Effect of energy density on cracking of ZGH451 superalloy by laser powder bed fusion
Source abstract
Abstract
Abstract ZGH451 is a novel age-strengthened nickel-based superalloy renowned for its exceptional toughness and corrosion resistance. However, it is susceptible to cracking during laser powder bed fusion (LPBF) processing. This study systematically investigates LPBF-fabricated ZGH451 to establish the inherent relationship between volumetric energy density (VED) and crack evolution, with particular emphasis on crack initiation and propagation mechanisms. Our findings confirm that optimized VED effectively suppresses cracking. Experimental results reveal that VEDs above 70 J/mm 3 induce edge-localized cracks dominated by stress cracks and ductility-dip cracks (DDC), whereas VEDs below 45 J/mm 3 produce surface-distributed fine cracks characterized as solidification/liquation cracks. Microstructural analysis demonstrates two distinct mechanisms: excessive VED facilitates high-angle grain boundary cracking, while Al/Ti-based low-melting eutectic phases and Cr/W/Ta/C-derived carbides synergistically enhance grain boundary embrittlement, thereby creating prerequisites for crack nucleation and growth. Moreover, by adjusting the VED from 100 J/mm 3 to 49.45 J/mm 3 , the grain size is refined from 62.43 µm to 35.83 µm, and the grain boundary density is increased by 42.6 %. These improvements significantly reduce stress concentrations and crack formation. This work establishes fundamental correlations between VED and crack behavior in LPBF-processed ZGH451, providing critical guidance for defect mitigation through controlled energy parameters.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · High Entropy Alloys Studies · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Ningbo Institute of Materials Technology and Engineering , Chinese Academy of Sciences , Ningbo , 315201 , China
School of Materials Science and Chemical Engineering , Ningbo University , Ningbo , 315211 , China
Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research , Chinese Academy of Sciences , Shenyang , 110016 , China
Key Laboratory of Advanced Marine Materials, Ningbo Institute of Materials Technology and Engineering , Chinese Academy of Sciences , Ningbo , 315201 , China
China SciLong Lightweight Technology Co., Ltd , Ningbo , 315336 , China
School of Materials Science and Engineering , Harbin Institute of Technology , Harbin , 150001 , China
References (33)
Show source-provided references
1. Xiao, H, Liu, X, Xiao, W, Yang, J, Li, C, Li, Y, et al.. Influence of molten-pool cooling rate on solidification structure and mechanical property of laser additive manufactured Inconel 718. J Mater Res Technol 2022;19:4404–16. https://doi.org/10.1016/j.jmrt.2022.06.162.10.1016/j.jmrt.2022.06.162 ↗
2. Sanchez, S, Smith, P, Xu, Z, Gaspard, G, Hyde, CJ, Wits, WW, et al.. Powder bed fusion of nickel-based superalloys: a review. Int J Mach Tool Manufact 2021;165:103729. https://doi.org/10.1016/j.ijmachtools.2021.103729.10.1016/j.ijmachtools.2021.103729 ↗
3. Wang, P, Zhu, Y, Lu, N, Liang, J, Zhou, Y, Sun, X, et al.. Controllable period of crystallographic lamellar microstructure in ZGH451 superalloy prepared by laser powder bed fusion. J Mater Sci Technol 2025;211:239–43. https://doi.org/10.1016/j.jmst.2024.06.008.10.1016/j.jmst.2024.06.008 ↗
4. Owolabi, AL, Megat-Yusoff, PSM, Said, MAM. Investigation on microstructure and mechanical properties of a varying surface region of a service-exposed IN738 turbine blade. Int J Microstruct Mater Prop 2017;12:38–54. https://doi.org/10.1504/ijmmp.2017.087661.10.1504/IJMMP.2017.087661 ↗
5. Wang, Y, Gao, L, Yang, L, Liu, T, Miao, J, Zang, Y, et al.. The effects of laser power on the performance and microstructure of Inconel 718 formed by selective laser melting. Appl Sci 2024;14:9686. https://doi.org/10.3390/app14219686.10.3390/app14219686 ↗
