Thermomechanical Properties of GFRP after Air and Cooling Fluid Exposure at Elevated Temperatures for Application in Electric Motors
Source abstract
Abstract
Abstract This paper investigates the effect of exposure of glass fiber reinforced plastic (GFRP) laminates with epoxy resins to air and a synthetic poly-alpha-olefin (PAO) oil at 180 °C for 500 h (h) and 1000 h. The test is intended for prequalifying material systems for the intended use of the laminates as a composite seal of a stator lamination to enable a directly cooled electric motor. Three commercially available amin curing and one non-commercial anhydride curing epoxy resin systems are investigated. The results of the mechanical testing indicate post curing effects for the epoxy resins during exposure. These translate to higher moduli in the laminates and for most systems the strength rises as well. These effects dominate the change in mechanical properties for the commercial systems making these systems well suited for the intended use case. However, for one commercial and the noncommercial system, some properties drop after exposure to cooling fluid (CF) e.g. in the transverse tensile test. Here a decrease of the fiber-matrix adhesion is the identified cause. This in turn is caused by a moderate laminate quality which is evident by visible imperfections of the laminate. Thermal properties are mostly affected by the chosen temperature and time of exposure, not so much by the ambient medium. From our findings we conclude that the exposure to PAO oils of the chosen systems is not as severe as the findings from other authors suggest. Therefore, the investigated laminates are prequalified for the intended use. In addition, through the successful subsequent use of our results, we find, that the identified test is suitable for prequalifying GFRP for the use in directly cooled electric motors. Graphical Abstract
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Epoxy Resin Curing Processes · High voltage insulation and dielectric phenomena · Fiber-reinforced polymer composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (72)
Show source-provided references
1. Richard, S.: Automotive composites offer lighter solutions. Reinf. Plast. 54(4), 22–28 (2010). https://doi.org/10.1016/S0034-3617(10)70061-810.1016/S0034-3617(10)70061-8 ↗
2. Krzyak, A., Bemowski, G., Szczepaniak, R., Grzesik, N., Gil, L.: Evaluation of the reliability of composite materials used in aviation. In: Safety and Reliability–Safe Societies in a Changing World, pp. 2093–2098, (2018). https://doi.org/10.1201/9781351174664-26310.1201/9781351174664-263 ↗
3. Nie, J., Jiaji, W., Gou, S., Zhu, Y., Fan, J.: Technological development and engineering applications of novel steel-concrete composite structures. Front. Struct. Civil Eng. 13(1), 1–14 (2018). https://doi.org/10.1007/s11709-0110.1007/s11709-01 ↗
4. Graham-Jones, J., Summerscales, J.: Marine Applications of Advanced Fibre-reinforced composites, 1. Edition, Woodhead PublishingCambridge, ISBN 978-178242-250-1 (2015)10.1016/B978-1-78242-250-1.00001-6 ↗
5. Wang, B., Zhang, Y., Tao, Y., Zhou, X., Song, L., Jie, G., Hu, Y.: Monitoring the degradation of physical properties and fire hazards of high-impact polystyrene composite with different ageing time in natural environments. Compos. Sci. Technol. 171, 135–151 (2018). https://doi.org/10.1016/j.jhazmat.2018.03.03310.1016/j.jhazmat.2018.03.033 ↗
6. Pyl, L., Kalteremidou, K.-A., Hemelrijck, D.V.: Exploration of the design freedom of 3D printed continuous fibre-reinforced polymers in open-hole tensile strength tests. Compos. Sci. Technol. 171, 135–151 (2019). https://doi.org/10.1016/j.compscitech.2018.12.02110.1016/j.compscitech.2018.12.021 ↗
