Microstructural Evolution of SAC-Based Solder Joints Exposed to Thermal Cycling: Effect of Paste Alloy, Paste Volume, and Surface Finish

Abdallah Alakayleh, Sa'd Hamasha, Saddam Daradkeh, Sufyan Tahat, John Evans, Ali Alahmer

Publisher page

Abstract

SAC (Sn-Ag-Cu) solder joints are frequently exposed to thermal cycling, leading to microstructural evolutions that accelerate thermal fatigue. During thermal cycling, the coarsening of Ag3Sn precipitates and recrystallization occur, impacting the reliability and microstructure of solder joints. To enhance the high-temperature performance of lead-free alloys, dopants such as Bismuth (Bi), Antimony (Sb), and Indium (In) have been proposed by leveraging the solid solution and dispersion-strengthening mechanisms. However, limited studies have investigated the impact of varying paste volumes of third-generation alloys on thermal cycling reliability and the resulting microstructural evolution. This study examines the thermal cycling reliability of three CABGA208 components mounted on a printed circuit board (PCB) using three different paste alloys, namely SAC305, SAC-Bi, and SAC-Bi-Sb, while maintaining fixed 18-mil SAC305 solder balls. Three paste volumes were printed to achieve paste-to-sphere-volume ratios of 0.1, 0.3, and 0.5. The PCB was plated with Electroless Nickel Immersion Gold (ENIG) and Organic Solderability Preservative (OSP) surface finishes. Thermal cycling tests were conducted between -40 °C and +125 °C, with a dwell time of 15 minutes and a ramp rate of 10°C/min. Weibull analysis revealed that doped alloys outperformed SAC305, with SAC-Bi exhibiting the highest reliability. A higher paste-to-sphere volume ratio generally improved reliability, except for SAC-Bi-Sb, where larger voids formed at higher paste volumes. The ENIG surface finish provided better performance than OSP, likely due to the beneficial effect of the Ni layer. Microstructural analysis showed that higher paste volume in SAC-Bi and SAC-Bi-Sb significantly reduced Ag3Sn coarsening. Additionally, increased paste volume resulted in a thinner intermetallic compound (IMC) layer and less evolution.
Source: openalex_inverted_index · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Electronic Packaging and Soldering Technologies · 3D IC and TSV technologies · Recycling and Waste Management Techniques

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Industrial and Systems Engineering, Auburn University, Auburn, AL, USA

Department of Industrial Engineering, School of Applied Technical Sciences, German Jordanian University, Amman, Jordan

Department of Mechanical Engineering, Tuskegee University, Tuskegee, AL, USA

References (58)