6. Wang, W, Wang, S, Zhang, X, Chen, F, Xu, Y, Tian, Y. Process parameter optimization for selective laser melting of Inconel 718 superalloy and the effects of subsequent heat treatment on the microstructural evolution and mechanical properties. J Manuf Process 2021;64:530–43. https://doi.org/10.1016/j.jmapro.2021.02.004.10.1016/j.jmapro.2021.02.004 ↗
7. Papadakis, L, Loizou, A, Risse, J, Bremen, S, Schrage, J. A computational reduction model for appraising structural effects in selective laser melting manufacturing: a methodical model reduction proposed for time-efficient finite element analysis of larger components in selective laser melting. Virtual Phys Prototyp 2014;9:17–25. https://doi.org/10.1080/17452759.2013.868005.10.1080/17452759.2013.868005 ↗
8. Kitano, H, Kusano, M, Tsujii, M, Yumoto, A, Watanabe, M. Process parameter optimization framework for the selective laser melting of hastelloy X alloy considering defects and solidification crack occurrence. Crystals 2021;11:578. https://doi.org/10.3390/cryst11060578.10.3390/cryst11060578 ↗
9. Yan, H, Zhu, G, Shi, H, Zhang, P, Li, H, Lu, Q, et al.. Microstructure and mechanical properties of K438 alloy processed by selective laser melting and subsequent heat treatment. Mater Char 2022;191:112116. https://doi.org/10.1016/j.matchar.2022.112116.10.1016/j.matchar.2022.112116 ↗
10. Carter, LN, Wang, X, Read, N, Khan, R, Aristizabal, M, Essa, K, et al.. Process optimisation of selective laser melting using energy density model for nickel-based superalloys. Mater Sci Technol 2016;32:657–61. https://doi.org/10.1179/1743284715y.0000000108.10.1179/1743284715Y.0000000108 ↗
11. Carter, LN, Attallah, MM, Reed, RC. Laser powder bed fabrication of nickel-base superalloys: influence of parameters; quantification and mitigation of cracking. Superalloys 2012;2012:2826–34.10.7449/2012/Superalloys_2012_577_586 ↗
12. Cloots, M, Uggowitzer, PJ, Wegener, K. Investigations on the microstructure and crack formation of IN738LC samples processed by selective laser melting using gaussian and doughnut profiles. Mater Des 2016;89:770–84. https://doi.org/10.1016/j.matdes.2015.10.027.10.1016/j.matdes.2015.10.027 ↗
13. Zhang, S, Lei, Y, Chen, Z, Wei, P, Liu, W, Yao, S, et al.. Effect of laser energy density on the microstructure and texture evolution of Hastelloy-X alloy fabricated by laser powder bed fusion. Materials 2021;14:4305. https://doi.org/10.3390/ma14154305.10.3390/ma14154305 ↗
14. Grange, D, Bartout, JD, Macquaire, B, Colin, C. Processing a non-weldable nickel-base superalloy by selective laser melting: role of the shape and size of the melt pools on solidification cracking. Materialia 2020;12:100686. https://doi.org/10.1016/j.mtla.2020.100686.10.1016/j.mtla.2020.100686 ↗
15. Wang, X, Read, N, Carter, LN, Ward, RM, Attallah, MM. Defect formation and its mitigation in selective laser melting of high γ’ Ni-base superalloys. Superalloys 2016:351–8.10.1002/9781119075646.ch38 ↗
16. Starikov, K, Polozov, I, Borisov, E, Kim, A, Voevodenko, D, Gracheva, A, et al.. Selective laser melting of non-weldable nickel superalloy: microstructure, cracks and texture. Metals 2023;13:1886. https://doi.org/10.3390/met13111886.10.3390/met13111886 ↗
17. Wang, F, Echlin, PM, Taylor, AA, Shin, J, Bammes, B, Levin, BD, et al.. Electron backscattered diffraction using a new monolithic direct detector: high resolution and fast acquisition. Ultramicroscopy 2021;220:113160. https://doi.org/10.1016/j.ultramic.2020.113160.10.1016/j.ultramic.2020.113160 ↗
18. Li, X, Cheng, H, Shi, C, Liu, R, Wang, R, Yang, C. Achieving equiaxed transition and excellent mechanical properties in a novel near-β titanium alloy by regulating the volume energy density of selective laser melting. Materials 2024;17:2631. https://doi.org/10.3390/ma17112631.10.3390/ma17112631 ↗