7. Manju, M.B., Vignesh, S., Nikhil, K.S., Sharaj, A.P., Murthy, M.: Electrical Conductivity Studies of Glass Fiber Reinforced Polymer Composites. In: Materials Today: Proceedings, Vol. 5, Issue 1, Part 3, pp. 3229 – 3226 (2018). https://doi.org/10.1016/j.matpr.2018.02.02710.1016/j.matpr.2018.02.027 ↗
8. Grand View Research: Epoxy Resin Market Size, Share & Trends Analysis Report By Application (Paints & Coatings, Wind Turbines), By Region (North America, Europe), And Segment Forecasts, 2024–2030. : ID: 978-1-68038-171-9 (2023)
9. Goosey, M.: Plastics for Electronics. 2. Edition, Kluwer academic PublishersDordrecht, ISBN 978-90-481-4018-3 (1999)
10. Kakaç, S., Yüncü, H., Hijikata, K.: Cooling of Electronic Systems. Springer Science + Business Media (Dordrecht, 1994), https://doi.org/10.1007/978-94-011-1090-710.1007/978-94-011-1090-7 ↗
11. Oechslen, S.: Thermische Modellierung Elektrischer Hochleistungsantriebe. Dissertation. Stuttgart (2018)10.1007/978-3-658-22632-9 ↗
12. Doppelbauer, M. (ed.): Grundlagen der Elektromobilitat. Springer Fachmedien Wiesbaden, isbn: 978-3-658-29729-9, (2020). https://doi.org/10.1007/978-3-658-29730-510.1007/978-3-658-29730-5 ↗
13. Engelhardt, T.: Derating-Strategien für elektrisch angetriebene Sportwagen. Dissertation, Wiesbaden, (2016). https://doi.org/10.1007/978-3-658-18207-610.1007/978-3-658-18207-6 ↗
14. Lange, J., Wachter, S., Engelhardt, T., Oechslen, S., Heitmann, A.: Highly Integrated Electric Axle. Ed. E-438 Motive 11th Interational Conference: Expert Forum on electric vehicle drives and e-mobility (2019)
15. Thumm, P., Oechslen, S., Berendes, P.: Direct cooling of electric machines for vehicles under Long-term testing in Climatic limit operation on a test bench. MTZ Worldw 85, 48–51 (2024). https://doi.org/10.1007/s38313-024-1943-z10.1007/s38313-024-1943-z ↗
16. Merrall, G.T., Meeks, A.C.: Effect of thermal aging on mechanical properties of an epoxy resin system. J. Appl. Polym. Sci. 16, 3389–3392 (1972). https://doi.org/10.1002/app.1972.07016122910.1002/app.1972.070161229 ↗
17. Causse, M., Dantras, E., Tonon, C., Chevalier, M., Combes, H., et al.: Environmental ageing of aerospace epoxy adhesive in bonded assembly configuration. In: Journal of Thermal Analysis and Calorimetry, vol. 114, pp. 621–628. Springer (2013). 2https://doi.org/10.1007/s10973-013-3009-310.1007/s10973-013-3009-3 ↗
18. Feng, Y., Zhang, Z., Yue, D., Maksimenko, B.V., Deng, S., Yang, J., Fu, Z., Liu, Q., Chen, B.: Q.: Recent progress in degradation and recycling of epoxy resin. In Journal of Materials REsearch and Technology, Elsevier, Vol. 32, pp.2891–2912 (2024). https://doi.org/10.1016/j.jmrt.2024.08.09510.1016/j.jmrt.2024.08.095 ↗
19. Su, X., Zhang, S., Zhao, F., Liu, P., Peng, Z.: Experimental study on the effect of thermal aging on epoxy composites used for UHV dry bushing. In: 12th International Conference on the Properties and applications of Dielectric Materials (ICPADM) Xi’an, (2018). https://doi.org/10.1109/ICPADM.2018.840108910.1109/ICPADM.2018.8401089 ↗
20. Odegard, G.M., Bandyopadhyay, A.: Physical Aging of Epoxy Polymers and Their Composites. In: Journal of Applied. Polym. Sci. Part. B: Polym. Phys. 49, 1695–1716 (2011). https://doi.org/10.1002/polb.2238410.1002/polb.22384 ↗
21. Bowles, K.J.: Thermal and Mechanical Durability of Graphite-Fibre-Reinforced PMR-15 Composites. Revised. NASA Technical Report, ID: 19980218858, NASA United States (1998)
22. Le Guen-Geffroy, A., Le Gac, P.-Y., Davies, P.: Physical ageing of epoxy in a wet environment: Coupling between plasticization and physical ageing. Polym. Degrad. Stab. (2019). https://doi.org/10.1016/j.polymdegradstab.2019.10894710.1016/j.polymdegradstab.2019.108947 ↗
23. Yang, Y., Xian, G., Li, H., Sui, L.: Thermal aging of an anhydride-cured epoxy resin. Polym. Degrad. Stab. 118, 111–119 (2015). https://doi.org/10.1016/j.polymdegradstab.2015.04.01710.1016/j.polymdegradstab.2015.04.017 ↗
