Machinability of Metal Matrix Composites Reinforced by 3-D Network Structure

Metal matrix composites reinforced by three-dimensional (3-D) continuous network structure reinforcement (3DCNRMMC) are difficult to machine due to serious tool wear and poor surface roughness caused by the brittle and hard reinforcement which interpenetrate into ductile matrix. In order to achieve the approach of low cost of 3DCNRMMC, the machinability of it needs to be understood. The influences of three cutting parameters and volume fraction of reinforcement on cutting force were analyzed in detail. The results indicate that: (1) Due to the brittle phase(s) introduced into ductile matrix of composites, there is a large fluctuation of cutting force causing deterioration of machinability. The fluctuation ranges of cutting forces, initially increase rapidly with the increase of volume fraction of reinforcement and then decrease finally, are largest at the range of the volume fraction of 55–65%; (2) The influence of cutting parameters on cutting force is obvious. With the increases of cutting speed, cutting force decreases gradually unless cutting speed exceeds the value of 209 m/min. Cutting forces increase with increasing feed rate and depth of cut; (3) Owing to the large fluctuation of cutting force, there were some cratered surfaces caused by Si3N4 reinforcement pulling-out and flaking-off. Some brittle phase protruding from the machined surface caused the deterioration of machined surface.