19. Blumm, J, Lindemann, A, Niedrig, B. Measurement of the thermophysical properties of an NPL thermal conductivity standard inconel 600. High Temp – High Press 2003;35:6–626. https://doi.org/10.1068/htjr145.10.1068/htjr145 ↗
20. Li, Z, Confalonieri, C, Gariboldi, E. Numerical and experimental evaluation of thermal conductivity: an application to Al-Sn alloys. Metals 2021;11:650. https://doi.org/10.3390/met11040650.10.3390/met11040650 ↗
21. Mostafaei, A, Ghiaasiaan, R, Ho, IT, Strayer, S, Chang, KC, Shamsaei, N, et al.. Additive manufacturing of nickel-based superalloys: a state-of-the-art review on process-structure-defect-property relationship. Prog Mater Sci 2023;136:101108. https://doi.org/10.1016/j.pmatsci.2023.101108.10.1016/j.pmatsci.2023.101108 ↗
22. Xia, M, Gu, D, Yu, G, Dai, D, Chen, H, Shi, Q. Selective laser melting 3D printing of Ni-based superalloy: understanding thermodynamic mechanisms. Sci Bull 2016;61:1013–22. https://doi.org/10.1007/s11434-016-1098-7.10.1007/s11434-016-1098-7 ↗
23. Vilanova, M, Garciandia, F, Sainz, S, Jorge-Badiola, D, Guraya, T, San Sebastián, M. The limit of hot isostatic pressing for healing cracks present in an additively manufactured nickel superalloy. J Mater Process Technol 2022;300:117398. https://doi.org/10.1016/j.jmatprotec.2021.117398.10.1016/j.jmatprotec.2021.117398 ↗
24. Khairallah, SA, Anderson, A. Mesoscopic simulation model of selective laser melting of stainless steel powder. J Mater Process Technol 2014;214:2627–36. https://doi.org/10.1016/j.jmatprotec.2014.06.001.10.1016/j.jmatprotec.2014.06.001 ↗
25. Boellinghaus, T, Herold, H, Cross, CE, Lippold, JC. Hot cracking phenomena in welds II. Berlin: Springer Science & Business Media; 2008.10.1007/978-3-540-78628-3 ↗
26. Zhao, Y, Ma, Z, Yu, L, Liu, Y. New alloy design approach to inhibiting hot cracking in laser additive manufactured nickel-based superalloys. Acta Mater 2023;247:118736. https://doi.org/10.1016/j.actamat.2023.118736.10.1016/j.actamat.2023.118736 ↗
27. Wei, Q, Xie, Y, Teng, Q, Shen, M, Sun, S, Cai, C. Crack types, mechanisms, and suppression methods during high-energy beam additive manufacturing of nickel-based superalloys: a review. Chin J Mech Eng: Addit Manuf Front 2022;1:100055. https://doi.org/10.1016/j.cjmeam.2022.100055.10.1016/j.cjmeam.2022.100055 ↗
28. Wang, P, Song, W, Yang, S, Yang, J, Liang, J, Li, J, et al.. Effect of Zr on microstructure and hot cracking susceptibility of ZGH451 superalloy fabricated by direct energy deposition. J Alloys Compd 2023;965:171371. https://doi.org/10.1016/j.jallcom.2023.171371.10.1016/j.jallcom.2023.171371 ↗
29. Tang, YB, Panwisawas, C, Ghoussoub, JN, Gong, Y, Clark, JWG, Nemeth, AN, et al.. Alloys-by-design: application to new superalloys for additive manufacturing. Acta Mater 2021;202:417–36. https://doi.org/10.1016/j.actamat.2020.09.023.10.1016/j.actamat.2020.09.023 ↗
30. Qiu, C, Chen, H, Liu, Q, Yue, S, Wang, H. On the solidification behaviour and cracking origin of a nickel-based superalloy during selective laser melting. Mater Char 2019;148:330–44. https://doi.org/10.1016/j.matchar.2018.12.032.10.1016/j.matchar.2018.12.032 ↗
31. Chen, Y, Lu, F, Zhang, K, Nie, P, Elmi Hosseini, SR, Feng, K, et al.. Dendritic microstructure and hot cracking of laser additive manufactured inconel 718 under improved base cooling. J Alloys Compd 2016;670:312–21. https://doi.org/10.1016/j.jallcom.2016.01.250.10.1016/j.jallcom.2016.01.250 ↗
32. Guo, B, Zhang, Y, Yang, Z, Cui, D, He, F, Li, J, et al.. Cracking mechanism of hastelloy X superalloy during directed energy deposition additive manufacturing. Addit Manuf 2022;55:102792. https://doi.org/10.1016/j.addma.2022.102792.10.1016/j.addma.2022.102792 ↗
33. Liu, Y, Yang, Y, Wang, D. A study on the residual stress during selective laser melting (SLM) of metallic powder. Int J Adv Manuf Technol 2016;87:647–56. https://doi.org/10.1007/s00170-016-8466-y.10.1007/s00170-016-8466-y ↗