24. Open Compute Project: Material Compatibility in Immersion Cooling. Revision 1.0, Last updated Nov 28: (2022). https://www.opencompute.org/documents/material-compatibility-in-immersion-cooling-document-version-1-0-nov-28-2022-1-pdf, last visited: 18.08.2025
25. Bansode, P., Ramalingam, M.S., Suthar, R., Bhandari, R., Lakshminarayana, A.B., Gupta, G.: Impact of Immersion Cooling on Thermomechanical Properties of Halogen-Free Substrate Core. ASME 2023 International Technical Conference and Exhibition on Packaging and Integration of Electronic and Photonic Microsystems. San Diego, California, USA, (2023). 10/24/2023–10/26/2023, October 24–26, San Diego, California, https://doi.org/10.1115/IPACK2023-11105610.1115/IPACK2023-111056 ↗
26. Ramdas, S., Rajmane, P., Chauhan, T., Misrak, A., Agonafer, D.: Impact of Immersion Cooling on Thermo-Mechanical Properties of PCB’s and Reliability of Electronic Packages. ASME International Technical Conference and Exhibition on Packaging and Integration of Electronic and Photonic Microsystems, October 7–9, 2019, Anaheim, California, USA. https://doi.org/10.1115/IPACK2019-656810.1115/IPACK2019-6568 ↗
27. Akderya, T., Çevik, M.: Investigation of thermal-oil environmental ageing effect on mechanical and thermal behaviours of E-glass fibre/epoxy composites. J. Polym. Res. (2018). https://doi.org/10.1007/s10965-018-1615-210.1007/s10965-018-1615-2 ↗
28. Cavasin, M.: Study on Accelerated Exposure Testing and Thermal Insulation for a Glass Fibre Reinforced Polymer in Simulated Oil & Gas environment. Doctoral Disseration. Politecnico di Torino, Turin (2019)
29. Amaro, A.M., Reis, P.N.B., Neto, M.A., Louro, C.: Effect of different commercial oils on mechanical properties of composite materials. Compos. Struct. 118, 1–8 (2014). https://doi.org/10.1016/j.compstruct.2014.07.01710.1016/j.compstruct.2014.07.017 ↗
30. Kim, C., Cho, C.H., Son, I., Lee, H., Han, J.W., Kim, J.-G., Lee, J.H.: Effect of microscale oil penetration on mechanical and chemical properties of carbon fiber-reinforced epoxy composites. J. Ind. Eng. Chem. 61, 112–118 (2018). https://doi.org/10.1016/j.jiec.2017.12.00710.1016/j.jiec.2017.12.007 ↗
31. Landmann, A.: Zur Gestaltung von Maschinenkomponenten aus Faser-Kunststoff-Verbund-Halbzeugen, Technische Universität Darmstadt, Fachbereich Maschinenbau, Dissertation (2017)
32. Selzer, R., Friedrich, K.: Mechanical properties and failure behaviour of carbon fibre-reinforced polymer composites under the influence of moisture. Composites Part A: Applied Science and Manufacturing 28(6), 595–604 (1997). https://doi.org/10.1016/S1359-835X(96)00154-610.1016/S1359-835X(96)00154-6 ↗
33. Costa, M.L., Almeida, S.F.M., Rezende, M.C.: Hygrothermal effects on dynamic mechanical analysis and fracture behavior of polymeric composites. Mater. Res. 8(3), 335–340 (2005). https://doi.org/10.1590/S1516-1439200500030001910.1590/S1516-14392005000300019 ↗
34. Khan, L.A., Nesbitt, A., Day, R.J.: Hygrothermal degradation of 977-2A carbon/epoxy composite laminates cured in autoclave and Quickstep. In: Compos.: Part A: Appl. Sci. Manuf. 41, 8, 942–953 (2010). https://doi.org/10.1016/j.compositesa.2010.03.00310.1016/j.compositesa.2010.03.003 ↗
35. Sun, P., Zhao, Y., Luo, Y., Sun, L.: Effect of temperature and Cyclic hygrothermal aging on the interlaminar shear strength of carbon fiber/bismaleimide (BMI) composite. Mater. Des. 32, 4341–4347 (2011). https://doi.org/10.1016/j.matdes.2011.04.00710.1016/j.matdes.2011.04.007 ↗
36. Yu, B., Jiang, Z., Yang, J.: Long-term moisture effects on the interfacial shear strength between surface treated carbon fiber and epoxy matrix. Compos. Part A: Appl. Sci. Manufac. 78, 311–317 (2015). https://doi.org/10.1016/j.compositesa.2015.08.02710.1016/j.compositesa.2015.08.027 ↗
