Thermo-Elastic Constants of Symmetric Laminates with Cracks and Local Delaminations in Off-Axis Ply
Source abstract
Abstract
Abstract Analytical expressions for in-plane thermo-elastic constants of symmetric laminates containing intralaminar cracks in off-axis plies and local delaminations at ply interfaces are presented. Exact relationships called GLOB-LOCdel model that links laminate stiffness to characteristics of cracks with delaminations were presented in Varna et al., 2025. The effect of a crack is described by normalized average opening (COD) and sliding displacements (CSD) of its faces, which are larger in the presence of local delaminations. The CSD dependence on delamination length was analyzed in the paper cited above, where simple fitting functions were presented. In the present paper, FEM is used to analyze the COD dependence on delamination length and crack density for different material systems in balanced laminates with cracked 90-ply, revealing the most significant parameters. Then, the obtained approximate COD and CSD expressions are used in the GLOB-LOCdel model to predict thermo-elastic constants of multidirectional laminates. The results are in good agreement with direct FEM calculations in the literature. When calculating COD and CSD, homogenization over adjacent plies to estimate the constraint on the damaged ply is suggested and validated with FEM data from literature.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Composite Structure Analysis and Optimization · Numerical methods in engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Varna, J.: Modeling mechanical performance of damaged laminates. J. Compos. Mater. 47(20–21), 2443–2474 (2013)10.1177/0021998312469241 ↗
2. Parvizi, A., Bailey, J.E.: On multiple transverse cracking in glass fibre epoxy cross-ply laminates. Journal of Materials Science 13, 2131–2136 (1978)10.1007/BF00541666 ↗
3. Jamison, R.D., Schulte, K., Reifsnider, K.L., Stinchcomb, W.W.: Characterization and analysis of damage mechanisms in tension-tension fatigue of Graphite/Epoxy laminates. ASTM STP. 836, 21–55 (1984)
4. Kashtalyan, M., Soutis, C.: Analysis of composite laminates with intra- and interlaminar damage. Progress in Aerospace Sciences 41, 152–173 (2005)10.1016/j.paerosci.2005.03.004 ↗
5. Takeda, N., Ogihara, S., Kobayashi, A.: Microscopic fatigue damage progress in CFRP cross-ply laminates. Composites 26, 859–867 (1995)10.1016/0010-4361(95)90879-5 ↗
6. Varna, J.: Strategies for stiffness analysis of laminates with microdamage: combining average stress and crack face displacement based methods. ZAMM 95(10), 1081–1097 (2015)10.1002/zamm.201400296 ↗
7. Nairn, J., Hu, S.: Matrix microcracking. In: Pipes, R.B., Talreja, R. (eds.) Damage Mechanics of Composite Materials. Composite Materials series, vol. 9, pp. 187–243. Elsevier, Amsterdam (1994)
8. Smith, P.A., Wood, J.R.: Poisson’s ratio as a damage parameter in the static tensile loading of simple cross-ply laminates. Compos. Sci. Technol. 38, 85–93 (1990)10.1016/0266-3538(90)90073-E ↗
9. Hashin, Z.: Analysis of cracked laminates: A variational approach. Mech. Mater. N.-Holl. 4, 121–136 (1985)10.1016/0167-6636(85)90011-0 ↗
10. Varna, J., Berglund, L.A.: Thermo-Elastic properties of composite laminates with transverse cracks. J. Compos. Technol. Res. 16(1), 77–87 (1994)10.1520/CTR10397J ↗
11. Zhang, J., Fan, J., Soutis, C.: Analysis of multiple matrix cracking in [±θm/90n]s composite laminates. Part 1. In-plane stiffness properties. Composites. 23(5), 291–304 (1992)10.1016/0010-4361(92)90327-Q ↗
12. McCartney, L.N., Schoeppner, G.A.: Predicting the effect of non-uniform ply cracking on the thermo-elastic properties of cross-ply laminates. Composites Science and Technology 62, 1841–1856 (2000)10.1016/S0266-3538(02)00091-X ↗
13. McCartney, L.N., Schoeppner, G.A., Becker, W.: Comparison of models for transverse ply cracks in composite laminates. Comp. Sci. Technol. 60, 2347–2359 (2000)10.1016/S0266-3538(00)00030-0 ↗
14. Hajikazemi, M., McCartney, N.L.: Comparison of Variational and Generalized Plane Strain approaches for matrix cracking in general symmetric laminates. Int. J. Damage Mechanics 27(4), 507–540 (2018)10.1177/1056789516685381 ↗