Show source-provided references
1. 10.1016/j.microrel.2005.06.00610.1016/j.microrel.2005.06.006 ↗
2. 10.37665/smTYLHZ4968210.37665/smTYLHZ49682 ↗
3. 10.1109/ITherm55375.2024.1070961510.1109/ITherm55375.2024.10709615 ↗
4. 10.1109/ITherm55375.2024.1070960010.1109/ITherm55375.2024.10709600 ↗
5. 10.1016/j.jmps.2024.10562310.1016/j.jmps.2024.105623 ↗
6. 10.1038/s41467-024-48532-610.1038/s41467-024-48532-6 ↗
7. 10.1109/TCPMT.2010.210107210.1109/TCPMT.2010.2101072 ↗
8. 10.3390/ma1519675910.3390/ma15196759 ↗
9. 10.1007/s11664-025-11747-410.1007/s11664-025-11747-4 ↗
10. 10.3390/ma1710236510.3390/ma17102365 ↗
11. 10.3390/polym1618259710.3390/polym16182597 ↗
12. 10.1007/s11837-015-1595-110.1007/s11837-015-1595-1 ↗
13. 10.1109/ECTC.2014.689735610.1109/ECTC.2014.6897356 ↗
14. 10.37665/smMPFQC4322310.37665/smMPFQC43223 ↗
15. 10.1016/j.microrel.2024.11545710.1016/j.microrel.2024.115457 ↗
16. 10.1016/j.microrel.2018.02.00910.1016/j.microrel.2018.02.009 ↗
17. 10.1109/ITherm55375.2024.1070956710.1109/ITherm55375.2024.10709567 ↗
18. 10.1007/s11664-003-0125-z10.1007/s11664-003-0125-z ↗
19. 10.1109/TEPM.2006.88250010.1109/TEPM.2006.882500 ↗
20. 10.1108/1356536121121920210.1108/13565361211219202 ↗
21. 10.1007/s10854-020-04982-410.1007/s10854-020-04982-4 ↗
22. 10.1016/S1003-6326(21)65585-110.1016/S1003-6326(21)65585-1 ↗
23. 10.1109/ECTC51529.2024.0008510.1109/ECTC51529.2024.00085 ↗
24. 10.1109/ITherm45881.2020.919046610.1109/ITherm45881.2020.9190466 ↗
25. 10.1109/ITherm55375.2024.1070960610.1109/ITherm55375.2024.10709606 ↗
26. 10.1109/ITherm55375.2024.1070943810.1109/ITherm55375.2024.10709438 ↗
27. 10.1007/s11664-023-10780-510.1007/s11664-023-10780-5 ↗
28. 10.1115/1.402384610.1115/1.4023846 ↗
29. 10.1109/ECTC.2018.0030510.1109/ECTC.2018.00305 ↗
30. 10.1109/ITherm55368.2023.1017756110.1109/ITherm55368.2023.10177561 ↗
31. 10.1109/TCPMT.2023.324036710.1109/TCPMT.2023.3240367 ↗
32. 10.37665/smKHVQS9829210.37665/smKHVQS98292 ↗
33. 10.3390/ma1304083110.3390/ma13040831 ↗
34. 10.1109/ITherm55375.2024.1070897310.1109/ITherm55375.2024.10708973 ↗
35. 10.1109/TCAPT.2005.85359310.1109/TCAPT.2005.853593 ↗
36. 10.1109/95.65093810.1109/95.650938 ↗
37. Reliability and IMC layer evolution of homogenous lead-free solder joints during thermal cycling
38. 10.1007/s11664-010-1401-310.1007/s11664-010-1401-3 ↗
39. 10.3390/app902022710.3390/app9020227 ↗
40. 10.1016/j.jallcom.2009.11.08810.1016/j.jallcom.2009.11.088 ↗
41. 10.1109/ECTC.2001.92776910.1109/ECTC.2001.927769 ↗
42. 10.1007/s10854-022-08567-110.1007/s10854-022-08567-1 ↗
43. 10.1007/s11664-011-1760-410.1007/s11664-011-1760-4 ↗
44. 10.1007/s11664-020-08641-610.1007/s11664-020-08641-6 ↗
45. 10.1016/j.jallcom.2008.02.10210.1016/j.jallcom.2008.02.102 ↗
46. 10.1016/j.msea.2006.01.06510.1016/j.msea.2006.01.065 ↗
47. 10.37665/smLSIQW5100910.37665/smLSIQW51009 ↗
48. 10.1109/ITherm55368.2023.1017753410.1109/ITherm55368.2023.10177534 ↗
49. 10.1016/s0026-2714(03)00124-010.1016/s0026-2714(03)00124-0 ↗
50. 10.1147/rd.494.060710.1147/rd.494.0607 ↗
51. 10.2320/matertrans.45.69510.2320/matertrans.45.695 ↗
52. 10.37665/smLQXLL6406610.37665/smLQXLL64066 ↗
53. 10.1016/j.jallcom.2008.03.09710.1016/j.jallcom.2008.03.097 ↗
54. 10.3390/ma1319444310.3390/ma13194443 ↗
55. 10.1115/1.405531810.1115/1.4055318 ↗
56. 10.37665/smUKXJF3824810.37665/smUKXJF38248 ↗
57. 10.1016/s0925-8388(01)01747-910.1016/s0925-8388(01)01747-9 ↗
58. 10.1007/s11664-009-0966-110.1007/s11664-009-0966-1 ↗