37. Mahieux, C.A.: Environmental Degradation of Industrial Composites, Elsevier Science; ISBN 978-1-85617-447-3, Amsterdam (2006)10.1016/B978-185617447-3/50026-8 ↗
38. Delannoy, R., Quélennec, B., Tognetti, V., Delbreilh, L., Delpouve, N., Richaud, E.: Glass and sub-glass relaxation changes induced by thermal ageing of epoxy-amine polymer networks – A DMA study. Polym. Degrad. Stab. (2023). https://doi.org/10.1016/j.polymdegradstab.2023.11048710.1016/j.polymdegradstab.2023.110487 ↗
39. Singh, N., Sinha, S.K.: Tribological and mechanical analysis of hybrid epoxy based polymer composites with different in situ liquid lubricants (silicone oil, PAO and SN150 base oil). Wear Volumes. 504–505 (2022). https://doi.org/10.1016/j.wear.2022.20440410.1016/j.wear.2022.204404 ↗
40. Hübsch, J.: Eine Auslegungsmethode für direkt einlaminierte Dichthülsen in elektrischen Antriebsmaschinen. Dissertation, Shaker Verlag; Technische Universität Darmstadt (2021)
41. Hübsch, J., Rosendahl, P., Mittelstedt, C.: An analytical failure model for pressurized blister tests of thermally loaded composite laminates. Compos. Part. B: Eng 214, 108588 (2021). https://doi.org/10.1016/j.compositesb.2020.10858810.1016/j.compositesb.2020.108588 ↗
42. Hübsch, J., Rosendahl, P., Mittelstedt, C.: Blister tests on thin-walled composite structures at different temperatures. Int. J. Adhesion Adhesives (2021). https://doi.org/10.1016/j.ijadhadh.2021.10290710.1016/j.ijadhadh.2021.102907 ↗
43. Hübsch, J., Meyer, N., Feldten, D., Mittelstedt, C., Berendes, P.: Investigations of Thin-Walled glass fiber reinforced plastic laminates with sealing function for electric motors. J. Compos. Sci. 9(4), 175 (2025). https://doi.org/10.3390/jcs904017510.3390/jcs9040175 ↗
44. Berendes, P., Oechslen, S., Wiedemann, B.: DE102017102141A1 - Verfahren zur Herstellung einer elektrischen Antriebsmaschine und elektrische Antriebsmaschine. Patent, Dr. Ing. h.c. F. Porsche AG (2018). https://register.dpma.de/DPMAregister/pat/register?AKZ=1020171021418&CURSOR=0
45. Oechslen, S., Berendes, P., Wiedemann, B.: DE102019117373A1 - Spaltrohrmotor mit einem verlustarmen Stützring. Patent, Dr. Ing. h.c. F. Porsche AG, (2020). https://register.dpma.de/DPMAregister/pat/register?AKZ=1020191173736&CURSOR=0
46. Kompass, M., Liebl, H.: Method for Produching an Electrical Machine and Machine Comprising a Fibre Can. Patent, WO2012/085281 A2, AVL Trimetrics GmbH (2012)
47. DIN EN ISO 291: Plastics - Standard atmospheres for conditioning and testing. (2008)
48. DIN EN ISO 527-4: Plastics - Determination of tensile properties - Part 4: Test conditions for isotropic and anisotropic fibre-reinforced plastic composites. (1997)
49. DIN EN ISO 527-5: Plastics - Determination of tensile properties - Part 5: Test conditions for unidirectional fibre-reinforced plastic composites. (2009)
50. DIN EN ISO 14125: Fibre-reinforced plastic composites - Determination of flexural properties.: Cor.1 (2001), Amd.1 (2011) (1998)
51. Hermsdorf, F., Rapp, H.: Untersuchung der reibschlüssigen Lastübertragung in doppelschnittigen Verbindungen m it CFK-Fügepartnern. In: Deutscher Luft- Und Raumfahrtkongress 2016, Braunschweig, Deutsche Gesellschaft für Luft- Und Raumfahrt – Lilienthal-Oberth e.V. Bonn (2016). https://publikationen.dglr.de/?tx_dglrpublications_pi1%5bdocument_id%5d=420203
52. DIN EN ISO 14129: Fibre-reinforced plastic composites - Determination of the in-plane shear stress/shear strain reponse, including the in-plane schear modulus and strength, by ± 45° tension test method. (1997)
53. ASTM D3518: Standard test Method for In-Plane Shear Response of Polymer Matrix Composite Materials by Tensile Test of a ± 45° Laminate, (2018)
