Tailored ablation processing of advanced biomedical hydroxyapatite by femtosecond laser pulses

The micromachining of hydroxyapatite (HAp) is highly important for orthopedics and dentistry, since human bone and teeth consist mainly of HAp. We demonstrate ultrashort Ti:sapphire laser ablation of HAp, using pulse-widths of 50 fs, 500 fs, and 2 ps at a wavelength of 820 nm and at 1 kpps. The crucial medical issue is to preserve the chemical properties of the machined (ablated) surface. If the chemical properties of HAp change, the human bone or tooth cannot re-grow after laser processing. Using X-ray photoelectron spectroscopy, we observe chemical properties of HAp ablated in air. The HAp is ablated at laser fluences of 3.2 J/cm2 (6.4×1013 W/cm2 at 50 fs), 3.3 J/cm2 (6.6×1012 W/cm2 at 500 fs), and 9.6 J/cm2 (4.8×1012 W/cm2 at 2 ps), respectively. As a result it is found that the ablated surface is unchanged after laser ablation over the pulse-width range used in this experiment.