cell volume, bond length, texture coefficient, lattice constants and dislocation density are also studied. Here, we also compared the interplaner spacing and relative peak intensities from their standard values with different angles. Crystallite sizes have been calculated by Debye–Scherrer’s formula whose values are decreasing with increase in cobalt content up to 3 %. It has been seen that the growth orientation of the prepared ZnO nanorods was (101). The XRD analysis also ensures that ZnO has a hexagonal (wurtzite) crystal structure. The electroluminescence (EL) cells were prepared by placing pure and cobalt-doped ZnO nanoparticles between ITO-coated conducting glass plate and aluminium foil. Alternating voltage of various frequencies was applied, and EL brightness at different voltages was measured and corresponding current was also recorded. The voltage dependence of electroluminescence (EL) brightness of the ZnO:Co shows exponential increase. The linear voltage–current characteristic indicates ohmic nature. The EL brightness at a particular voltage is found to increase by increasing Co doping, but for higher percentage of Co the EL brightness is reduced. It is also seen that Co does not influence the threshold voltage. The brightness is also affected by increasing the frequency of AC signal.