54. Basan, R.: Untersuchung der intralaminaren Schubeigenschaften von Faserverbundwerkstoffen mit Epoxidharzmatrix unter Berücksichtigung nichtlinearer Effekte, Technische Universität Berlin, Fakultät V – Verkehrs- und Maschinensysteme, Bundesanstalt für Materialforschung und –prüfung (BAM), Dissertation, (2011)
55. ISO 178: Plastics – Determination of flexural properties.: (2019)
56. ISO 6721-5: Plastics – Determination of dynamic mechanical properties – Part 5: Flexural vibration – Non-resonance method, (2019)
57. Chartoff, R.P., Sircar, A.K.: Thermal analysis of polymers. In: Encyclopedia of Polymer Science and Technology. John Wiley & Sons, Inc (2005). https://doi.org/10.1002/047144026410.1002/0471440264 ↗
58. Deng, S., Hou, M., Ye, L.: Temperature-dependent elastic moduli of epoxies measured by DMA and their correlations to mechanical testing data. Polym. Test. 26(6), 803–813 (2007). https://doi.org/10.1016/j.polymertesting.2007.05.00310.1016/j.polymertesting.2007.05.003 ↗
59. DIN EN ISO 11357-1: Plastics - Differential scanning calorimetry (DSC) - Part 1: General principles, (2023)
60. DIN EN ISO 11357-2: Plastics - Differential scanning calorimetry (DSC) - Part 2: Determination of glass transition temperature and step height, (2020)
61. DIN EN ISO 11357-5: Plastics - Differential scanning calorimetry (DSC) - Part 5: Determination of characteristic reaction-curve temperatures and times, enthalpy of reaction and degree of conversion, (2025)
62. Bicerano, J.: Glass transition. In: Encyclopedia of Polymer Science and Technology. John Wiley & Sons, Inc. (2006). https://doi.org/10.1002/047144026410.1002/0471440264 ↗
63. Deng, S., Ye, L.: Influence of Fiber-Matrix adhesion on mechanical properties of Graphite/Epoxy composites: Part I. Tensile, Flexure, and fatigue properties. J. Reinf. Plast. Compos. 18(11), 1021–1040 (1999). https://doi.org/10.1177/07316844990180110510.1177/073168449901801105 ↗
64. Deng, S., Ye, L.: Influence of Fiber-Matrix adhesion on mechanical properties of Graphite/Epoxy composites: Part II. Interlaminar fracture and inplane shear behavior. J. Reinf. Plast. Compos. 18(11), 1041–1057 (1999). https://doi.org/10.1177/07316844990180110610.1177/073168449901801106 ↗
65. Puck, A.: Festigkeitsanalyse von Faser-Matrix-Laminaten: Modelle für die Praxis, Carl Hanser VerlagMunich, Vienna, ISBN 978-3-446-18194-6 (1996)
66. ISO 13586: Plastics - Determination of fracture toughness (GIC and KIC) - Linear elastic fracture mechanics (LEFM) approach, (2018)
67. Dimitrienko, Y.I.: Thermomechanics of Composites under High Temperatures (Solid Mechanics and Its Applications), Springer Science + Business Media (Dordrecht, 2016), ISBN 978-94-017-7492-5
68. Ehrenstein, G.W., Riedel, G., Trawiel, P.: Thermal Analysis of Plastics: Theory and Practice, Carl Hanser VerlagMunich, ISBN 978-3-446-22673-9 (2004)10.3139/9783446434141 ↗
69. Wallenberger, F.T., Bingham, P.A.: Fiberglass and Glass Technology, Springer US (New York, Dordrecht, Heidelberg, London, ISBN 978-1-4419-0735-6, (2010). https://doi.org/10.1007/978-1-4419-0736-310.1007/978-1-4419-0736-3 ↗
70. Barton, J.M.: A thermoanalytical study of the cure characteristics of an epoxy resin system. Br. Polym. J. 11, 115–119 (1979). https://doi.org/10.1002/pi.498011030310.1002/pi.4980110303 ↗
71. Sun, L., Negulescu, I.I., Pang, S.-S., Sterling, A.M.: Characterization of epoxy Prepreg curing process. J. Adhes. 82(2), 161–179 (2006). https://doi.org/10.1080/0021846060055957310.1080/00218460600559573 ↗
72. Deng, S., Ye, L.: Influence of Fiber-Matrix adhesion on mechanical properties of Graphite/Epoxy composites: Part III. Impact and dynamic mechanical properties. J. Reinf. Plast. Compos. 19(9), 689–703 (1999). https://doi.org/10.1177/00219983920260070110.1177/002199839202600701 ↗