15. O’Brien, T.K.: Characterization of delamination onset and growth in a composite laminate. Damage Compos. Mater. Basic. Mech. Accumulation Toler Charact., 140–167. (1982)10.1520/STP34325S ↗
16. McCartney, L.N., Blazquez, A., Paris, F.: Energy-based delamination theory for biaxial loading in the presence of thermal stresses. Composites Science and Technology 72(14), 1753–1766 (2012)10.1016/j.compscitech.2012.06.015 ↗
17. Kashtalyan, M., Soutis, C.: The effect of delaminations induced by transverse cracks and splits on stiffness properties of composite laminates. Composites Part A: Applied Science and Manufacturing 31, 107–119 (2000)10.1016/S1359-835X(99)00066-4 ↗
18. Kashtalyan, M., Soutis, C.: Analysis of local delaminations in composite laminates with angle-ply matrix cracks. International Journal of Solids and Structures 39, 1515–1537 (2002)10.1016/S0020-7683(02)00007-0 ↗
19. Carraro, P.A., Maragoni, L., Quaresimin, M.: Stiffness degradation of symmetric laminates with off-axis cracks and delamination: an analytical model. International Journal of Solids and Structures 213, 50–62 (2021)10.1016/j.ijsolstr.2020.12.013 ↗
20. Hajikazemi, M., Ahmadi, H., McCartney, L.N., Van Paepegem, W.: A variational approach for accurate prediction of stress and displacement fields and thermo-elastic constants in general symmetric laminates containing ply cracking and delamination under general triaxial loading. Int. J. Solids Struct. 254–255, 111917 (2022)10.1016/j.ijsolstr.2022.111917 ↗
21. Maragoni, L., Carraro, P.A., Simonetto, M., Quaresimin, M.: A novel method to include crack-induced delamination in a fatigue damage predictive procedure for composite laminates. Composites Science and Technology 238, 110011 (2023)10.1016/j.compscitech.2023.110011 ↗
22. Kulkarni, A.N., Pupurs, A., Varna, J.: Analysis of initiation and growth of new transverse cracks in high crack density regions in cross-ply laminates. Journal of Composite Materials 0(0), 1–12 (2024). https://doi.org/10.1177/0021998324129581110.1177/00219983241295811 ↗
23. Gudmundson, P., Zang, W.: A universal model for thermoelastic properties of macro cracked composite laminates. Int J Sol Struct 30, 3211–31 (1993)10.1016/0020-7683(93)90110-S ↗
24. Lundmark, P., Varna, J.: Constitutive relationships for damaged laminate in in-plane loading. Int J Dam Mech 14(3), 235–259 (2005)10.1177/1056789505050355 ↗
25. Lundmark, P., Varna, J.: Crack face sliding effect on stiffness of laminates with ply cracks. Comp. Sci. Technol. 66, 1444–1454 (2006)10.1016/j.compscitech.2005.08.016 ↗
26. Lundmark, P., Varna, J.: Stiffness reduction in laminates at high intralaminar crack density: Effect of crack interaction. Int. J. Damage Mech. 20(2), 279–297 (2011)10.1177/1056789509351840 ↗
27. Loukil, M.S., Varna, J.: Crack face sliding displacement (CSD) as an input in exact GLOB-LOC expressions for in-plane elastic constants of symmetric damaged laminates. International Journal of Damage Mechanics 29(4), 547–569 (2020)10.1177/1056789519866000 ↗
28. Varna, J., Freire, R.T.S., Loukil, M.S., Al-Ramahi, N.J.: COD and CSD based model for in-plane stiffness of symmetric laminates with cracks in plies and local delaminations: Analysis of crack face sliding. Composites Part A: Applied Science and Manufacturing 189, 108594 (2025)10.1016/j.compositesa.2024.108594 ↗
29. Loukil, M.S., Varna, J., Ayadi, Z.: Engineering expressions for thermo-elastic constants of laminates with high density of transverse cracks. Composites A 48(1), 37–46 (2013)10.1016/j.compositesa.2012.12.012 ↗
30. Loukil, M.S., Varna, J., Ayadi, Z.: Applicability of solutions for periodic intralaminar crack distributions to non-uniformly damaged laminates. Journal of Composite Materials 47(3), 287–301 (2013)10.1177/0021998312440126 ↗
31. Varna, J., Loukil, M.S.: Effective transverse modulus of a damaged layer: Potential for predicting symmetric laminate stiffness degradation. Journal of Composite Materials 51(14), 1945–1959 (2017)10.1177/0021998316658965 ↗