The investigation on the middle period dephosphorization in 70t converter
Source abstract
Abstract
Abstract An experimental test is carried out on the 70t converter in Masteel to study the law of middle period dephosphorization in the smelting period. It is found that the dephosphorization rate is slow in the early and middle period of smelting and the content of the final P in steel cannot reach the standard due to the low oxidation of slag. The content of the final P in steel can be controlled within 0.02% by adding ore to the molten bath in the middle period and raising the lance position. The experimental test shows that the dephosphorization can still be achieved by a large margin if appropriate slag conditions are maintained in the middle period when the C and O reactions are strong. By theoretical calculation, it is concluded that the slag content should be controlled between 15 and 23%, and the basicity of slag should be between 2.5 and 2.8 in the middle period of production. Through the observation of experimental slag by SEM, it is found that the limiting factor of dephosphorization in the middle period under the test conditions is that the dephosphorization speed is too slow due to the low oxidation, rather than the solidification of phosphorus.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Microstructure and Mechanical Properties of Steels · Iron and Steelmaking Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Metallurgical Engineering, Anhui University of Technology , Ma’anshan , 243000 , China
Ma’anshan Iron & Steel Co., Ltd. , Ma’anshan , 243000 , China
References (20)
Show source-provided references
1. Zhou, J. D., X. G. Bi, and F. Yang. Experimental study on phosphorus distribution between CaO–FeO*–SiO2–P2O5(15%)–CaF2 slag and carbon-saturated hot metal at 1573.15 K. Ironmaking Steelmaking, Vol. 41, 2014, pp. 298–303.10.1179/1743281213Y.0000000128 ↗
2. Yang, X. M., J. Y. Li, M. Zhang, G. M. Chal, D. P. Duan, and J. Zhang. Coupling relationship between dephosphorisation and desulphurisation abilities or potentials for CaO–FeO–Fe2O3–Al2O3–P2O5 slags over a large variation range of slag oxidisation ability during secondary refining process of molten steel. Ironmaking Steelmaking, Vol. 45, 2018, pp. 25–43.10.1080/03019233.2016.1235674 ↗
3. Cao, L. L., Q. Liu, Z. Wang, and N. Li. Interaction behaviour between top blown jet and molten steel during BOF steelmaking process. Ironmaking Steelmaking, Vol. 45, 2018, pp. 239–248.10.1080/03019233.2016.1255373 ↗
4. Liu, Y. W., X. Cui, Y. Q. Zhou, and Y. Y. Gong. Study on phosphorus control process in low-phosphorus steel semi-steel steelmaking process, Hebei Metallurgy, 2017, pp. 20–21.
5. Han, Y., M. B. Zhang, Q. He, P. Wang, and D. Zhang. Process practice of slag composition control for low phosphorus steel by vanadium extraction semi-steel smelting with 100t converter and “slag-remaining + double-slag” techniques, Special Steel, Vol. 38, 2017, pp. 27–28.
6. Tian, Z. H., B. H. Li, X. M. Zhang, and Z. H. Jiang. Double slag operation dephosphorization in BOF for producing low phosphorus steel. J Iron Steel Res Int, Vol. 16, 2009, pp. 6–14.10.1016/S1006-706X(09)60036-4 ↗
7. Li, X., Y. P. Bao, M. Wang, and L. Lin. Study on slag formation route in dephosphorization stage of converter slag-remaining + double-slag process. Steelmaking, Vol. 32, 2016, pp. 6–11.
8. Wang, B. G., Y. B. Tang, J. Li, Y. J. Xia, and G. L. Wang. Production practice of double-slag dephosphorization process with converter of Ma’anshan Iron and Steel Co., Ltd. Metallurgical Power, Vol. 10, 2014, pp. 84–86.
9. Wu, H., J. Li, C. G. Zhou, et al. Process practice of single slag tapping double-slag dephosphorization of 120t top-bottom combined blowing converter. Special Steel, Vol. 34, 2014, pp. 30–32.
10. Li, J. X., X. D. Hao, S. T. Qiu, and P. Zhao. Multi-functional dephosphorization process with double-blowing converter. Journal of Beijing University of Science and Technology, Vol. 34, 2009, pp. 84–85.
11. Liao, P., Z. W. Hou, Z. Qin, X. Z. Zhang, and S. T. Qiu. Dephosphorization test of combined blowing converter with double slag technique. Iron Steel, Vol. 48, 2013, pp. 30–36.
12. Liu, K., L. Liu, P. He, Y. Cui, G. S. Zhu, and H. B. Li. Thermodynamics of dephosphorization reaction in converter production of low phosphorus steel. Iron Steel, Vol. 47, 2012, pp. 34–39.
13. Yu, L. Z. Analysis of factors affecting dephosphorization of converter and its process development. China High-Tech Enterprise, Vol. 1, 2014, 71–74.
14. Yang, L. B. Analysis of dephosphorization in converter smelting process. The 19th National Conference on Steelmaking, Vol. 55, 2016.
15. Zhuo, W. W. Study on Dephosphorization of Combined Blowing Converter and its Influencing Factors. PhD thesis, Wuhan University of Science and Technology, Vol. 34, 2009.
16. Wan, X. F., D. Cao, D. G. Li, X. W. Liao, L. J. Wang, and G. H. Chang. Research and practice of deep dephosphorization process by double-slag technique in anshan iron and steel co. Iron Steel, Vol. 47, 2012, pp. 32–36.
17. Zhou, C. G., J. Li, H. Wu, K. S. Cai, G. P. Wu, and Y. L. Cao. Study on the temperature of single slag tapping dephosphorization by converter double-slag technique. Iron Steel, Vol. 49, 2014, pp. 24–28.
18. Wang, J., J. Q. Zeng, and L. B. Yang. Optimization of the temperature of the single tapping in the double-slag dephosphorization smelting process of a combined blowing converter. Steelmaking, Vol. 31, 2015, pp. 34–37.
19. Healy, G. W. New look at phosphorus distribution. The Iron and Steel Institute, Vol. 208, 1970, pp. 664–668.
20. Suito, H., R. Inoue, and M. Takada. Phosphorus dissribution between liquid iron and MgO saturated slags of the system CaO-MgO-FetO-SiO2. Transactions ISIJ, Vol. 67, 1981, pp. 2645–2654.10.2355/tetsutohagane1955.67.16_2645 ↗